• Journal of the Korean Ceramic Society
• /
• v.28 no.2
• /
• pp.130-140
• /
• 1991

The powders of the system Si3N4-Y2O3-AlN were prepared using Si(OC2H5)4 and YCl3.6H2O together with commercial AlN powder. $\alpha$-Si3N4 was prepared by the carbothermal reduction and nitridation of the hydrolyzed gel at 135$0^{\circ}C$ for 10h in N2 atmosphere. YCl3.6H2O was observed to be changed to Y2O3 during the reaction. $\alpha$-Sialon(X=0.2, 0.4, 0.6) ceramics were obtained by hot-pressing the Si3N4-Y2O3-AlN mixture at 178$0^{\circ}C$ for 1h under 30 MPa. The content of $\alpha$-Sialon increased with increasing metal solubility(x value) and $\alpha$-Sialon single phase was obtained at the metal solubility of 0.6. With increasing metal solubility, flexural strength, fracture toughness and thermal shock resistence were decreased, while the microhardness was increased. Large elongated $\beta$-Si3N4 grains were mainly observed at lower metal solubility. Mechanical prorerties of the sintered ceramics with X=0.2 were measured as follows : flexural strength ; 650 MPa, fracture toughness ; 3.63 MN/m3/2, hardness ; 14.7 GPa, thermal shock resistence temperature ; 58$0^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.429-433
• /
• 2013

Silicon, carbon, and B4C powders were used as raw materials for the fabrication of porous SiC. ${\beta}$-SiC was synthesized at $1500^{\circ}C$ in an Ar atmosphere from a silicon and carbon mixture. The synthesized powders were pressed into disk shapes and then heated at $2100^{\circ}C$. ${\beta}$-SiC particles transformed to ${\alpha}$-SiC at over $1900^{\circ}C$, and rapid grain growth of ${\alpha}$-SiC subsequently occurred and a porous structure with elongated plate-type grains was formed. The mechanism of this rapid grain growth is thought to be an evaporation-condensation reaction. The mechanical properties of the fabricated porous SiC were investigated and discussed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.07a
• /
• pp.431-434
• /
• 2001

The mechanical and phase transformation of the cold isostatically pressed $\alpha$-SiC ceramic were investigated as a function of the sintering temperature. The result of phase analysis by XRD revealed 6H, 4H, 3C and phase transformation between 6H and 4H showed a sudden change over 200$0^{\circ}C$. However, the alongrightarrow$\beta$ reverse transformation did not occur to any sintering temperature. The relative density and the mechanical properties of $\alpha$-SiC ceramic was increased with increased sintering temperature. The flexural strength rapidly inclosed below 210$0^{\circ}C$ and showed the highest value of 410 MPa at 220$0^{\circ}C$. This reason is because crack was propagated through surface flaw. The fracture toughness showed the highest value of 3.3 MPa.m$_{1}$2/ at 220$0^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.25 no.5
• /
• pp.561-569
• /
• 1988

Mixtures of very small amounts of additive, carbon and silica(about 0.46${\mu}{\textrm}{m}$) which synthesized by the hydrolysis of ethyl silicate, the molar ratio of SiO2/C was fixed to 1/10, was nitrided at 145$0^{\circ}C$. It was considered that the optimum amount of additive to promote the nitridation reaction was below 2.0wt%. By the addition of additive, the nitridation reaction was promoted and formation of $\beta$-Si3N4 was promoted at 145$0^{\circ}C$ for 1hour, but, the nitridation reaction was decreased and the ratio of $\alpha$/$\beta$ of Si3N4, was increased at 145$0^{\circ}C$ for 5 hours. The crystal phase was $\alpha$ phase and the nitridation reaction was promoted and the particle size of silicon nitride was become smaller by the addition of $\alpha$-Si3N4, but silicon nitride of whisker-like form was produced by the addition of transition elements. There was a difference in the lattice constants of $\alpha$-Si3N4, but no difference in its of $\beta$-Si3N4 according to kinds of added substance and reaction time.

• Korean Journal of Materials Research
• /
• v.26 no.6
• /
• pp.337-341
• /
• 2016

Cu-30 vol% SiC composites with relatively densified microstructure and a sound interface between the Cu and SiC phases were obtained by pressureless sintering of PCS-coated SiC and Cu powders. The coated SiC powders were prepared by thermal curing and pyrolysis of PCS. Thermal curing at $200^{\circ}C$ was performed to fabricate infusible materials prior to pyrolysis. The cured powders were heated treated up to $1600^{\circ}C$ for the pyrolysis process and for the formation of SiC crystals on the surface of the SiC powders. XRD analysis revealed that the main peaks corresponded to the ${\alpha}$-SiC phase; peaks for ${\beta}$-SiC were newly appeared. The formation of ${\beta}$-SiC is explained by the transformation of thermally-cured PCS on the surface of the initial ${\alpha}$-SiC powders. Using powder mixtures of coated SiC powder, hydrogen-reduced Cu-nitrate, and elemental Cu powders, Cu-SiC composites were fabricated by pressureless sintering at $1000^{\circ}C$. Microstructural observation for the sintered composites showed that the powder mixture of PCS-coated SiC and Cu exhibited a relatively dense and homogeneous microstructure. Conversely, large pores and separated interfaces between Cu and SiC were observed in the sintered composite using uncoated SiC powders. These results suggest that Cu-SiC composites with sound microstructure can be prepared using a PCS coated SiC powder mixture.

• Journal of the Korean Ceramic Society
• /
• v.30 no.11
• /
• pp.941-948
• /
• 1993

The powder mixture of Si3N4-AlN-Y2O3, Si3N4-AlN-CeO2 and Si3N4-AlN-Y2O3-CeO2 system was hot-pressed at 175$0^{\circ}C$ for 2h in N2 to prepare $\alpha$-Sialon ceramics. The mechanical property and oxidation behaviour of the prepared $\alpha$-Sialon ceramics were investigated. At 120$0^{\circ}C$, oxidation resistance was best for the Y2O3 added $\alpha$-Sialon ceramics and oxidation rate increased when the amount of CeO2 increased. But when the mixture of Y2O3 and CeO2 added $\alpha$-Sialon ceramics showed a good oxidation resistance. Fracture toughness of (Y2O3＋CeO2) added $\alpha$-Sialon ceramics was higher than Y2O3 added $\alpha$-Sialon ceramics.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.6 no.3
• /
• pp.386-391
• /
• 1996

SiC particles (average size is 270 nm) of 0, 10, 20, 30, 40 vol% were dispersed in $Si_{3}N_{4}$, and $Si_{3}N_{4}/SiC$ nanocomposites were fabricated by hot press. After sintering, matrix phase, ${\alpha}-Si_{3}N_{4}$ was transformed to ${\beta}-Si_{3}N_{4}$, and second phase, ${\beta}-SiC$ was not changed. No grain boundary crystalline phase by adding of sintering additives was detected. Grain growth of $Si_{3}N_{4}$ was supressed with increasing of SiC contents, and then fine grain was occurred. The highest fracture strength was obtained at 10 vol% SiC, and fracture toughness was decreased, but hardness was linearly increased with SiC content.

• Journal of the Korean Ceramic Society
• /
• v.27 no.4
• /
• pp.553-559
• /
• 1990

The nonuniform shrinkage has been investigaed in pressureless sintering of $\alpha$-SiC, where born carbide and phenolic resin as a carbon source are used as densification aids. Compacted specimens, prepared from the granulated powder, were sintered at 215$0^{\circ}C$ for 30min in Ar atmosphere. Using the fresh and unseasoned graphite crucible, the upwarped specimens were obtained, while specimens were uniformly shrunk in the seasoned crucible. This effect is mainly due to the nonuniform distributjion of boron carbide during heatig, which originates in the reaction of boron carbide with CO gas, providing from the result of SiO2 reduction with carbon during heating.

• Toxicological Research
• /
• v.29 no.4
• /
• pp.257-261
• /
• 2013

${\alpha}$-Curcumene is one of the physiologically active components of Curcuma zedoaria, which is believed to perform anti-tumor activities, the mechanisms of which are poorly understood. In the present study, we investigated the mechanism of the apoptotic effect of ${\alpha}$-curcumene on the growth of human overian cancer, SiHa cells. Upon treatment with ${\alpha}$-curcumene, cell viability of SiHa cells was inhibited > 73% for 48 h incubation. ${\alpha}$-Curcumene treatment showed a characteristic nucleosomal DNA fragmentation pattern and the percentage of sub-diploid cells was increased in a concentration-dependent manner, hallmark features of apoptosis. Mitochondrial cytochrome c activation and an in vitro caspase-3 activity assay demonstrated that the activation of caspases accompanies the apoptotic effect of ${\alpha}$-curcumene, which mediates cell death. These results suggest that the apoptotic effect of ${\alpha}$-curcumene on SiHa cells may converge caspase-3 activation through the release of mitochondrial cytochrome c.

• Journal of the Korean Ceramic Society
• /
• v.29 no.5
• /
• pp.347-356
• /
• 1992

Various kaolin samples with different alumina content were prepared from calcined admixture of kaolin and ammonium sulfate by varying the treatment time in sulfuric acid. Samples were nitridated under N2 or N2-H2 atmosphere with changing the amount of added carbon, the reaction time and temperature. As the alumina content lowered, the size of kaolin particles decreased and the specific surface area increased. XRD analysis indicated that ${\alpha}$-quartz remained by decomposition of halloysite and meta-halloysite. Experimental results of nitridation behavior are summerized as follows; 1) Nitridation under N2 atmosphere. With the increase of C/SiO2 ratio and with the decrease of Al2O3 content, disappearance of XRD pattern peaks of mullite, ${\alpha}$-quartz and ${\alpha}$-Al2O3 were accelerated at 1300$^{\circ}C$. SiC was the main phase in the reaction product of acid-treated kaolin samples nitridated at 1300$^{\circ}C$ for 10 hours regardless of C/SiO2 ratio. But the XRD peak intensities of ${\beta}$-Si3N4, ${\beta}$-sialon and SiC did not show much difference when untreated raw kaolin was fired at the same condition. When the ratio of C/SiO2 was 3.5, ${\beta}$-sialon and ${\beta}$-Si3N4 existed in the reaction product of about 22% alumina containing kaolin sample fired at 1350$^{\circ}C$ for 7 hours. Only ${\beta}$-sialon existed in the same sample fired at 1400$^{\circ}C$ for 10 hours. ${\beta}$-sialon was obtained from all of the acid-treated kaolin samples fired at 1400$^{\circ}C$ for 40 hours, but AlN and SiC remained in the untreated kaolin sample. Z value of the ${\beta}$-sialon obtained from the 22% alumina containing kaolin sample fired at 1400$^{\circ}C$ for 40 hours was about 1.3(XRD) and 1.5(EDS). 2) Nitridation under 80N2+2OH2 mixed gas atmosphere with the C/SiO2 ratio of 1 Mullite was not found, but ${\alpha}$-Si3N4, and ${\beta}$-sialon were present in the reaction product of about 22% alumina containing kaolin sample fired at 1300$^{\circ}C$ for 10 hours. When untreated kaolin sample was nitridated at the same condition, mullite remained. AlN and SiC were not found in the reaction product of about 22% alumina containing kaolin sample fired at 1350$^{\circ}C$ for 5 hours. On the other hand, AlN and SiC remained in the product of untreated kaolin fired at the same condition.