• 한국세라믹학회지
• /
• 제34권6호
• /
• pp.553-560
• /
• 1997

A fine $\alpha$-Al2O3 powder was prepared by sol-gel process for membrane application. And it was carried out by adding 1.5wt% $\alpha$-Al2O3 powders(mean size : 87 nm) as seeds to the prepared sols and by controlling the heating schedule (the heating rate and the soaking time) to prevent the microstructural change, which occured during $\theta$-to $\alpha$Al2O3 phase transformation. The seeded $\alpha$-Al2O3 particles acted as the heterogeneous nucleation sites for the $\alpha$-Al2O3 nucleation during the transformation of $\theta$- to $\alpha$-Al2O3 and resulted in increasing the driving force of phase transformation to activate the formation of $\alpha$-Al2O3 phase at 82$0^{\circ}C$. By $\alpha$-Al2O3 seeding and controlling of heating condition the phase transformation of $\theta$- to $\alpha$-Al2O3 was accomplished at low temperature and the grain growth process was depressed. Therefore, the unsupported membrane could be fabricated in $\alpha$-Al2O3 . The average diameter of pores in the fabricated membrane was 7 nm and the porosity was 47%.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 1999년도 제17회 학술발표회 논문개요집
• /
• pp.145-145
• /
• 1999

La-Ca-Mn-O (LCMO) 박막에서 초거대 자기 저항 효과와 발견된 이후 자기 센서와 고밀도 자기 저장 매체로서 응용하기 위한 연구가 진행되고 있다. 그러나 현재 대부분의 증착은 타겟과 박막간의 조성의 일치를 위하여 PLD 방법을 이용하고 있으며 RF magnetron sputtering 법으로 증착한 예는 많이 보고되고 있지 않으며 특히 적층 성장시킨 예는 아직 보고되지 있지 않다. 또한 LCMO와의 낮은 격자 상수 불일치를 보이는 SrTiO3와 LaAlO3 기판에 LCMO 박막을 성장시킬 경우 LaAlO3의 경우 XRD rocking curve의 curve의 FWHM 값이 SrTiO3 상에 증착시킨 것의 10배 이상의 값을 보인다는 것은 주목할 만한 사실이다. RF magnetron sputtering 법을 이용하여 LaAlO3 기판상에 145nm MCMO 박막을 적층성장시켰다. XRD $ heta$-2$\theta$ scan을 통해 박막이 c-축 배향한 것을 확인할 수 있었으며 RBS 분석결과 4.98%의 minimumyield를 보였으며 이로부터 박막이 적층성장한 것을 확인할 수 있었다. LCMO (200) peak의 XRD $\theta$-rocking 결과 FWHM의 값은 0.311$^{\circ}$를 보였으나 2개의 피크가 존재하는 것을 볼 수 있었다. 따라서 기판의 (200) 피크를 XRD $\theta$-2$\theta$ scan에서 0.3$^{\circ}$ 간격으로 두 개의 피크를 관찰할 수 있었는데 이는 기판과 박막간의 stress로 인한 tetragonal distortion에 의한 것으로 알려져 있었다. 따라서 기판상에 박막이 어떤 식으로 적층 성장되었는지를 RBS를 이용하여 <001>과 <011> 방향으로 2MeV He++를 주입하여 0.1$^{\circ}$ 간격으로 틸팅을 해본 결과 <001> 방향에서는 1.12$^{\circ}$의 차이를 보였다. 이는 기판과의 compressive stress로 인해 c축 방향으로 늘어났으며 stress relaxed layer는 XRD 결과와는 달리 관찰할 수 없었다. 이러한 현상의 기판 자체의 twin 구조로 인한 것으로 생각된다. RBS 분석후 고분해능 XRD를 이용해 LCMO (200) peak의 $\theta$-rocking 결과 이제R지 laAlO3 상 증착한 LCMO의 값으로는 제일 작은 0.147$^{\circ}$를 나타내었다.

• 청정기술
• /
• 제18권2호
• /
• pp.162-169
• /
• 2012

n-부탄의 탈수소화 촉매로 Pt와 Sn을 알루미나 지지체에 담지하기 위하여 함침법을 이용하여 Pt-Sn/${\theta}-Al_2O_3$ 촉매를 제조하였다. 물리적화학적 특성을 알아보기 위해 XRD, $N_2$ 흡탈착, $NH_3$-TPD, $H_2$-TPR 분석을 실시하였다. 또한 Pt-Sn/${\theta}-Al_2O_3$ 촉매상에서 탈수소반응에 대한 활성에 대한 영향을 관찰하기 위해서 전처리 온도, 전처리 시간, 반응온도, 공간속도에 따른 촉매의 활성에 대한 영향과 더불어 탈수소 반응에 대한 온도 조건에 따른 반응속도의 변화를 관찰하였다. 5~55% 부탄의 전환율 변화에 따른 부텐의 선택도 합은 95% 정도로 일정하게 유지되었다. 아레니우스식을 이용하여 얻은 활성화 에너지 $82.4kJ\;mol^{-1}$이었고, 멱함수를 이용하여 얻은 n-부탄 및 수소의 반응차수는 각각 0.70과 -0.20차로 나타났다.

• 한국결정성장학회지
• /
• 제5권3호
• /
• pp.269-277
• /
• 1995

초고온(5000K 이상)의 고주파 유도 플라즈마(ICP)를 열원으로 사용하여 $AlCl_3$와 $Al_2(SO_4)_3$로부터 $Al_2O_3$ 초미세분말을 합성하였다. 각각 합성된 $Al_2O_3$ 미분말의 결정상은 모두${\alpha} - group({\alpha}, {wdelta}, {\theta})$의 상이었으며, 평균입경 20 nm 내외의 좁은 입도 분포를 가지는 미분말이 형성되었다. ICP tail flame 중간부(X = 500 mm)에서 MgO polycrystal plate위에 부착된 응집플록, whisker 및 판형의 형태를 통 해 기상-고상반응에 의한 성장과 입자간 소결현상을 제안 할 수 있었다. 그리고 위의 결과들로부터 spray-ICP 반응기 내에서의 $Al_2O_3$미 분말 형성과정을 제안하였다.

• 한국세라믹학회지
• /
• 제20권4호
• /
• pp.289-296
• /
• 1983

The Wetting of fusion cast $Al_2O_3$ brick and $Al_2O_3 -ZrO_2$ brick by liquid Ag was studied by the sessile drop technique in Ar atmosphere. In this experiment the specimens were photographed per 2$0^{\circ}C$with increasing temperature from 96$0^{\circ}C$ melting point of Ag. And the method of photographing was carried out by shadow technique. The cosine of the contact angle increased linearly with increasing temperature in both systems. And the relation between the cosine of the contact angle and the temperature was Cos$\theta$=1.132+$0.75{\times}10^{-3}T$ for $Al_2O_3$ brick and Cos$\theta$=-1.706+$1.125{\times}10^{-3}T$ for $Al_2O_3 -ZrO_2$ brick In both systems the contact angle decreased as the surface of substrate became smoother. The work of adhesion which was 503.5ergs/$cm^2$ for $Al_2O_3$brick and 393.6 ergs/cm2 for $Al_2O_3 -ZrO_2$ brick at 96$0^{\circ}C$ increased parabolically with increasing temperature in both system.

• 한국세라믹학회지
• /
• 제30권12호
• /
• pp.1045-1053
• /
• 1993

Alumina hydrates were prepared by the neutralization of AlCl3.6H2O solution with NH3 gas diluted with N2 gas. The values of pH in reaction solution influenced the formation of alumina hydrates minerals. Amorphous alumina hydrates, for example, were formed at ${\gamma}$-Al2O3longrightarrow$\delta$-Al2O3longrightarrow$\theta$-Al2O3longrightarrow$\alpha$-Al2O3. (2) Bayeritelongrightarrowamorphouslongrightarrow${\gamma}$-Al2O3longrightarrow$\delta$-Al2O3longrightarrowη-Al2O3longrightarrow$\theta$-Al2O3longrightarrow$\alpha$-Al2O3. On the other hand, the shape of alumina hydrates whichw ere prepared by the reacton of Al2(SO4)3.16H2O solution and NH3 gas was spherical, the progress of its phase transformation with increasing temperature was amorphouslongrightarrow${\gamma}$-Al2O3longrightarrow$\alpha$Al2O3 in sequence.

• Bulletin of the Korean Chemical Society
• /
• 제23권8호
• /
• pp.1166-1168
• /
• 2002

• 한국결정성장학회지
• /
• 제22권6호
• /
• pp.286-290
• /
• 2012

알루미늄 에칭 폐액으로부터 boehmite(AlOOH) 분말을 합성하였다. 폐액에서 침전되어 있는 결정상은 gibbsite ($Al(OH)_3$)였으며, 산을 이용하여 pH를 조절한 결과 pH가 7~8 영역에서 boehmite 결정상이 얻어졌다. 침전 분말에 남아 있는 Na 이온을 제거하고자 세척공정을 진행하여 boehmite 분말을 얻었다. 합성한 분말의 평균입경은 약 40 nm이었다. 또한 열처리 온도가 증가함에 따라 boehmite는 ${\gamma}-Al_2O_3$와 ${\delta}-Al_2O_3$, ${\Theta}-Al_2O_3$를 거쳐 ${\alpha}-Al_2O_3$ 결정상으로 상전이가 일어났다.

• 한국세라믹학회지
• /
• 제26권2호
• /
• pp.210-220
• /
• 1989

The properties of the powder of Al2O3-15v/o ZrO2(＋3m/o Y2O3) system prepared by co-precipitation method at the pH values of 7, 9, 10 and 11 were investigated. Al2(SO4)3.18H2O, ZrOCl2.8H2O and YCl3.6H2O were used as starting materials and NH4OH as a precipitation agent. Zirconium hydroxide decreased the specific surface area of aluminum hydroxide of AlOOH type, while increased the specific surface area of aluminum hydroxide of Al(OH)3 type, and formed co-network structure of Al-O-Zr type with the aluminum hydroxides. The rate of transition to $\alpha$-Al2O3 from co-precipitated materials occurred in the order of 7≒10, 9 and 11 of pH values. Al2O3 and ZrO2 interacted to bring about coupled grain growth, and the growth of ZrO2 crystallite size rapidly occurred within $\theta$-Al2O3 matrix. Segregation did not occur in the system Al2O3-15v/o ZrO2(＋3m/o Y2O3) and Y2O3 acted as a stabilizer to ZrO2. The lattice strain of tetragonal ZrO2 was increased by the constraint effect of Al2O3 matrix.

• Bulletin of the Korean Chemical Society
• /
• 제23권6호
• /
• pp.793-795
• /
• 2002