• 전기화학회지
• /
• 제11권2호
• /
• pp.89-94
• /
• 2008

GNP(Glycine Nitrate Process)을 이용하여$(La_{0.75}Sr_{0.25})_{1-x}FeO_{3-\delta}$를 합성하고, perovskite의 A-site deficiency에 따른 특성을 분석하기 위해 x=0, 0.02, 0.04, 0.06, 0.08로 바꾸어 합성하였다. SEM과 XRD분석을 통하여 균질하고 결정성이 높은 분말이 합성된것을 확인하였으며, 4단자법과 AC impedance spectroscopy를 통하여 전도도는 x = 0.02가 $750^{\circ}C$ $155{\Omega}cm^2$로 가장 우수하였으며, AC impedance결과 역시 x = 0.02가 가장 낮은 분극저항과 활성화 에너지를 가지고 있었다. 이 결과 Perovskite의 A-site deficiency를 가함에 따라 산소 결핍 및 구조의 변화가 생겼으며 이로 인해 전도도와 분극 저항, 활성화 에너지에 영향을 미친 것을 알 수 있었다.

• The Korean Journal of Ceramics
• /
• 제4권2호
• /
• pp.95-98
• /
• 1998

We have developed new type of superconducting-superionic conducting nanohybrids, $Ag_xI_wBi_2Sr_2Ca_{n-1}Cu_nO_y$ (n=1 and 2) by applying the chimie douce reaction to the superconducting Bi-based cuprates. These nanohybrids can be achieved by the stepwise intercalation whereby the $Ag^+$ ion is thermally diffused into the pre-intercalated iodine sublattice of $IBi_2Sr_2Ca_{n-1}Cu_nO_y$. According to the X-ray diffraction analysis, the Ag-I intercalates are found to have an unique heterostructure in which the superionic conducting Ag-I layer and the superconducting $IBi_2Sr_2Ca_{n-1}Cu_nO_y$ layer are regularly interstratified with a remarkable basal increment of ~7.3$\AA$. The systematic XAS studies demonstrate that the intercalation of Ag-I accompanies the charge transfer between host and guest, giving rise to a change in hole concentration of $CuO_2$ layer and to a slight $T_c$ change. The Ag K-edge EXAFS result reveals that the intercalated Ag-I has a $\beta$-AgI-like local structure with distorted tetrahedral symmetry, suggesting a mobile environment for the intercalated $Ag^+$ ion. In fact, from ac impedance analyses, we have found that the Ag-I intercalates possess a fast ionic conductivity ($\sigma_i=10^{-1.4}\sim 10^{-2.6}\Omega^{-1}\textrm{cm}^{-1}\;at\;270^{\circ}C$ with an uniform activation energy ($\DeltaE_a=0.22\pm 0.02$ eV). More interesting finding is that these intercalates exhibit high electronic conducting as well as ionic ones ($t_i$=0.02~0.60) due to their interstratified structure consisting of superionic conducting and superconducting layers. In this respect, these new intercalates are expected to be useful as an electrode material in various electrochemical devices.

• 한국결정성장학회지
• /
• 제1권2호
• /
• pp.79-93
• /
• 1991

초 고집적 회로의 시대로 접어들면서 지금까지의 금속선 형성 기술 및 배선 재료에 많은 문제점들이 나타나고 있다. 알루미늄의 대체 재료로서 검토되고 있는 구리를, 전기 화학적 방법에 의해 미세 접촉창에 선택적으로 충전함으로써 새로운 금속선 형성 기술을 제시하고자 하였다. 0.75M의 황산구리 수용액을 전해액으로 사용하여 p형 (100) 규소 박판위에 구리 전착막을 형성한 후 Alpha Step, 주사 전자 현미경, 4-탐침법을 사용하여 막의 두께, 입자 크기, 비저항을 측정함으로써 전착 시간, 전류 밀도, 첨가물로 사용한 젤라틴 농도가 전착막의 성질에 미치는 영향에 대해 조사하였다. 평균 전착 속도는 전류 밀도가 $ 2A/dm^2$일 때 0.5-0.6\mu\textrm{m}$/min 였고 구리 입자의 크기는 전류밀도 증가에 따라 증가하였다. 입자 크기 $4000{\AA}$이상에서 얻어진 비저항값은 3-6 Ω.cm였다. 젤라틴을 첨가하여 입자의 크기를 $0.1\mu\textrm{m}$이하로 감소시킴으로써 크기 $1\mu\textrm{m}$이하의 접촉장에 구리를 선택적으로 충전시키는데 성공하였다.

• 대한전자공학회논문지SD
• /
• 제38권10호
• /
• pp.671-677
• /
• 2001

사파이어 기판 위에 성장된 GaN위에 RUO₂/GaN 쇼트키형 자외선 수광소자를 설계, 제작하였다. 자외선 빛의 흡수율을 높이기 위해, MOCVD 다층구조는 undoped GaN(0.5 ㎛)in￣-GaN(0.1 ㎛)/n＋-GaN(1.5 ㎛)로 성장하였다. 성장층은 3.8×10/sup 18/ cm￣³의 캐리어 농도와 283 ㎠/V· s의 이동도를 가진다. 500 ㎛내외의 직경을 가지는 메사구조를 형성하기 위해 ECR 식각한 후, n＋-GaN층위에 Al으로 저항성 접촉을 하였다. 저항성 및 쇼트키 접촉 사이에 Si₃/N₄ 박막으로 절연한 이후 undoped GaN 층위에 RuO₂ 쇼트키 접촉을 하였다. 제작된 쇼트키 다이오드는 1.15×10/sup -5/ ［Ω-㎠］의 접촉비저항을 가졌다. 제작된 다이오드는 역전압인 -5V에서 305pA의 낮은 누설전류를 확인하였는데, 이 값은 RuO₂ 쇼트키 금속증착에 의해 현저히 향상된 것이다. 광측정에서는 10/sup 5/의 자외선대가시광선 제거비와 365nm 파장에서 0.23A/W로 높은 응답도를 보인다.

• 한국정보통신학회논문지
• /
• 제9권3호
• /
• pp.576-581
• /
• 2005

강유전체$(SrTiO_3)$ 박막을 게이트 절연층으로 하여 수소화 된 비정질 실리콘 박막 트랜지스터를 유리 기판 위에 제조하였다. 강유전체는 기존의 $SiO_2,\;SiN$ 등과 같은 게이트 절연체에 비하여 유전특성이 매우 뛰어나 TFT의 ON 전류를 증가시키고 문턱전압을 낮추며 항복특성을 개선하여 준다. PECVD에 의하여 증착된 a-Si:H는 FTIR 측정 결과 $2,000cm^{-1}$과 $876cm^{-1}$에서 흡수 밴드가 나타났으며, $2,000cm^{-1}$과 $635cm^{-1}$은 $SiH_1$의 stretching과 rocking 모드에 기인한 것이며 $876cm^{-1}$의 weak 밴드는 $SiH_2$ vibration 모드에 의한 것이다. a-SiN:H는 optical bandgap이 2.61 eV이고 굴절률은 $1.8\~2.0$, 저항률은 $10^{11}\~10^{15}\Omega-cm$ 정도로 실험 조건에 따라 약간 다르게 나타난다. 강유전체$(SrTiO_3)$ 박막의 유전상수는 $60\~100$ 정도이고 항복전계는 IMV/cm 이상으로 우수한 절연특성을 갖고 있다. 강유전체를 이용한 TFT의 채널 길이는 $8~20{\mu}m$, 채널 넓이는 $80~200{\mu}m$로서 드레인 전류가 게이트 전압 20V에서 $3.4{\mu}A$이고 $I_{on}/I_{off}$ 비는 $10^5\~10^8,\;V_{th}$는 $4\~5\;volts$이다.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2014년도 제46회 동계 정기학술대회 초록집
• /
• pp.454-454
• /
• 2014

Silicon microwire array is one of the promising platforms as a means for developing highly efficient solar cells thanks to the enhanced light trapping efficiency. Among the various fabrication methods of microstructures, deep reactive ion etching (DRIE) process has been extensively used in fabrication of high aspect ratio microwire arrays. In this presentation, we show precisely controlled Si microwire arrays by tuning the DRIE process conditions. A periodic microdisk arrays were patterned on 4-inch Si wafer (p-type, $1{\sim}10{\Omega}cm$) using photolithography. After developing the pattern, 150-nm-thick Al was deposited and lifted-off to leave Al microdisk arrays on the starting Si wafer. Periodic Al microdisk arrays (diameter of $2{\mu}m$ and periodic distance of $2{\mu}m$) were used as an etch mask. A DRIE process (Tegal 200) is used for anisotropic deep silicon etching at room temperature. During the process, $SF_6$ and $C_4F_8$ gases were used for the etching and surface passivation, respectively. The length and shape of microwire arrays were controlled by etching time and $SF_6/C_4F_8$ ratio. By adjusting $SF_6/C_4F_8$ gas ratio, the shape of Si microwire can be controlled, resulting in the formation of tapered or vertical microwires. After DRIE process, the residual polymer and etching damage on the surface of the microwires were removed using piranha solution ($H_2SO_4:H_2O_2=4:1$) followed by thermal oxidation ($900^{\circ}C$, 40 min). The oxide layer formed through the thermal oxidation was etched by diluted hydrofluoric acid (1 wt% HF). The surface morphology of a Si microwire arrays was characterized by field-emission scanning electron microscopy (FE-SEM, Hitachi S-4800). Optical reflection measurements were performed over 300~1100 nm wavelengths using a UV-Vis/NIR spectrophotometer (Cary 5000, Agilent) in which a 60 mm integrating sphere (Labsphere) is equipped to account for total light (diffuse and specular) reflected from the samples. The total reflection by the microwire arrays sample was reduced from 20 % to 10 % of the incident light over the visible region when the length of the microwire was increased from $10{\mu}m$ to $30{\mu}m$.

• 센서학회지
• /
• 제23권3호
• /
• pp.185-191
• /
• 2014

The width of depletion region in a varactor diode can be modulated by varying a reverse bias voltage. Thus, the preferred characteristics of depletion capacitance can obtained by the change in the width of depletion region so that it can select only the desirable frequencies. In this paper, the TV tuner varactor diode fabricated by hyper-abrupt profile control technique is presented. This diode can be operated within 3.3 V of driving voltage with capability of UHF band tuning. To form the hyperabrupt profile, firstly, p+ high concentration shallow junction with $0.2{\mu}m$ of junction depth and $1E+20ions/cm^3$ of surface concentration was formed using $BF_2$ implantation source. Simulation results optimized important factors such as epitaxial thickness and dose quality, diffusion time of n+ layer. To form steep hyper-abrupt profile, Formed n+ profile implanted the $PH_3$ source at Si(100) n-type epitaxial layer that has resistivity of $1.4{\Omega}cm$ and thickness of $2.4{\mu}m$ using p+ high concentration Shallow junction. Aluminum containing to 1% of Si was used as a electrode metal. Area of electrode was $30,200{\mu}m^2$. The C-V and Q-V electric characteristics were investigated by using impedance Analyzer (HP4291B). By controlling of concentration profile by n+ dosage at p+ high concentration shallow junction, the device with maximum $L_F$ at -1.5 V and 21.5~3.47 pF at 0.3~3.3 V was fabricated. We got the appropriate device in driving voltage 3.3 V having hyper-abrupt junction that profile order (m factor) is about -3/2. The deviation of capacitance by hyper-abrupt junction with C0.3 V of initial capacitance is due to the deviation of thermal process, ion implantation and diffusion. The deviation of initial capacitance at 0.3 V can be reduced by control of thermal process tolerance using RTP on wafer.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제42회 동계 정기 학술대회 초록집
• /
• pp.358-359
• /
• 2012

최근 분극 특성이 상이한 무분극 GaN 에피성장에 관한 심도 있는 연구와 함께 전자-전공 캐리어의 주입 및 캐리어의 거동, 방출되는 편광 특성 및 다양한 물리적 특성들에 대해 보고되고 있으며, 광학적 특성 및 물리적 특성의 확보를 위한 많은 연구가 활발히 진행 중이다 [1]. GaN의 ohmic 접촉(ohmic contact)의 형성은 발광 다이오드(light emitting diode), 레이저 다이오드(Laser), 태양전지(solar cell)와 같은 고신뢰도, 고효율 광전자 소자를 제조하기 위해서는 매우 중요하다 [2]. 그러나 이와 함께 병행 되어야 할 무분극 p-GaN 의 ohmic contact에 관한 연구는 많이 이루어지고 있지 않는 실정이다. 따라서 본 논문에서는 r-plane 사파이어 기판 상에 성장된 p-GaN에서의 ohmic 접촉 형성 연구를 위하여 Ni/Au ohmic 전극의 접촉저항 특성을 연구하였다. 본 실험에서는 성장된 a-plane GaN의 Hole농도가 $3.09{\times}1017cm3$ 인 시편을 사용하였다. E-beam evaporation 장비를 이용하여 Ni/Au를 각각 20 nm 그리고80 nm 증착 하였으며 비접촉저항을 측정하기 위해 Circle-Transfer Length Method (C-TLM) 패턴을 사용하였다. 샘플은 RTA (Rapid Thermal Annealing)를 사용하여 $300^{\circ}C$에서 $700^{\circ}C$까지 온도를 변화시키며 전기적 특성을 비교하여 그림 1(a) 나타내었다. 그림에서 알 수 있듯이 $400^{\circ}C$에서 가장 낮은 비접촉저항 값인 $6.95{\times}10-3{\Omega}cm2$를 얻을 수 있음을 발견하였다. 이 때의 I-V curve 도 그림1(b)에 나타낸 바와 같이 열처리에 의해 크게 향상됨을 알 수 있다. 그러나, $500^{\circ}C$ 이상 온도를 증가시키면 다시 비접촉 저항이 증가하는 것을 관찰하였다. XRD (x-Ray Diffraction) 분석을 통하여 $400^{\circ}C$ 이상열처리 온도가 증가하면 금속 표면에 $NiO_2$가 형성되며, 이에 따라 오믹특성이 저하 된다고 사료된다. 또한 $Ni_3N$의 존재를 확인 하였으며 이는 nonpolar surface의 특성으로 인해 nitrogen out diffusion 현상이 동시에 발생하여 계면에는 dopant로 작용하는 질소 공공을 남기고 표면에 $Ni_3N$을 형성하여 ohmic contact의 특성이 저하되기 때문인 것으로 사료된다.

• 한국재료학회지
• /
• 제13권6호
• /
• pp.347-351
• /
• 2003

II-Ⅵ ZnO compound semiconductor thin films were grown on $\alpha$-Al$_2$O$_3$(0001) single crystal substrate by radical beam assisted molecular beam epitaxy and the optical properties were investigated. Zn(6N) was evaporated using Knudsen cell and O radical was assisted at the partial pressure of 1$\times$10$^{4}$ Torr and radical beam source of 250-450 W RF power. In $\theta$-2$\theta$ x-ray diffraction analysis, ZnO thin film with 500 nm thickness showed only ZnO(0002)and ZnO(0004) peaks is believed to be well grown along c-axis orientation. Photoluminescence (PL) measurement using He-Cd ($\lambda$=325 nm) laser is obtained in the temperature range of 9 K-300 K. At 9 K and 300 K, only near band edge (NBE) is observed and the FWHM's of PL peak of the ZnO deposited at 450 RF power are 45 meV and 145 meV respectively. From no observation of any weak deep level peak even at room temperature PL, the ZnO grains are regarded to contain very low defect density and impurity to cause the deep-level defects. The peak position of free exciton showed slightly red-shift as temperature was increased, and from this result the binding energy of free exciton can be experimentally determined as much as $58\pm$0.5 meV, which is very closed to that of ZnO bulk. By van der Pauw 4-point probe measurement, the grown ZnO is proved to be n-type with the electron concentration($n_{e}$ ) $1.69$\times$10^{18}$$cm^3$, mobility($\mu$) $-12.3\textrm{cm}^2$/Vㆍs, and resistivity($\rho$) 0.30 $\Omega$$\cdot$cm.

• 센서학회지
• /
• 제9권1호
• /
• pp.70-75
• /
• 2000

단결정 실리콘웨이퍼를 사용한 태양전지 제조에 있어 가장 큰 문제점은 재료의 높은 가격이다. 본 연구에서는 이러한 문제의 해결방안으로 현재 DRAM 소자 제조과정에서 폐기되는 웨이퍼를 리사이클링하여 태양전지를 제작하고 저가의 제조공정과 전지의 특성을 연구하였다. DRAM용 실리콘 웨이퍼는 비저항이 높고 두꺼워 태양전지 재료로서 부적합하나, 본 연구에서는 후면전계 (Back Surface Field) 형성, 표면 Texturing, 반사 방지막 형성 등의 공정들을 조합하여 효율향상을 위한 최적조건을 찾아내고, 두께변화에 따른 효율변화를 조사하였다. 최적화된 위의 모든 조건들을 적용하였을 때, $4\;cm^2$의 면적, $300\;{\mu}m$ 두께를 가지는 태양전지에서 단락전류밀도 ($J_{sc}$)는 $28\;mA/cm^2$, 개방전압 ($V_{oc}$) 0.51V, 충실도(Fill Factor)면에서는 0.53으로 가장 높은 값을 얻었고, 10% 이상의 효율을 확보할 수 있었다. 이와 같은 방법으로 폐기되는 실리콘 웨이퍼들을 재활용하여 실용성이 큰 저가의 단결정 실리콘 태양전지를 제작할 수 있는 방법을 확보할 수 있었다.