• The Korean Journal of Ceramics
• /
• v.7 no.1
• /
• pp.6-10
• /
• 2001

Ultrafine $(CeO_2)_{0.9}(Gd_2O_3)_{0.1}$ solid solution powders synthesized by the glycine-nitrate process, with specific surface areas of $19-23\;\textrm{m}^2$/g were sintered at $1500^{\circ}C$ for various sintering times and then their electrical characteristics were investigated using AC impedance and four-point probe measurements. The electrical resistivity of the sintered $(CeO_2)_{0.9}(Gd_2O_3)_{0.1}$ bodies showed the minimum value at the sintering time of 10 hrs. The minimum total resistivity of the $(CeO_2)_{0.9}(Gd_2O_3)_{0.1}$ bodies sintered at $1500^{\circ}C$ for 10 hrs seems to result from the lowest activation energy for the electrical resistivity by the combination between the activation energies for the resistivities at the grain interior and grain boundary.

• Transactions of the Korean hydrogen and new energy society
• /
• v.22 no.2
• /
• pp.161-167
• /
• 2011

Proton conductors have attracted considerable attention for solid oxide fuel cell (SOFC), hydrogen pump, gas sensor, and membrane separators. Doped $SrCeO_3$ exhibits appreciable proton conductivity in hydrogen-containing atmosphere at high temperature. However commercial realization has been hampered due to the reactivity of $SrCeO_3$ with $CO_2$. The chemical stability and proton conductivity are dependent on dopant type. The purpose of this work is to investigate chemical stability of $SrCe_{0.95}Gd_{0.05}O_{3-\alpha}-Ce_{0.9}Gd_{0.1}O_{2-\beta}$ composites in $CO_2$ and $H_2$ gases. Thermogravimetric analysis (TGA) was performed in gaseous $CO_2$ and electrical conductivity of the composites were also measured between 500 and $900^{\circ}C$ in air and $H_2$ atmosphere. $SrCe_{0.95}Gd_{0.05}O_{3-\alpha}-Ce_{0.9}Gd_{0.1}O_{2-\beta}$ composite membranes showed good chemical stability of in $CO_2$ atmosphere and high conductivity at hydrogen condition. The hydrogen permeation of $SrCe_{0.95}Gd_{0.05}O_{3-\alpha}-Ce_{0.9}Gd_{0.1}O_{2-\beta}$ composite membranes was investigated as a function of volumetric content of $SrCe_{0.95}Gd_{0.05}O_{3-\alpha}$. The $SrCe_{0.95}Gd_{0.05}O_{3-\alpha}-Ce_{0.9}Gd_{0.1}O_{2-\beta}$(6:4) membrane with a thickness of 1.0 mm showed the highest hydrogen permeability with the flux reaching of 0.12 $ml/min{\cdot}cm^2$ at $800^{\circ}C$ in 100%$H_2/N_2$ as feed gas.

• Journal of the Korean Ceramic Society
• /
• v.35 no.9
• /
• pp.981-987
• /
• 1998

$La_{0.5}Sr_{0.5}MnO_{3-\delta}$ as air electrode for soild oxide fuel cell was synthesized by a citrate process and its cathodic polarization was determinated by the current interruption method on the Gd-doped ceria as electrolyte. The addition of citric acid increased the exothermic heat for the formation of $La_{0.5}Sr_{0.5}MnO_{3-\delta}$ perovskite oxide. The degree of the initial particle agglomeration was affected by the exothermic heat. Also the increase of cal-cination temperature enlarged the particle size and the higher sintering temperature accelerated the den-sification of $La_{0.5}Sr_{0.5}MnO_{3-\delta}$ layer after its being painted on $Ce_{0.8}Gd_{0.2}O_{1.9}$ electrolyte. In this study $La_{0.5}Sr_{0.5}MnO_{3-\delta}$ synthesized by citrate process of which the molar ratio of citric acid to metal nitrate was 2 calcined at $650^{\circ}C$ for 2hr and sintered at 1100 at $1200^{\circ}C$ for 4 hrs after slurry coating on Ce0.8Gd0.2O1.9 electrlyte showed the lowest cathodic polarization.

• Transactions of the Korean hydrogen and new energy society
• /
• v.30 no.3
• /
• pp.209-219
• /
• 2019

Methanol is a liquid fuel which could also be produced from renewable energy sources and has appreciably high energy density. In this work, we investigated the application of $Ce_{0.9}Gd_{0.1}O_{2-x}$ supported Cu and Ni catalysts for hydrogen production via methanol steam reforming. Catalysts were synthesized by solution combustion synthesis. The prepared catalysts with various active materials and Cu loading amounts were tested in a reactor at $200-300^{\circ}C$, 0-5 barg range and steam to methanol molar ratio was 1.5. The catalytic properties of Cu and Ni were compared, and the catalytic performance was shown to depend on the amounts of metal loading and operating conditions such as reaction temperature and pressure.

• Journal of the Korean Ceramic Society
• /
• v.47 no.2
• /
• pp.183-188
• /
• 2010

$Ce_{0.8}Gd_{0.2}O_{1.9}$(GDC20) powder was synthesized by milling of $CeO_2$ slurry and Gd oxalate precipitation. The mixture of $CeO_2$ powder and Gd precipitates calcined at $600^{\circ}C$ for 2 h showed the particle size distribution similar to that of $CeO_2$ powder, which had been milled during the synthesis process. Attrition milling of the calcined powder with an average particle size of $0.36\;{\mu}m$ for 2 h resulted in a decrease in the particle size to $0.24\;{\mu}m$. Although the milled powder consisted of small particles(<$1\;{\mu}m$), a small amount of fine platy $Gd_2O_3$ particles, which had been survived in the milling process, was observed. Sintering of the powder compacts for 4 h showed relative densities of 80.7% at $1300^{\circ}C$ and 97% at $1400^{\circ}C$, respectively. Densification was found to almost complete at $1500^{\circ}C$, resulting in a dense and homogeneous microstructure with a relative density of 99.5%.

• Korean Journal of Materials Research
• /
• v.17 no.10
• /
• pp.526-531
• /
• 2007

The sintering behavior and electrical property of $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics were investigated with the iron oxide concentration ranging from 0 to 5 mol%. Both the sintered density and grain size were found to increase up to 2 mol% $Fe_2O_3$, and then to decrease with further additions. At a higher $Fe_2O_3$ content above 3 mol%, grain size decreased by a pinning effect induced by different shape grains. The electrical conductivity was also increased with increasing $Fe_2O_3$ content up to 2 mol%. Total conductivity of 2 mol% $Fe_2O_3-added$ specimen showed the maximum conductivity of $2{\times}10^{-2}{\Omega}{\cdot}cm^{-1}$ at $500^{\circ}C$. The addition of $Fe_2O_3$ was found to promote the sintering properties and electrical conductivities of $Gd_2O_3-dope\;CeO_2$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.2
• /
• pp.145-152
• /
• 2006

The densification behavior and electrical conductivity of $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics were investigated with the strontium gallate concentration ranging from 0 to $5\;mol\%$. Both the sintered density and grain size were found to increase rapidly up to $0.5\;mol\%$ $Sr_2Ga_2O_5$, and then to decrease with further addition. Dense $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics with $97\%$ of the theoretical density could be obtained for $0.5\;mol\%$ $Sr_2Ga_2O_5$-added specimen sintered at $1250^{\circ}C$ for 5 h, whereas pure $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics needed to be sintered at $1550^{\circ}C$ in order to obtain an equivalent theoretical density, Electrical conductivity was measured as a function of dopant content, over the temperature range of $350\;-\;600^{\circ}C$ in air. Total conductivity of $0.5\;mol\%$ $Sr_2Ga_2O_5$-added specimen showed the maximum conductivity of $2.37{\times}10^{-2}{{\Omega}-1}{\cdot}cm^{-1}$ at $500^{\circ}C$, The addition of strontium gallate was found to promote the sintering properties and electrical conductivities of $Gd_2O_3$-doped $CeO_2$.

• Journal of the Korean Ceramic Society
• /
• v.38 no.1
• /
• pp.45-51
• /
• 2001

고체산화물 연료전지의 삼상 계면의 길이를 증가시키기 위해 Glycine-Nitrate Process(GNP)를 이용하여 환원극 재료인 L $a_{0.5}$S $r_{0.5}$Mn $O_3$(LSM)과 전해질 재료인 C $e_{0.8}$G $d_{0.2}$ $O_{1.9}$(CGO)를 합성하였다. 적당한 합성조건을 찾기 위하여 글리신의 양을 달리하여 분말을 합성한 결과 LSM의 경우 글리신이 양이온 몰수의 2배일 때 perovskite상이 얻어졌으며 비표면적은 34$m^2$/g 이었다. 합성된 LSM과 CGO 분말을 50:50 wt%로 혼합하여 제작된 환원극을 screen-printing법으로 코팅한 후 각각 1200, 1300, 1350 및 140$0^{\circ}C$에서 4시간 동안 소결한 후 80$0^{\circ}C$에서 power density와 양극과전압 등을 측정한 결과 130$0^{\circ}C$에서 소결한 단위전지에서 최대 309 mW/$ extrm{cm}^2$의 power density를 얻을 수 있었다.다.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.521-526
• /
• 2015

$Ce_{0.8}Gd_{0.2}O_{1.9}$(GDC20) powder was prepared from a mixture of submicron-sized $CeO_2$ powder and Gd precipitates using ammonium carbonate $((NH_4)_2CO_3)$ as a precipitant. The mixture was calcined at $700^{\circ}C$ for 4 h followed by ball-milling that resulted in the GDC powder with an average particle size of $0.46{\mu}m$. The powder had a very uniform particle size distribution with particle sizes ranging from $0.3{\mu}m$ to $1{\mu}m$. Sintering of undoped GDC samples did not show a relative density of 99.2% until the temperature was increased to $1500^{\circ}C$, whereas GDC samples doped with 5 mol% CoO exhibited a significant densification at lower temperature reaching a relative density of 97.6% at $1100^{\circ}C$ and of 98.8% at $1200^{\circ}C$.

• Progress in Superconductivity
• /
• v.13 no.3
• /
• pp.163-168
• /
• 2012

The effects of Ta substitution on the superconducting and magnetic properties of the $(Ru_{1-x}Ta_x)Sr_2(Gd_{1.4}Ce_{0.6})Cu_2O_z(0{\leq}x{\leq}0.5)$ system have been investigated. The X-ray diffraction measurements indicate that the Ta ion replaces Ru sites up to x = 0.4. It is found that the Ta substitution for Ru significantly reduces the weak-ferromagnetic component of the field-cooled magnetic susceptibility without an appreciable change of room temperature thermopower at lower Ta doping level below x = 0.2. The resistive transition temperature tends to decrease monotonically from 27 K for the x = 0 sample to 16 K (9 K) for the x = 0.4 (x = 0.5) sample. These results suggest that superconductivity of the $(Ru_{1-x}Ta_x)Sr_2(Gd_{1.4}Ce_{0.6})Cu_2O_z$ compound is not significantly affected by the magnetic state of the Ru sublattice. The experimental results are discussed in connection with previous reports on the effects of Nb substitution.