• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.28 no.2
• /
• pp.80-84
• /
• 2015

We investigated the dielectric relaxation properties $0.5Ba(Zr_{0.2}Ti_{0.8})O_3-0.5(Ba_{0.7}Ca_{0.3})TiO_3$ ceramics with CuO addition. With increasing CuO addition, the lattice parameter was increased by substitution of small amount $Cu^{2+}$ ion in B-site of $0.5Ba(Zr_{0.2}Ti_{0.8})O_3-0.5(Ba_{0.7}Ca_{0.3})TiO_3$ ceramics. Also the grain size and the maximum dielectric constant of $0.5Ba(Zr_{0.2}Ti_{0.8})O_3-0.5(Ba_{0.7}Ca_{0.3})TiO_3$ ceramics was decreased with increasing amounts of CuO addition. Moreover, the diffused phase transition properties (${\gamma}$) of $0.5Ba(Zr_{0.2}Ti_{0.8})O_3-0.5(Ba_{0.7}Ca_{0.3})TiO_3$ ceramics was increased by compositional fluctuation with increasing of CuO amount, changed from 1.45 at 1 wt% CuO addition to 1.94 at 7 wt% CuO addition.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.180-181
• /
• 2009

$(Ba_{0.6},Sr_{0.3}Ca_{0.1})TiO_3$ powders, which were prepared by sol-gel method using a solution of Ba-acetate, Sr-acetate and Ca-acetate and Ti iso-propoxide, $(Ba_{0.6},Sr_{0.3}Ca_{0.1})TiO_3$ array thick films doped with 0.1 mol% $MnCO_3$ and $Yb_2O_3$ (0.1~0.7 mol%) were fabricated by the screen printing method on the alumina substrate. And the structural and electrical properties as a function of $Yb_2O_3$ amount were investigated. The thickness of all (Ba,Sr,Ca)$TiO_3$ thick films was approximately 60mm. The Curie temperature of doped with 0.1 mol% $Yb_2O_3$ specimen was $45^{\circ}C$, and the dielectric constant and at this temperature was 1062.

• Journal of the Korean Ceramic Society
• /
• v.40 no.1
• /
• pp.37-45
• /
• 2003

The dielectric and sintering characteristics of composites made by substituting Ca ion to Ba-site and Zr ion to Ti site in $(Ba{1-x}Ca_x)(Ti{0.96-yZr_ySn_{0.04})O_3$ $(0.15{\leq}x{\leq}0.20,\;0.09{\leq}y{\leq}0.14)$ were investigated. As the content of Ca was more than 15 mol%, composite was formed by precipitating the second phase whose main element was $CaTiO_3$ and the fraction of the second phase was increased. The curie temperature of composites was depended on Ca concentration, $-1.7^{\circ}C$ per mol% and the maximum dielectric constant of composite was decreased by the rate of 200/mol%. The substitution of Zr ion decreased the curie temperature by the rate of $10^{\circ}C$ per mol% and the maximum dielectric constant was decreased by 217/mol% due to the increase of diffuse phase transition. The density and insulation breakdown characteristics were improved by suppressing the abnormal grain growth due to the increase of second phase. We developed the composition of Y5U (EIA standard) condenser which had high breakdown voltage and dielectric constant by controlling diffuse phase transition by the addition of Zr ion into composite.

• Journal of the Korean Ceramic Society
• /
• v.38 no.3
• /
• pp.280-286
• /
• 2001

10 이하의 저유전율을 갖는 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스의 미세구조와 고주파 유전특성을 조사하였다. (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스는 정방정(tetragonal) 구조를 가진다. 0.1BaWO$_4$-0.9Mg$_2$SiO$_4$세라믹스는 BaWO$_4$와 $Mg_2$SiO$_4$의 상들이 공존하는 혼합상을 보였으며, $Mg_2$SiO$_4$가 이차사으로 형성된 것이 관찰되었다. 120$0^{\circ}C$~140$0^{\circ}C$에서 2시간 동안 소결된 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x=0.1~0.9) 세라믹스는 $\varepsilon$$_{r}$=6.37~8.21, Q.f=15000~99422 그리고 $ au$$_{f}$=73.9~48.9 ppm/$^{\circ}C$의 고주파 유전특성을 가졌다. $\tau$$_{f}$를 보정하기 위해, CaTiO$_3$(1,5 wt%)가 (1-x)BaWO$_4$-xMg$_2$SiO$_4$(x$\geq$0.9) 세라믹스에 첨가되었다. 135$0^{\circ}C$에서 2시간 동안 소결된 0.1BaWO$_4$-0.9Mg$_2$SiO$_4$+CaTiO$_3$(5 wt%) 세라믹스는 $\varepsilon$$_{r}$=7.3, Q.f=30532 그리고 $\tau$$_{f}$=-30 ppm/$^{\circ}C$의 고주파 유전특성을 얻었다. 얻었다.

• Journal of the Korean Ceramic Society
• /
• v.23 no.1
• /
• pp.7-12
• /
• 1986

Dielectric properties of $Ba_{0.9}Ca_{0.1}(Ti_{1-x}Sn_x)O_3$ were investigated from x=0 to 0.20, and temperature range -4$0^{\circ}C$~13$0^{\circ}C$ Density and grain size decreased with increasing Sn content due to grain growth inhibitor. Dielectric constant below the Curie temperature increased with increasing Sn content and dissipation factor dec reased. These results are due to grain size effect and internal stress. Curie temperature was shifted to lower temperature with increasing ratio of total polarizability to volume resulting from substitution of $Ba^{2+}$ ion with $Ca^{2+}$ ion $Ti^{4+}$ ion with $Sn^{4+}$ ion.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.8
• /
• pp.680-684
• /
• 2007

In this study, we investigated the effects of structural and electrical properties of $(Ba_{0.6},\;Sr_{0.3},\;Ca_{0.1})TiO_3$ thick films with variation $Dy_2O_3$ contents. $(Ba_{0.6},\;Sr_{0.3},\;Ca_{0.1})TiO_3$ powders, prepared by the sol-gel method, were mixed organic vehicle. The BSCT thick films doped with 0.1, 0.3, 0.5, 0.7 mol% $Dy_2O_3$ were fabricated by the screen-printing techniques on the alumina substrates and the structural and dielectric properties were investigated with variation of $Dy_2O_3$ doping contents. All BSCT thick films were sintered at $1420^{\circ}C$, for 2hr. In the TG-DTA analysis, the formation of the polycrystalline perovskite phase was observed at around $670 ^{\circ}C$. In the XRD analysis, all BSCT thick films showed the cubic perovskite structure. The average thickness of BSCT thick films was approximately $65{\mu}m$. The Curie temperature decreased with increasing $Dy_2O_3$ amount. The relative dielectric constant and dielectric loss of BSCT thick films doped with $Dy_2O_3$ 0.1 mol% were 6267 and 2.6 %, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.7
• /
• pp.645-651
• /
• 2008

To reduce noise in high frequency and distortion of signal, the composition of $(Ca_{0.7}Sr_{0.3})(Zr_{0.97}Ti_{0.03})O_3$ and $(Ba_{0.2}Ca_{0.4}Sr_{0.4})TiO_3$ was developed. The composition was not solid solution, but mixtures of various phases composed of Ca, Sr, Zr, Ti and Ba oxides. The dielectric constant increased, the quality factor and the insulation resistance decreased with $(Ba_{0.2}Ca_{0.4}Sr_{0.4})TiO_3$ content. The composition of $0.4(Ba_{0.2}Ca_{0.4}Sr_{0.4})TiO_3$ satisfied the electric characteristics and the temperature coefficient of dielectric constant (TCC). In addition, the glass frit and $MnO_2$ also affected the electric characteristics. From the result of the best fit simulation, $MnO_2$ 0.3 mol%, the glass frit 0.6 wt% showed the insulation resistance $906{\Omega}{\cdot}F$, the quality factor 821, and the dielectric constant 92. With the selected composition, MLCC capacitors sized $4.5{\times}3.2{\times}2.5mm$ were manufactured with 105 layered of the dielectric thickness $16{\mu}m$ using Ni inner electrode, They represented the capacitance $98{\sim}102$ nF, the quality factor 1,200 and the insulation resistance $1,500{\Omega}{\cdot}F$. Also, they had high break-down voltage with $107{\sim}115V/{\mu}m$, and satisfied the SL TCC characteristics.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.7
• /
• pp.404-407
• /
• 2016

In this study, to develop low temperature sintering capacitor composition ceramics with the good dielectric properties, $(Ba_{0.86}Ca_{0.14})(Ti_{0.85}Zr_{0.12}Sn_{0.03})O_3$ (BCTZ) ceramics were prepared by the conventional solid-state reaction method. The effects of $B_2O_3$ addition on the dielectric properties and microstructure was investigated. The XRD patterns demonstrated that all the specimens showed Perovskite phase, and secondary phases are indicated in the measurement range of XRD. And also, temperature coefficient of capacitance(TCC) of all the specimen sintered at $1,180^{\circ}C$ showed +3~-56% except for x=0.006. For all the specimens, observed one peak was tetragonal cubic difuse phase transition temperature(Tc), which is located in the vicinity of room temperature.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.7 no.2
• /
• pp.253-258
• /
• 1997

The characteristics of crystal structure and phase transition with dopants ($Nb_2O_5$= 0.1~0.4 mol% and $Y_2O_3$ : 0.2~0.4 mol%) on the PTCR $BaTiO_3$ system were investigated. In the case of $Nb_2O_5$ additive, the lattice parameter of PTCR $BaTiO_3$ was changed linearly with the increasement of $Nb_2O_5$ which substituted B-site of BaTiO$_3$ and the lattice parameter of c-axis decreased abruptly at 0.3 mol%. These phenonmena were assumed to originate from the distortion of octahedron and we could confirm that the change of lattice parameter accorded with the characteristics of the phase transition temperature. $Y^{3+}$ ions substituted both of A- and B-site until the 0.3 mol% addition, but $Y^{3+}$ substitution preferred A- to B-site above 0.3 mol%. This was affirmed by the variation ,of lattice parameter and the characteristics of phase transition. It also was found that $Y^{3+}$ions in the A-site substituted both of $Ba^{2＋}$ and $Ca^{2＋}$ ions with equal ratio by Rietveld method.

• The Transactions of the Korean Institute of Electrical Engineers
• /
• v.43 no.7
• /
• pp.1144-1151
• /
• 1994

The humidity-sensitive specimens-(BaS11T-S1xTCaS1xT)TiOS13T, x=0, 0.1, 0.2, 0.3, 0.4, 0.5-were fabricated by a solid-state reaction method which is easy in process control of microstructure and good in mass production, and their humidity-sensitive characteristics were examined. Ca inhibits grain growth and the open porosity increases with Ca substitution, and the specimens at x=0.5 show the best humidity sensitivity. Their humidity sensitivity is higher at the lower frequencies, and drift phenomenon in humidity sensitivity is exhibted with aging in the air, which disappears by a heat treatment. The electrical conduction with water adsorption is dominated by the ions, and the activation energy decreases with increasing relative humidity.