A Study on the Mechanical Properties as a Result of Friction Welding With SKH55 and SM45C  

Choi, Su-Hyun (충남대학교 교육대학원)
Min, Byung-Hoon (충남대학교 교육대학원)
Kim, Noh-Kyung (충남대학교 교육대학원)
Lim, Hyung-Taek (충남대학교 대학원)
Min, Taeg-Ki (충남대학교 기계공학과)
Publication Information
Transactions of the Korean Society of Machine Tool Engineers / v.17, no.2, 2008 , pp. 65-70 More about this Journal
Abstract
This study deals with the friction welding of SKH55 and SM45C; The friction time was variable conditions under the conditions of spindle revolution 2,000rpm, friction pressure of 190MPa, upset pressure of 270MPa and upset time of 2.0 seconds. Under these conditions, the microstructure of weld interface, tensile fracture surface and mechanical tests were studied, and so the results were as follows. 1. When the friction time is 1.0 seconds, the tensile strength of friction welds was 926MPa, which is around as much as 84% of the tensile strength of base metal(SKH55), the bending strength of friction welds was 1,542MPa, which is around as much as 80% of the bending strength of base metal(SKH55), the shear strength of friction welds was 519MPa, which is around as much as 70% of the shear strength of base metal(SKH55). 2 According to the hardness test, the hardness distribution of the weld interface was formed from 964Hv to 254Hv. HAZ(Heat Affected Zone) was formed from the weld interface to 1.5mm of SKH55 and 2mm of SM45C.
Keywords
Friction welding; Friction time; Friction pressure; Tensile strength; SKH55; SM45C;
Citations & Related Records
Times Cited By KSCI : 2  (Citation Analysis)
연도 인용수 순위
1 Yang Min-Tang, 1988, "Optimization of cutting tool for high speed machining," Transaction of KSME, Vol. 12, No. 6, pp. 1290-1295   과학기술학회마을
2 Cheng, C. J., 1962, "Transient Temperature Distribution During Friction Welding of Two Similar Materials in Tubular Form," Welding Research Supplement, Vol. 41, No. 12, pp. 542s-550s
3 Min Taeg-Ki, 1992, "Properties of Friction Welding Between the Back Metal of Bushing Part and Flange Part in A-Sn Alloy Metal Bearing," Dong-A University, Busan, Korea, pp. 4-5
4 Cheng, C. J., 1963, "Transient Temperature Distribution During Friction Welding of Two Similar Materials in Tubular Form," Welding Research Supplement, Vol. 42, No. 5, pp. 233s-240s
5 Park Keun-Hyung, Min Taeg-Ki, Yoon Young-Joo, and Park Chang-Soo, 2006, "A Study on the Joint Properties according to the Friction Welding Area Change of Carbon Steel(SM45C)," Transaction of KSMTE, Vol. 15, No. 1, pp. 102-107   과학기술학회마을
6 Vill, V. I., 1957, "Friction Welding of Metals," American Welding Society, Vol. 3, No. 9, pp. 8-23
7 Komanduri, R., Schroeder, T. A., B. F. Von Turkovich, and Flow, D. G., 1982, "On the Catastrophic Shear Instability in the High Speed Machining of an AISI 4340 Steel," Trans. ASME, J. of Eng. for Ind., Vol. 104, pp. 121-131   DOI