This test was attempted to investigate the effects of some mix designs of concreteon the compressive strengths and corrosive rates when exposed to sea water of the West Sea. In this test, concrete mixes consisted of an ordinary concrete, a pozzolan concrete and concretes with different admixtures such as fly ash, pozzolith and vinsol resin. Compressive strengths of the concrete were measured at ages of 1-year and 2-years when exposed to both sea water and fresh water. Corrosive rate was tested at ages of 1-year and 2-years when exposed to sea water only. The results obtained from the test may be summarized as follows: (1) When all of concretes were exposed to fresh water, compressive strength of an ordinary concrete was the lowest at all mixes of concretes, and all of them showed higher strength as the exposing age is longer. It was evidance that the uses of pozsolan cement, fly ash, pozzolith and vinsol resin in mix design of concrete had an effect on increasing compressive strength and that fresh water also had an effect on curing concretes even though at a long-time age. (2) When concretes were exposed sea water, a concrete with fly ash was the highest in compressive strength and its strength was increasing as the exposing age is longer, but the other concretes were decreased at 2-year exposure. It was found that a concrete with fly ash was the most effective on compressive strength of all concrete, but the other concretes were attacked by action of the sea water. (3) The use of vinsol resin admixture was the most resistant to corrosion by sea water, while the use of pozzolith was the most serious at corrosion and the others were corroded to almost same extent. (4) The relationship between corrosions and compressive strengths of concretes was not clearly correlated yet. It was known that the corrosive rate of concretes could not affect to compressive strengths by 2-year exposure of the sea water. (5) Pozzolan concrete was the most effective in compressive strength when exposed to fresh water only, However, the use of a fly ash admixture was available for compressive strength when exposing to both fresh water and sea water. It was also noticed that the use of vinsol resin was not available for strengths of concrete but for resistance to corrosion when exposed to sea water. (6) It was found that the use of pozzolith was so defective in compressive strengths and corrosiive resistance when exposing to sea water that it was only available for fresh water.

Following are the results of the study on the property of falling permeation of stratified soil in the close state under existence of stagnant water on a soil layer. 1. When on the stratified soil a least permeating layer was put on the soil layer the load Pressure was present owing to appearance of saturation close state driving decrease of the pressure in the lower layer, on the other hand when the least permeating layer was placed under the layer the lower least permeating layer pressure was decreased. 2. In the case of least permeating layer the variation of current gradient according to the respective level after treating the layer was enormous and due to usal storage phenomena for the Kl layer which was coarse that was trifle. 3. The permeability of the respective layer of stratified soil in the close state died not always coincide with that of single layer. 4. Generally Zunker's equation of average permeability was valid but actually calculated permeating velocity after treating the layer of stratified soil was seriously differ from the measured value owing to the variation of current gradient, especially when the pressure head at the layer boundany was discontinuous the validity of the equation of average permeability was seemed to be doubtful. 5. The permeating velocity of stratified soil was regulated by the least permeating layer, i.e. it is thought to be rational to estimate the value by calculating the current gradient with its proper permeability, pressure headon the layer and its thickness.

This study was attempted in order to search for physical properties of sail cement. In this study, soil samples were specified according to soil particle analysis and used for compaction, strength, abrasion, absorption tests respectively according to different cement contents. Cement content sused in each treatment were 6%, 8%, 10% and 12% of total weight of soil-consent mixture. In the test, compressise strengths of the specimens were measured at the following ages; 3 days, 7-days, 14-days, 21-days and 28-days. Abrasion and absorption tests of the specimens were carried out at the 7-days age only. The results obtained from the tests are summarized as follows; 1. As the cement contents were in creased, the compressive strengths of soil-cement were almost proportionally increased. 2. The Compressive strength of soil-cement was not always proporportional to ages. The gradient of compressive strength of the soil-cement was steeper as the cement content was rucreased. 3. As the cement content was increased, the amount of the weight loss of the samples due to the abrasion was decreased remarkably, giving no abrasion for about 8% of the cement content. 4. As the cement content was increased, the absorption ratio of the specimens was not changed remarkably.

Maximum density and optimum moisture content of a soil may be one of the very important properties to be specified in the design of earth structures and their works. However, the determination of these soil properties may not be done without the necessary equipment and time-consuming field tests. This study was conducted to develop an easier method by determing the relations between the natural moisture content and optimum moisture content and between maximum density and optimum moisture content so determined. These velations are remarkably defferent according to the areas where the samples were taken, and thus analysis of the experimental results are shown by regions as follows: Eastern Districs:{{{{Tdmax= { 1} over {0.0090Wopt+0.417 } ( delta = +- 0.042, gamma =0.92) Wopt=0.251WN+8.5( delta = +- 2.41%, gamma =0.87) }}}} Southern Districts: {{{{Tdmax= { 1} over {0.0088Wopt+0.412 } (delta = +- 0.083, gamma =0.89) Wopt=0.332WN+8.42(delta = +- 3.41%, gamma =0.84)}}}}Central Districtsl1): {{{{Tdmax= { 1} over {0.0112Wopt+0.383} ( delta = +- 0.052, gamma =0.97) Wopt=0.758WN+2.606( delta = +- 4.72%, gamma =0.79)}}}}($\delta$:Standard Deviation, ${\gamma}$:Correlation Coefficient)