An emulsion of octadecamidoethylaminoethyl dodecate (which provides softness) and an emulsion silicone oil KF-96 (which provides lubricity) were separately synthesized. Then PP finishing softeners (SSA-7) was prepared by blending of the synthesized emulsions with beef tallow hardened oil (a softness improving agent). PP finishing treatment was carried out with the prepared SSA-7 and PP finishing resin by a one bath method, and several physical properties were tested. As a result, crease recovery, tear strength, softness, lubricity, and bending resistance were all good, indicating that the prepared SSA-7 is a good PP finishing softener.

Acrylic resins ($HSC_s$ : EA/EMA/2-HEMA/CLA) which contain 70% solid content were synthesized by the copolymerization of monomers (2-hydroxyethyl methacrylate, ethyl acrylate, and ethyl methacrylate) and functional monomer (caprolactone acrylate : CLA) which improves the crosslinking density and physical properties of films. The physical properties of the prepared acrylic resins (HSCs) containing CLA, are as follows : viscosity 245${\sim}$515 cps ; $M_n$ 2670${\sim}$2840 ; and conversions, 83${\sim}$91%, respectively. From the correlation of $T_g$ values, viscosities, and $M_n$ of the HSCs, it was found that viscosity and $M_n$ increased with $T_g$ value.

Extraction of Sedum sarmentosum Bunge by super critical carbon dioxide was operated under $40-50^{\circ}C$and 200-250 atm, thus, yield of extraction was very low as 4 wt%. Rats were administrated with the extract orally once a day for succesive 6 days, followed by treatment with carbon tetrachloride ($CCl_4$) on the sixth day. The activities of aminotransferase, alkaline phosphatase, ${\gamma}$-glutamyl transpeptidase, lactate dehydrogenase and contents of triglyceride, total cholesterol in the extract-pretreated rats were decreased compared to the $CCl_4$controled rats, whereas content of HDL-cholesterol was increased. Especially content of hepatic malondialdehyde (MDA) and atherogenic index (AI) were decreased and HTR was increased in the extract-pretreated rats, and reduced peroxidative liver damage in the $CCl_4$-induced hepatotoxicity rats. In addition, activities of hepatic superoxide dismutase, catalase, glutathione peroxidase in the extract-pretreated rats were significantly decreased compared to the $CCl_4$ controled rats, but the content of glutathione was significantly increased. These results suggest that extract of Sedum sarmentosum Bunge has hepatoprotective effect in the $CCl_4$-intoxicated rats.

Although the structure of carbon nanotubes is important factor characterizing its properties, it is very difficult to control the structure of carbon nanotubes (MWNTs) and to predict the range of their diameter, which is the primary factor of MWNTs' physical properties. We tried to control the diameter of MWNTsby governing the feed injection temperature of floating catalyst method. The structure of MWNTs was influenced by the phase change of ferrocene fed as the catalyst,. The carbon nanotubes were very narrow at injection temperatures close to the sublimation pt. of ferrocene, in which most MWNTs had diameters in the range of 20$^{\sim}$30 nm. At injection temperatures between the boiling pt. and melting pt. of ferrocene, the diameters became larger and had broad distribution. However, at injection temperatures higher than the boiling pt., the diameters became narrow again and had very uniform distribution.

Synthesis gas is a high valued compound as a basic chemicals at various chemical processes. Synthesis gas is mainly produced commercially by a steam reforming process. However, the process is highly endothermic so that the process is very energy-consuming process. Thus, this study was carried out to produce synthesis gas by the partial oxidation of methane to decrease the energy cost. The effects of reaction temperature and flow rate of reactants on the methane conversion, product selectivity, product ratio, and carbon deposition were investigated with 13wt% Ni/MgO catalyst in a fluidized bed reactor. With the fluidized bed reactor, $CH_4$ conversion was 91%, and Hz and CO selectivities were both 98% at 850$^{\circ}C$ and total flow rate of 100 mL/min. These values were higher than those of fixed bed reactor. From this result, we found that with the use of the fluidized bed reactor it was possible to avoid the disadvantage of fixed bed reactor (explosion) and increase the productivity of synthesis gas.

Ga-MFI was synthesized by a hydrothermal process at atmospheric pressure. The effect of mole ratios of reactants on crystallization was also investigated thoroughly. The characteristics of synthesized Ga-MFI was compared with ZSM-5. The synthesis of Ga-MFI was carried out with five different mole-compositions of $\underline{a}SiO_2-\underline{b}Ga_2O_3-\underline{c}Na_2O-\underline{d}TPA_2o-\underline{e}H_2O$. The synthesized Ga-MFI and ZSM-5 were characterized by XRD and FT-IR. The inorganic cation ($Na^+$) and water played an important role in crystallinity and the organic cation ($TPA^+$) as a template played a great influence on yields. With the increase in the amount of $Ga^{3+}$, crystallization time was increased. With a fixed $SiO_2/Ga_2O_3$ ratio of 400, the optimum reaction condition was obtained at $H_2O/SiO_2$=30${\sim}$35, $Na_2O/SiO_2$=0.5${\sim}$0.6, and $TPA_2O/Na_2O$=1${\sim}$1.25. In these cases, the crystallinity and yield were more than 95% and 90%, respectively. By comparing IR spectrum of Ga-MFI with those of ZSM-5 and silicalite, it was found that Ga-MFI showed a unique peak at 970 $cm^{-1}$, which may be used to identify Ga-MFI from ZSM-5 and silicalite.

The interaction between anion and zwitterionic surfactants was investigated by means of surface tension, NMR spectroscopy, and fluorescence studies. These systems are N-tetradecyloxymethyl-N,N-dimethyl betaine ($C_{14}$, TDB), N-octadecyloxymethyl-N,Ndimethyl betaine ($C_{18}$, ODB), and sodium dodecylethoxy sulfate (SDE). These systems show a composition dependency in micellar properties. When the molar fraction of TDB and ODB was about 0.6, the cmc values of these systems showed minima, whereas the solubilized amount of a water insoluble dye, NMR line width showed maxima. These changes comes from the intramolecular complexes formed in the mixed micelles. The complexes are due to the electrostatic interaction of oppositely charged head groups of betaine and sodium dodecylethoxy sulfate. A comparison of betaine and SDE alkyl methylene group line widths to those of n-methyl group indicates that the interior of the micelle in the restricted region is more immobile than the head group.

Diazotization of three aminopyridine such as 3-amino-2-chloropyridine, 5-amino-2-chloropyridine, and 3-aminopyridine were investigated. Preparation of pyridinediazonium tetrafluoroborates were carried out employing two different methods. Diazotization of aminopyridines with a chlorine substituent in the pyridine ring were conducted in acidic aqueous solution with sodium nitrite in 70% and 74% yields respectively. 3-Pyridinediazonium tetrafluoroborate without any ring subsituent was unstable in an aquous solution and the diazotiation of 3-aminopyridine was proceded in an anhydrous methylene chloride-etherial $BF_3$ solution with tert-butyl nitrite in 40% yield.

This study was performed to evaluate characteristic of acid mine drainages (AMD) from abandoned mines in Kangwon-Do. Youngdong abandoned mine, and Soo and Hambaek abandoned mines in Hamtae were selected for this study. Average pHs of the mine drainages were 3-6.5, and those of Youngdong and Hambaek drainages were very acidic as 3-4. $SO_4^{-2}$ of Youngdong and Hambaek drainages were over 1,600 mg/L, which higher than average value (845 mg/L) of acid mine drainages in nationwide. Cu, Mn, and As concentrations of the drainages were lower than ‘Pollutant Discharge Permission'. Fe concentrations of Youngdong and Hambaek drainages were approximately 96 mg/L, which were two times higher than average value in nationwide. From correlation analysis using SPSS, significant correlation was not discovered between 'contaminants' analyzed in three acid mine drainages.

Film properties of monodispersed model composite latexes with particle size of 190 nm, which consist of n-butyl acrylate as a soft phase monomer and methyl methacrylate as a hard phase monomer with different morphology was examined. Five different types of model latexes were used in this study such as random copolymer particle, soft-core/hard-shell particle, hard-core/soft-shell particle, gradient type particle, and mixed type particle. Tensile strength and tensile elongation at break of final films were evaluated. Those properties can be interpreted in terms of PBA/PMMA phase ratio and their morphology. The interfacial adhesion strength was also evaluated using $180^{\circ}$ peel strength measurement and cross hatch cutting test.