Abstract
Many coating technologies have been developed so far to improve the corrosion resistance, strength, abrasion resistance and other surface properties of materials and equipment. Among them, the formation of CCO (CaCoO, then CCO) thin films has been studied and used in the electronic material field. One of the characteristics of CCO thin films is that it is resistant to high temperature heat. Particularly, the method of forming the CCO thin film is relatively simple, and it was judged that it could be introduced into the existing equipment. Therefore, in this study, an experiment and analysis were carried out to determine whether the coating of CCO thin films can be applied to hot dip galvanizing facilities. A CCO thin film was formed on the surface of STS304 base material and oxidized in a Zn fume atmosphere in a $650^{\circ}C$ furnace with an air atmosphere. Oxidation was carried out for 30 days, after which the shape of the CCO thin film was confirmed by SEM and its corrosivity was analyzed through a potentiodynamic polarization experiment.
산업의 발전에 따라 설비 및 재료 등 따라서 재료 표면의 특성을 내식성 및 고강도, 내마모성 등을 향상 시키기 위하여 지금까지 많은 코팅 기술들이 발전해 왔다. 그 중 CCO(CaCoO, 이후 CCO) 박막 형성은 전자재료 영역에서 연구, 사용이 되어오고 있는데, 이 CCO 박막의 특징 중 하나가 고온의 열에 강하다는 것이 있다. 특히 CCO 박막을 형성 시키는 방법 또한 비교적 간단하여 고온의 산화 분위기에 도입이 가능 할 것으로 판단되었다. 따라서 본 연구에서는 이 CCO 박막의 코팅이 용융 아연 도금 설비에 적용을 하기 전에, 고온 및 Zn fume에 대한 부식성을 파악하여 용융 아연 도금 설비에 적용이 가능한지를 파악하기 위한 실험 및 분석을 실시 하였다. 우선 기본 소재 STS304 표면에 CCO 박막을 형성 시키고, 650도의 대기로에서 Zn fume의 분위기 내에서 산화 시킨 후 CCO 박막의 부식 정도를 확인 및 측정 하였다. 산화는 30일간 진행되었고, 30일 후 SEM을 이용하여 CCO박막의 형상을 확인 하였으며 동전위분극 실험을 통하여 부식성을 분석하였다.