Abstract
This experimental study is purposed to analyze the effect of alkaline aqueous solution by electrolysis on strength development in order to develop high volume cement matrix using industrial by-products. Blast furnace slag was used a binder, and an alkaline aqueous solution obtained by electrolyzing pure water was used as an alkali activator. The hydration properties of these specimens were then investigated by compressive strength test, XRD and observation of micro-structures using SEM. As a result, we found that compressive strength increased with the addition of alkaline aqueous solution which cement matrix incorporating blast furnace slag. But those strength decreased reversely when replacing ratio of blast furnace slag was increased. It is judged that results of engineering properties evaluation on the binder and alkaline aqueous solution are useful as a basic data for mixtures design and evaluation properties of high volume cement matrix using by-products.
본 연구는 $CO_2$를 다량 발생시키는 시멘트의 사용량을 줄이기 위한 일련의 연구로서, 산업부산물인 고로슬래그 미분말을 다량 치환하고 기존 알칼리 자극제를 대체하여 전기분해한 알칼리 수용액을 사용한 하이볼륨 시멘트 경화체의 개발을 위한 기초적인 연구를 수행하였다. 즉, 일반적인 시멘트를 사용한 시험체와 고로슬래그 미분말 40%, 60%에 일반적인 물과 전기분해 알칼리 수용액을 사용한 시험체에 대하여 압축강도, XRD 및 SEM을 측정하였다. 그 결과, 고로슬래그 미분말을 사용하는 경화체에 있어서 알칼리 수용액을 사용할 시 강도가 증가하고 입자 표면에 수화물이 다량 생성되는 결과를 얻었다. 특히, 고로슬래그 미분말을 40% 치환하고 알칼리 수용액을 사용한 경우, 일반적인 시멘트 경화체 보다 높은 압축강도를 발현하였다. 그러나 본 연구는 재령 10일에 한정하여 실시한 연구로서, 고로슬래그 및 전기분해 알칼리 수용액을 사용한 시험체에 대한 추가적인 연구가 필요하다고 판단된다.