Abstract
Despite the size layer is an important part for conserving the artworks in the configuration of oil painting, the conservation scientific approaches of that have not been made yet. Therefore, this study produced standard samples on the basis of the analysis results of oil painting works, and carried out the evaluation of functions of the size layer materials. As a result of literature material, traditionally, animal glue was used for the size layer, whereas synthetic resin have been used in combination with animal glue since the modern age, in particular, it was identified that Polyvinyl Acetate(PVAc) was in general use. As a result of analysis of oil painting works, size layer was detected on the support and it was identified as animal glue. As a result of analysis based on Funaoka canvas for ground, it showed that the lead oxide and the titanium dioxide were the main constituents. On the basis of these results, standard samples were produced. As a result of evaluation on the functions of the size layer materials, in the case of the animal glue, stable result was observed in the shrinkag expansion rate, whereas slight weakness was observed in moisture proofing, color, and tensile strength, and dense cracks were found on surface. As for PVAc(A), moisture proofing, color, and the tensile strength exhibited stable results. Higher shrinkage rate was observed and the cracks with wide gaps were found on surface. As for PVAc(B), tensile strength, shrinkage expansion rate, and surface observation showed stable results, whereas moisture proofing property showed poor results. Different aspects were observed in each experiment, and this phenomena were considered to be due to the density and the adhesion properties between the hydrophilic and hydrophobic molecules in the size layer materials. The results are expected to be used as materials for the oil painting work conservation henceforth.
유화의 구성 조건 중 차단층은 작품보존에 중대한 영향을 미치는 부분이나, 차단층의 역할 및 재료에 대한 보존과학적 접근은 미미한 실정이다. 이에 본 연구에서는 문헌자료 및 유화작품의 구조별 분석 결과를 근거로 표준시료를 제작하였으며, 방습성 평가 및 가속열화실험을 통해 차단층 재료의 기능을 평가하였다. 문헌자료 조사 결과, 과거부터 차단층으로 이용되어온 재료는 아교이고, 현대로 넘어오면서 합성수지가 병용되고 있으며, 특히 Polyvinyl Acetate(PVAc)가 널리 사용되고 있는 것으로 나타났다. 유화작품 분석 결과, 지지체의 표면에서 차단층이 확인되었으며 차단층 재료는 아교로 동정되었다. 바탕칠층 안료는 Funaoka canvas를 기준으로 분석한 결과, 산화납과 산화타이타늄이 주요 구성성분인 것으로 나타났다. 이러한 결과를 근거로 표준시료를 제작하여 차단층 재료의 기능평가를 수행한 결과, 아교의 경우 낮은 수축률을 보였으나, 방습성, 색도, 그리고 인장강도에서 다소 취약한 것으로 나타났으며, 조밀한 균열이 확인되었다. PVAc(A)의 경우 방습성, 색도, 그리고 인장강도에서 안정적인 결과를 나타냈으나, 높은 수축률과 넓은 간격의 균열이 확인되었다. PVAc(B)의 경우 인장강도, 수축 팽창률, 그리고 표면관찰에서 안정적인 결과를 나타낸 반면, 방습성에서 취약한 결과를 보였다. 각각의 차단층 재료별로 상이한 결과가 나타난 것은 차단층 재료의 친수성과 소수성, 분자 간의 밀도와 접착 특성에 기인한 것으로 판단된다. 이러한 결과는 향후 유화작품 보존을 위한 자료로 활용될 것으로 기대된다.