Abstract
The present study evaluated the mechanical properties of open graded asphalt for semi-rigid pavements in order to determine the mixing proportion experimentally. A total twelve types of basic mixing proportions were set up and mechanical tests such as marshall stability, porosity, permeability, and cantabro loss were conducted based on Korean standards. From the tests results, it was found that the marshall stability in case of straight and modified asphalt increase up to the contents with 5.0% and 5.5% respectively. The porosity and permeability of asphalt tended to decrease as the asphalt contents increase, the coefficient of correlation between both were estimated 86%. The increase contents with asphalt range from 3.5% to 6.0% tended to decrease the cantabro loss and the modified asphalt enhanced the resistance of cantabro loss with range from 18.8% to 33.1% than straight asphalt under same asphalt contents. In comparison with test results and quality standards, it was concluded that the modified asphalt content of 4.5% is effective to adopt for open graded asphalt.
본 연구에서는 반강성포장용 개립도 아스팔트 혼합물의 배합조건을 결정하기 위한 실험적 연구를 수행하였다. 두 종류의 아스팔트 및 함량에 따른 총 12가지의 기본배합을 설정하였고, 국내 KS 기준에 따라 마샬안정도, 공극률 및 투수계수, 칸타브로 시험을 수행하였다. 시험결과로부터 다음과 같은 결론을 얻었다. 마샬안정도는 스트레이트 아스팔트와 개질 아스팔트의 함량이 각각 5.0% 및 5.5%까지는 증가하였으나 함량이 더 높아질 경우에는 증가량이 미미하거나 감소되는 경향을 나타내었다. 공극량의 경우 아스팔트 함량 증가에 따라 감소되고 투수계수도 감소되는 경향을 나타내었는데 상관계수가 86% 수준으로 평가되었다. 칸타브로 손실률 평가 결과 아스팔트 함량이 3.5%에서 6.0%로 증가될수록 감소되었고 개질 아스팔트는 스트레이트 아스팔트에 비해 손실률을 18.8%~33.1% 감소시킬 수 있었다. 국내 규정에서 제시하는 품질기준과 시험 결과를 종합해 볼 때 개질 아스팔트 함량 4.5%가 모체 개립도 아스팔트 제조에 유효한 배합으로 평가되었다.