Pretilt Angle Properties of Mixture Nematic Liquid crystal for Mobile Information Device

휴대용 통신단말에 사용되는 혼합액정계에서의 프리틸트각 특성에 관한 연구

  • Received : 2015.02.11
  • Accepted : 2015.02.27
  • Published : 2015.03.31
Download PDF
⟨ Previous Next ⟩

Abstract

We studied the state of the dual liquid crystal (LC) alignment which displays both homeotropic and homogeneous alignment on blended polyimide (PI) layer. The research was conducted using rubbing method at different imidizing temperatures and the blended PI was made using homeotropic PI having an alkyl side chain and homogeneous PI without the side chain. The uniform LC alignments were achieved, and have thermal stability. The results of contact angles were similar to that of pretilt angles.

본 연구에서는 폴리이미드 박막위에서의 수직 및 수평배향에서 혼합액정의 배향 특성에 대해서 연구하였다. 혼합액정은 러빙을 이용하여 배향처리하였으며, 러빙에 사용된 폴리이미드 박막은 알킬기를 Side Chain으로 가진 수직배향용 배향막과 그렇지 배향막으로 나누어서 프리틸트각 특성을 측정하였다. 실험결과 혼합액정을 사용하여 양호한 배향상태를 얻을 수 있었으며, 고온에서의 열안 정성에서도 우수한 특성을 보이는 것을 알 수 있었다. 또한 프리틸트각의 발생 원리를 이해하기 위해서 접촉각 측정을 실시하였으며, 이 둘이 밀접한 상관관계를 갖고 있음을 알 수 있었다.

Keywords

References

  1. Berreman, D. W., Phys. Rev. Lett., 28, 1683, (1972). https://doi.org/10.1103/PhysRevLett.28.1683
  2. Toney, M. F., Russell, T. P., Logan, J. A., Kikuchi, H., Sands, J. M., Kumar, S. K., Nature, 374, 709, (1995). https://doi.org/10.1038/374709a0
  3. D. S. Seo, S. Kobayashi, and M. Nishikawa, Appl. Phys. Lett., 61, 2392, (1992). https://doi.org/10.1063/1.108174
  4. D. S. Seo, and S. Kobayashi, J. Appl. Phys., 86, 4046, (1999). https://doi.org/10.1063/1.371327
  5. T. Uchida, M. Ohgawara, and M. Wada, Jpn. J. Appl. Phys., Part 1 19, 2127, (1980). https://doi.org/10.1143/JJAP.19.2127
  6. D. S. Seo, J. Appl. Phys., 86, 3594, (1999). https://doi.org/10.1063/1.371264
  7. F. S. Yeung, J. Y. Ho, Y. W. Li, F. C. Xie, O. K. Tsui, P. Sheng, and H. S. Kwok, Appl. Phys. Lett., 88, 051910, (2006). https://doi.org/10.1063/1.2171491
  8. J. Y. L. Ho, V. G. Chigrinov, and H. S. Kwok, Appl. Phys. Lett., 90, 243506, (2007). https://doi.org/10.1063/1.2748345
  9. J. B. Kim, K. C. Kim, H. J. Ahn, B. H. Hwang, J. T. Kim, S. J. Jo, C. S. Kim, and H. K. Baik, Appl. Phys. Lett., 91, 023507, (2007). https://doi.org/10.1063/1.2757121
  10. J. B. Kim, K. C. Kim, H. J. Ahn, B. H. Hwang, D. C. Hyun, and H. K. Baik, Appl. Phys. Lett., 90, 043515, (2007). https://doi.org/10.1063/1.2432272
  11. K. E. Vaughn, M. Sousa, D. Kang, and C. Rosen-blatt, Appl. Phys. Lett., 90, 194102, (2007). https://doi.org/10.1063/1.2737427
  12. H. G. Park, B. Y. Oh, Y. H. Kim, B. Y. Kim, J. M. Han, J. Y. Hwang, and D. S. Seo, Electrochem. Solid State Lett., 12, J37, (2009). https://doi.org/10.1149/1.3074331