Abstract
The aim of this research is providing the fundamental data for treating and recycling the byproducts by using the wet processed bottom ash as a fine aggregate replacement for cement-based extruded panel. Although the cement-based extruded panel was used mainly as a cladding component with its high strength and outstanding durability, it was hardly spread because of low economic feasibility due to the high cost of additives or fibers which were used to achieve 14 MPa of flexural strength as a cladding material. As a solution of this drawback, by the previous research, it was possible to replace cement by fly ash up to 80 % by decreasing quality criteria with restricting the application to indoor purpose. In this research, based on the previous research, by using the bottom ash as a replacement of fly ash, improvement of shape retention performance is tried. As a result of the experiment on evaluating the optimum content and PSD of bottom ash, as the fineness modulus and content of bottom ash was increased, the extruding performance was decreased and penetration resistance was increased. Additionally, the optimum content and the maximum particle size was found as 20 %, and 0.3 mm, respectively.
본 연구의 목적은 석탄회 중 바텀애시를 이용하여 시멘트압출성형 패널에 잔골재대체재(보형성 유지)의 용도로 적용을 함으로써 산업 부산물을 처리함과 동시에 새로운 용도를 창출하기 위한 기초자료를 제시하는 것이다. 선행연구에서는 건식벽체로 사용되는 시멘트 압출성형 패널에 비정제 플라이애시를 시멘트계 재료로 대체하여, 최대 80%까지 대체가 가능하였다. 하지만, 압출성형체는 압출 직후 자중에 의해 약간의 침하가 발생을 하게 되는데, 이는 반응성이 느린 플라이애시를 대량 사용한 경우에 늦은 경화로 인한 것이다. 본 연구에서는 자중에 의한 침하에 저항하기 위한 용도로 바텀애시를 잔골재대체재로의 사용가능성과 최적사용량을 검토하였다. 그 결과 바텀애시의 대체율이 증가함에 따라 압출경화체의 압출성은 저하 되었지만 관입저항성은 증가하였다. 그러므로 기존의 자중에 의한 패널의 침하현상은 잔골재 대체재를 사용함으로써 보완이 가능하였다. 또한 바텀애시 대체율 20%, 최대 입자 크기 0.6mm, 오토클레이브 양생에서 적절한 강도특성을 발현하고 있다. 본 연구의 결과를 통해 차후 바텀애시의 활용방법이 확대되고, 바텀애시를 잔골재로 활용함으로서 부가가치 상승에 기여할 것으로 예상된다.