Abstract
Construction materials using soil which is the most common material around us have many advantages, but their long-term durability and sensation of walking as pavements have problems. Therefore, they are used after compaction or mixed with various hardening agents such as lime and cement for strength enhancement. However, studies on the behavior of pavement materials mixed with environment-friendly hardening agents or admixtures to improve walking property are still insufficient. In this study, therefore, in order to evaluate the appropriate mixing ratio and field application characteristics of pavement materials using mixed soils with environment-friendly hardening agents and natural materials such as wood chips, mechanical tests were performed to evaluate the rational mixing ratios and the ball test was performed as an elasticity test to evaluate the field applicability. The results suggest that the content of wood chips should be selected at 1.5% or lower according to the purpose of the structure, and the hardening agent at 10~15%. The evaluation results for GB/SB coefficient ratio which indicates the walking property show that the appropriate mixing ratio of the hardening agent in terms of the sensation of walking is 15% of lower, but different mixing ratios should be chosen according to the proportion of wood chips.
우리 주변에서 가장 흔한 재료인 흙을 이용한 건설재료는 많은 장점에도 불구하고 장기적인 내구성과 보도로서의 보행감 등이 포장재로써 문제시되어 다짐 후 사용하거나 강도보강용으로 석회나 시멘트 등 다양한 고화재를 혼합하여 포장용으로 사용하고 있다. 그러나 친환경 고화재나 기타 보행성을 증가시키기 위한 혼합재가 포함된 포장재의 거동에 대한 연구는 아직 미진한 상황이다. 따라서 본 연구에서는 친환경 고화재와 목재칩과 같은 자연재료를 이용한 혼합토를 이용한 포장재의 적정 배합비와 현장적용 특성을 평가하기 위해 역학시험을 통해 합리적인 배합비를 평가하고 현장 적용성을 평가하기 위해 탄성도시험인 볼 테스트를 수행하였다. 시험결과 목재칩의 함량은 1.5% 이하에서 구조물의 목적에 따라 선택하고 고화재는 10~15% 함량의 범위 내에서 결정하며, 보행성을 표현하는 GB 계수/SB 계수 비의 평가결과, 보행감을 고려한 고화재의 비율은 15% 이하의 값이 적합하나 목재칩의 비율에 따라 상이한 배합비의 선정이 필요할 것으로 판단된다.