Abstract
Entering the 20th century since the industrial revolution, the cement has been widely used in the field of construction and civil engineering due to the remarkable development of construction industry. However, result from that development, each kind of industrial by-products and waste and the carbon dioxide generated in the process of cement production cause air pollution and environmental damage so earth is getting sick now slowly. Therefore, we have to recognize importance about this. It means that the time taking specific and long-term measures have come. In this research paper, as substitution of the cement generating environmental pollution, we investigate the hydration reaction of non-Sintered Cement mortar mixed with GBFS, active stimulant of alkaline and sulphate series by using SEM and XRD, mechanical and chemical properties according to the curing method. As a result of this experiment, NSC realized outstanding strength for water curing and steam curing. It means that it has a good possibility as substitution of cement. From now on, it can be used for structure satisfying specific standard. We expect to find a substitution of outstanding cement by progressing continuous research making the best use of pros and cons according to the curing method.
시멘트는 건설 산업의 발전과 비례하여 눈부신 발전을 이루었다. 그러나 이산화탄소의 발생량 또한 매우 치명적이다. 이러한 문제를 해결하기 위해 이산화탄소의 배출이 적은 시멘트의 개발이 시급한 상황이다. 따라서 본 연구에서는 시멘트의 대체제로 소성과정이 없어 에너지 손실률이 낮으며 이산화탄소의 배출량이 적은 비소성 시멘트(Non-Sintered Cement, 이하 NSC) 모르타르를 개발하고자 하였다. 산업 부산물인 고로슬래그 미분말(Granulated ground Blast Furnace Slag, 이하 GBFS)에 이를 활성화시키기 위한 자극제를 배합하였다. 그리고 GBFS와 자극제의 배합비율이 어떠한 양생조건에서 우수한 지를 알아보기 위해 각각의 양생조건에 따른 휨 및 압축강도, 그에 따른 수화 반응 생성물과 메커니즘을 알아보기 위해 SEM, XRD 실험을 진행하였고, 또한 화학저항성, pH측정, 염화물 이온 침투 저항성 및 탄산화 촉진실험을 실시하여 내구성을 알아보았다. 실험 결과 보통 포틀랜드 시멘트와 비교하여 전체적으로 우수한 특성과 내구성을 보여주었고, 콘크리트 2차 제품으로 개발하여 경제성 향상, 친환경적인 제품 생산, 환경문제 및 에너지 절약에 큰 이바지를 할 것으로 기대된다.