Preparation of Alkyl Acrylate and Functional Monomer Multi Core-Shell Composite Particles

알킬 아크릴레이트와 관능성 단량체계 다중 Core-Shell 복합입자의 제조

  • Choi, Sung-Il (Department of Chemical Engineering, Dong-A University) ;
  • Cho, Dae-Hoon (Department of Chemical Engineering, Dong-A University) ;
  • Seul, Soo-Duk (Department of Chemical Engineering, Dong-A University)
  • 최성일 (동아대학교 공과대학 화학공학과) ;
  • 조대훈 (동아대학교 공과대학 화학공학과) ;
  • 설수덕 (동아대학교 공과대학 화학공학과)
  • Received : 2013.01.14
  • Accepted : 2013.03.11
  • Published : 2013.03.30
Download PDF
⟨ Previous Next ⟩

Abstract

Multi core-shell composite particles were prepared by the water-born emulsion polymerization of various core monomers such as methyl methacrylate (MMA), ethyl methacrylate (EMA) and shell monomers such as MMA, EMA, 2-hydroxyl ethyl methacrylate (2-HEMA), glycidyl methacrylate (GMA) and methacrylic acid (MAA) in the presence of different concentrations of sodium dodecyl benzene sulfonate (SDBS). The following conclusions are drawn from the conversion, particle size and distribution, average molecular weight, molecular structure, glass transition temperature with DSC, contact angle after plasma treatment, tensile strength and isothermal decomposition kinetics. In the case of the concentration of 0.02 wt% SDBS, the conversion of MMA core-(EMA/GMA) shell composite particles was excellent as 98.5%. In the case of the concentration of 0.03 wt% SDBS, the particle size of EMA core-(MMA/GMA) shell composite particles was high as $0.48{\mu}m$. We confirmed that 3 points of glass transition temperatures appear for multi core-shell composite particles compared to 1~2 points of glass transition temperatures appear for general copolymer particles. Overall, the adhesion strength of shell composite particles was in the order of EMA/MAA > EMA/2-HEMA > EMA/GMA.

Core 입자로 methyl methacrylate (MMA), ethyl methacrylate (EMA)를 사용하고 shell 입자로 MMA, EMA, 2-hydroxyl ethyl methacrylate (2-HEMA), glycidyl methacrylate (GMA) 및 methacrylic acid (MAA)를 각각 사용하여 개시제 ammonium persulfate (APS), 유화제로 sodium dodecyl benzene sulfonate (SDBS)의 농도(0.01~0.03 wt%), 단량체의 종류와 조성을 변화시켜 수용성 유화중합으로 다중 core-shell복합입자를 제조하여 전환율, 입자경 및 입도분포, 평균분자량, 분자구조, 유리전이온도, 플라즈마 처리후의 접촉각, 등온열분해속도 및 인장강도를 각각 측정하여 다음과 같은 결론을 얻었다. SDBS 농도 0.02 wt%에서 MMA core-(EMA/GMA) shell 복합입자의 전환율이 98.5%로 우수하였고, 입자직경은 SDBS 농도 0.03 wt%에서 EMA core-(MMA/GMA) shell의 복합입자가 $0.48{\mu}m$로 높게 나왔다. 유리전이온도 측정으로부터 공중합체는 1~2개의 전이곡선 그리고 다중 core-shell 복합입자는 3개의 전이곡선을 얻었다. 전체적으로 접착박리강도의 크기는 shell 단량체가 MMA core인 경우 EMA/MAA > EMA/2-HEMA > EMA/GMA의 순으로 되었다.

Keywords

References

  1. S. D. Seul, J. Adhesion and Interface, 11, 3 (2010).
  2. D. H. Cho, S. I. Choi, H. M. Go, and S. D. Seul, J. Adhesion and Interface, 12, 1 (2011).
  3. Y. S. Jung, S. K. Min, and S. D. Seul, J. Adhesion and Interface, 10, 4 (2009).
  4. D. H. Cho, S. I. Choi, and S. D. Seul, J. Adhesion and Interface, 13, 2 (2012).
  5. C. E. Rehberg and C. H. Fisher, J. Am. Chem. Soc., 66, 1203 (1944). https://doi.org/10.1021/ja01235a040
  6. A. C. Nuessle, Chem. Ind. (London), 1580 (1966).
  7. D. W. Aubrey and S. J. Ginosatics, J. Adhes., 12, 189 (1981). https://doi.org/10.1080/00218468108071200
  8. H. P. Brown, Rubber Chem. Technol., 36, 931 (1963). https://doi.org/10.5254/1.3539642
  9. K. Cho, Polymer, 39, 14 (1988).
  10. T. O. Ahn, T. W. Hwang, and J. Y. Jho, Polymer, 21, 290 (1997).
  11. A. J. Backhouse, U. S. Patent, 4, 403, 003 (1983).
  12. T. R. Paxton, J. Polym. Sci., 46, 1387 (1992).
  13. J. N. Goodier, J. Appl. Mech., 55, 39 (1993).
  14. D. H. Sim and S. D. Seul, Polymer, 32, 276 (2008).
  15. D. H. Sim, J. E. Ban, M. S. Kim, and S. D. Seul, Polymer, 32, 470 (2008).
  16. K. C. Lee, Polymer, 21, 384 (1997).
  17. F. Vazquez, Polym. Int., 41, 1 (1996). https://doi.org/10.1002/(SICI)1097-0126(199609)41:1<1::AID-PI556>3.0.CO;2-2
  18. T. I. Min, A. Klein, M. S. El-Aasser, and J. W. Vanderhoff, J. Polym. Sci. Polym. Chem. Ed., 21, 2845 (1983). https://doi.org/10.1002/pol.1983.170211001
  19. I. Cho and K. W. Lee, J. Appl. Polym. Sci., 30, 1903 (1985). https://doi.org/10.1002/app.1985.070300510
  20. M. Okubo, S. Yamaguchi, and T. Matsumoto, J. Appl. Polym. Sci., 31, 1075 (1986). https://doi.org/10.1002/app.1986.070310409
  21. Y. Nakamura, H. Tabata, H. Suzuki, K. Iko, M. Okubo, and T. Matsumoto, J. Appl. Polym. Sci., 32, 4865 (1986). https://doi.org/10.1002/app.1986.070320509
  22. S. D. Seul, Korean Chem. Eng. Res., 49, 557 (2010).
  23. M. S. Kim and S. D. Seul, Polymer (Korea), 33, 232 (2009).
  24. K. Ito, J. Polym. Sci. Polym. Part A-1, 10, 1481 (1972).