Effects of binder type and heat treatment temperature on physical properties of a carbon composite bipolar plate for PEMFCs

  • Kang, Dong-Su (School of Advanced Materials and Systems Engineering, Kumoh National Institute of Technology) ;
  • Roh, Jea-Seung (School of Advanced Materials and Systems Engineering, Kumoh National Institute of Technology)
  • Received : 2013.02.14
  • Accepted : 2013.04.01
  • Published : 2013.04.30
Download PDF
⟨ Previous Next ⟩

Abstract

This study investigated a developed process for producing a composite bipolar plate having excellent conductivity by using coal tar pitch and phenol resin as binders. We used a pressing method to prepare a compact of graphite powder mixed with binders. Resistivity of the impregnated compact was observed as heat treatment temperature was increased. It was observed that pore sizes of the GCTP samples increased as the heat treatment temperature increased. There was not a great difference between the flexural strengths of GCTP-IM and CPR-IM as the heat treatment temperature was increased. The resistivity of GPR700-IM, heat treated at $700^{\circ}C$ using phenolic resin as a binder, was $4829{\mu}{\Omega}{\cdot}cm$ which was best value in this study. In addition, it is expected that with the appropriate selection of carbon powder and further optimization of process we can produce a composite bipolar plate which has excellent properties.

Keywords

References

  1. Bar-On I, Kirchain R, Roth R. Technical cost analysis for PEM fuel cells. J Power Sources, 109, 71 (2002). http://dx.doi.org/10.1016/S0378-7753(02)00062-9.
  2. Costamagna P, Srinivasan S. Quantum jumps in the PEMFC science and technology from the 1960s to the year 2000: Part I. Fundamental scientific aspects. J Power Sources, 102, 242 (2001). http://dx.doi.org/10.1016/S0378-7753(01)00807-2.
  3. Kim JH. Commercializing technology development of bipolar plates for polymer electrolyte membrane fuel cell. Trans Korean Hydrog New Energy Soc, 22, 409 (2011).
  4. Hwang IU, Yu HN, Kim SS, Lee DG, Suh JD, Lee SH, Ahn BK, Kim SH, Lim TW. Bipolar plate made of carbon fiber epoxy composite for polymer electrolyte membrane fuel cells. J Power Sources, 184, 90 (2008). http://dx.doi.org/10.1016/j.jpowsour.2008.05.088.
  5. Cho EA, Jeon US, Hong SA, Oh IH, Kang SG. Performance of a 1 kW-class PEMFC stack using TiN-coated 316 stainless steel bipolar plates. J Power Sources, 142, 177 (2005). http://dx.doi. org/10.1016/j.jpowsour.2004.10.032.
  6. Hung Y, El-Khatib KM, Tawfik H. Testing and evaluation of aluminum coated bipolar plates of pem fuel cells operating at 70$^{\circ}C$. J Power Sources, 163, 509 (2006). http://dx.doi.org/10.1016/j.jpowsour.2006.09.013.
  7. Cho EA, Jeon US, Ha HY, Hong SA, Oh IH. Characteristics of composite bipolar plates for polymer electrolyte membrane fuel cells. J Power Sources, 125, 178 (2004). http://dx.doi.org/10.1016/j.jpowsour.2003.08.039.
  8. Yamashita Y, Ouchi K. A study on carbonization of phenol-formaldehyde resin labelled with deuterium and 13C. Carbon, 19, 89 (1981). http://dx.doi.org/10.1016/0008-6223(81)90112-3.
  9. Walker PL, Jr., Thrower PA. Chem Phys Carbon, 9, 173 (1973).
  10. Kwon YK, Lee JK, Ji D, Lee JY. Electrochemical characteristics of home-made bipolar plate and its relationship with fuel cell performance. J Korean Electrochem Soc, 12, 68 (2009). https://doi.org/10.5229/JKES.2009.12.1.068
  11. Maheshwari PH, Mathur RB, Dhami TL. Fabrication of high strength and a low weight composite bipolar plate for fuel cell applications. J Power Sources, 173, 394 (2007). http://dx.doi. org/10.1016/j.jpowsour.2007.04.049.