Compressive Shear and Bending Performance of Compressed Laminated Wood after Microwave Heating

  • Park, Cheul-Woo (Department of Architectural Engineering, Tongmyong University) ;
  • Lim, Nam-Gi (Department of Architectural Engineering, Tongmyong University)
  • 투고 : 2012.06.12
  • 심사 : 2012.08.31
  • 발행 : 2012.10.20

초록

To manufacture laminated wood with improved mechanical properties by providing uniform adhesiveness, the adhesive was applied and the plate adhesive was laminated on the wood surface. Then, after laminating the wood on the top part of the adhesivebond, it was heated and dried while the adhesive was stiffened using microwaves, and the test piece was manufactured by compressing it with the press machine for thirty minutes. The temperature and the water content were examined according to the heating time of the wood heated with the microwave, and testing was conducted on the shear strength and flexural strength of the wood. In addition, the microstructure of the adhesive bond between the wood was recorded to confirm the penetrabilityinto the wood structure for the adhesive. After the test was conducted, it was found that the test piece manufactured with wood that has its water content leveled with the microwave heating showed improved shear strength and bending strength compared to the standard test piece. With regard to adhesives, liquefied polyvinyl acetate resin and plate's PVB resin were found to have superior adhesive strength. Also, after filming the cellular microstructure, it was found that when the laminated wood is heated with microwaves, the infiltration of the adhesive into the inside of the wood becomes easy, which makes it effective for improving adhesiveness.

키워드

참고문헌

  1. Yoon HW. Vision and strategy of wood industry whit the times of low carbon and green growth. 1nd ed. Seoul (Korea): Media wood wood korea; c2009. 112 p.
  2. Lee KH. Glued-Laminated Timber. Glulam. Architectural institute of Korea. 2005 October;49(10):40-5.
  3. Lim NG. Flame Resistance and Durability of Compressed Structural Wood through Microwave Heat Drying Method. Journal of the Korea Institute of Building Construction. 2011 April;11(2):162-70. https://doi.org/10.5345/JKIC.2011.04.2.162
  4. Park CH, Her JW, Lim NG. The Liquid Flame Proofing Agent's Permeating Effect of Wood Using Microwave. Journal of the Korea Institute of Building Construction. 2011 June;11(3):256-64. https://doi.org/10.5345/JKIC.2011.06.3.256
  5. KS F 3021. Structural glued laminated timber. Korea Standard Information Center.
  6. Jim L. Bowyer, Rubin Shmulsky, John G. Haygreen. Forest Products and Wood Science An Introduction(Fourth Edition). 1rd rev. ed. Seoul (Korea): Cheonkwang munhwasa; c2004. 570 p.
  7. Jim L. Bowyer, Rubin Shmulsky, John G. Haygreen. Forest Products and Wood Science An Introduction(Fourth Edition). 1st rev. ed. Seoul (Korea): Cheonkwang munhwasa; c2004. Chapter 16, composition wood; p. 448-9.
  8. Murasaki. Industrial Microwave Application Technology. 4rd rev. ed. Seoul (Korea): Gigeon; c1999. Chapter 5.2.5, Drying wood; p. 123-4.
  9. KS F 2209. Method of shear test for wood.
  10. KS F 2208. Method of bending test for wood. Korea Standard Information Center.
  11. Jeong HS. Latest Wood Drying Methods. 1rd rev. ed. Seoul:Seoul university press;c2005. Chapter 10, Special drying wood; p. 412-3.
  12. Park JC, Shin YJ, Hong SI. Bonding Performance of Glulam Reinforced with Glass Fiber-Reinforced Plastics. Mokchae Konghak. 2009 June;37(4):357-63.
  13. Kim DY, Kang SH, Jeong HY. A study on Pyrolytic and Anatomical Characteristics of Korean Softwood and Hardwood. Mokchae Konghak. 2007 August;35(6):31-42.