Improvement of Strength Characteristics in ALC added Silica Powder and Gypsum

규석 분말 및 석고 혼입에 따른 경량기포콘크리트의 강도특성 개선

Autoclaved lightweight concrete, also known as autoclaved aerated concrete(AAC) or autoclaved cellular concrete (ACC), is made with fine silica powder, quik lime, cement, and an Al powder. ALC contains 70~80% air. The lightweight material offers excellent sound and thermal insulation, and like all cement-based materials, is strong and fire resistant. However, ALC have high water absorption, low compressive strength and popout the origin of the low surface strength in its properties. These properties make troubles under construction such as cracking and popout. Thus, this study is to improve the fundamental strength by controls of increasing of admixtures, gypsum and silica powder size. Admixtures make use of metakaolin and silica fume. From the test result, the ALC using admixture have a good fundamental properties compared with plain ALC. Compressive strength, specific strength and abrasion's ratio were improved depending on increasing admixtures ratio's, gypsum and silica powder size.

ALC는 경량이며 단열 및 차열 등의 성능이 우수한 반면 낮은 강도로 인한 모서리부의 취성파괴가 발생하기 쉬우므로 운반 및 취급 시 상당한 주의를 요구한다. 본 연구에서는 ALC의 물리적 성능개선을 위해 메타카올린 및 실리카퓸 등의 혼화재나 규석 분말 및 석고의 혼입율을 조절하여 제조한 ALC의 성능을 평가하였다. 연구결과 메타카올린이나 규석 분말의 혼입율이 18%인 경우 강도의 개선이 현저하였다. 이와 같은 결과는 공극의 충전효과에 의한 것으로 강도는 개선되나 밀도가 증가하므로 밀도를 낮추면서 강도를 개선할 수 있는 배합이나 제조법에 대한 연구가 필요하다.