초록
The characteristics of Ga-doped zinc oxide (GZO) thin films deposited at different deposition temperatures (TS~250 to $550^{\circ}C$) on 4H-SiC have been investigated. Structural and electrical properties of GZO thin film on n-type 4H-SiC(0001) were investigated by using x-ray diffraction(XRD), atomic force microscopy(AFM), Hall effect measurement, barrier height from I-V curve and Auger electron spectroscopy(AES). XRD $2\theta$ scan shows GZO thin film has preferential orientation with c-axis perpendicular to SiC substrate surface. The lowest resistivity ($\sim1.9{\times}10^{-4}{\Omega}cm$) was observed for the GZO thin film deposited at $400^{\circ}C$. As deposition temperature increases, barrier height between GZO and SiC was increased. Whereas, resistivity of GZO thin films as well as barrier height between GZO and SiC were increased after annealing process in air atmosphere. It has been found that the c-axis oriented crystalline quality as well as the relative amount of activated Ga3+ ions and oxygen vacancy may affect the electrical properties of GZO films on SiC.