Effect of PWHT on Variability of fatigue Crack Propagation Resitance in TIG Welded Al 6013-T4 Aluminum Alloy

TIG 용접된 Al6013-T4 알루미늄 합금에서 피로균열전파저항의 변동성에서의 PWHT의 영향

  • Received : 2011.07.01
  • Accepted : 2011.08.13
  • Published : 2011.12.31

Abstract

The experimental investigation focuses on an influence of artificial aging time in longitudinal butt welded Al 6013-T4 aluminum alloy on the fatigue crack growth resistance. The preferred welding processes for this alloy are frequently tungsten inert gas welding (TIG) process due to its comparatively easier applicability and better weldability than other gas metal arc welding. Fatigue crack growth tests were carried out on compact tension specimens (CT) in longitudinal butt TIG welded after T82 heat treatment was varied in three artificial aging times of 6 hours, 18 hours and 24 hours. Of the three artificial aging times, 24 hours of artificial aging time are offering better resistance against the growing fatigue cracks. The superior fatigue crack growth resistance preferred spatial variation of materials within each specimen in the Paris equation based on reliability theory and fatigue crack growth rate by crack length are found to be the reasons for superior fatigue resistance of 24 hours of artificial aging time was compared to other joints. The highest of crack propagation resistance occurs in artificial aging times of 24 hours due to the increase in grain size (fine grained microstructures).

Keywords

References

  1. Y. Birol, 2004, "Improvement in Bake Hardening Response of a Twin-roll Cast Al-Mg-Si Sheet", International Conference on Aluminum 2004, Subodh K. Das, Ed., The Minerals, Metals & Materials Society, TMS.
  2. Yakubovski V.V. and Valteris J. J., 1989, "Geometrical Parameters of Butt and Fillet Welded and Their Influence on The Welded Joint Fatigue Life", In: IIW Doc. No. XIII, pp. 1326-69.
  3. Maddox S. J., 2003, "Review of Fatigue Assessment Procedures for Welded Aluminum Structures", Int. J. Fatigue, pp 1359-78.
  4. Welding Handbook, 1976, "Fundamentals of Welding", American Welding Society, Miami, Vol. 1, 7thEd., pp. 9-11.
  5. Wang C. and Chang Y., 1996, "Effect of Post-Weld Treatment on the Fatigue Crack Growth Rate of Electron Beam-Welded AISI 4130 Steel", Trans. Of Metallurgical and Material, Vol. 27A, pp. 3162-3169.
  6. S. Malarvizhi, K. Raghukandan, N. Viswanathan, 2008, "Investigations on the Influence of Post Weld Heat Treatment on Fatigue Crack Growth Behaviour of Electron Beam Welded AA2219 alloy", Int. J. Fatigue, Vol.30, pp.1543-1555. https://doi.org/10.1016/j.ijfatigue.2007.12.002
  7. Pinho da Cruz JAM, Costa DM, Borrego LFP, Ferreira JAM, 2000, "Fatigue Life Prediction in ALMgSi1 Lap Joint Weldments", International Journal of Fatigue, Vol. 07, pp. 601-610.
  8. Standard test method for measurement of fatigue crack growth rates, "ASTM E 647-08", 2008, American Society for Testing Materials (ASTM), New York.
  9. F. Casciati, P. Colombi, L. Faravelli, 2006, "Inherent variability of an experimnetal crack growth curve", Structural Safety, Vol. 29, pp. 66-76.
  10. Y. L. Liu and S. B. Kang, 1997, "The Solidification Process of Al-Mg-Si alloys", J. Mater. Sci., Vol. 32, pp. 1443-1447. https://doi.org/10.1023/A:1018545732009
  11. V. Balasubramanian, V. Ravisankar, and G. Madhusudhan Reddy, 2008, "Influences of Pulsed Current Welding and Post Weld Aging Treatment on Fatigue Crack Growth Behaviour of AA7075 Aluminium Alloy Joints", International Journal of Fatigue, Vol. 30, pp. 405-416. https://doi.org/10.1016/j.ijfatigue.2007.04.012
  12. J. C. Huang, C. S. Shin, and S. L. I. Chan,2004, "Effect of Temper Specimen Orientation and Test Temperature on Tensile and Fatigue Properties of Wrought and PM AA6061-alloys", International Journal of Fatigue, Vol. 26, pp. 691-703. https://doi.org/10.1016/j.ijfatigue.2003.11.006
  13. V. Balasubramanian, V. Ravisankar, and G. Madhusudhan Reddy, 2008, "Effect of Postweld Aging Treatment on Fatigue Behavior of Pulsed Current Welded AA7075 Aluminum Alloy Joints", ASM International, Vol. 17, pp. 224-233.