Abstract
In order to use as weight-reduced sintered parts for automobiles, mechanical properties of sintered compacts of 2712 Al-alloys containing 0, 10, 20, and 33% ceramics, respectively, were investigated in this study. (1)Regardless of ceramic contents, all sintered compacts possessed 4~7% pores. (2)After aging the compacts sintered for 12 minutes, tensile strength of the 2712 Al-alloys containing 0, 10, 20, and 33% ceramics was 165, 260, 256, and 166 N/$mm^2$, respectively, whereas those aged after sintering for 30 minutes exhibited the tensile strength of 186, 229, 219, and 202 N/$mm^2$, respectively. In addition, the 2712 sintered compact containing 10% ceramics showed the maximum elongation of about 3.6%, (3)After aging the 10% ceramic-containing sintered compacts reached a maximum apparent hardness ($H_RF$) of 97. (4)The minimum wear volume ($174{\times}10^{-3}mm^3$) was shown in the 10% ceramic-containing 2712 sintered compact after aging. From these results, the 2712 sintered compact containing 10% ceramics thought to be the most suitable one for the fabrication of aluminum engine part.
자동차용 경량소결부품으로 사용하기 위하여 2712 Al 합금 및 2712에 세라믹스를 각각 10, 20, 33% 첨가한 소결체의 기계적 특성에 대하여 조사하였다. 그 결과, (1)모든 소결체에서 4~7%의 기공이 잔류하는 것을 발견하였다. (2)시효처리한 2712 소결체 및 10, 20, 33% 세라믹스 함유 소결체의 인장강도 값은, 12분 소결에서는 각각 165, 260, 256, 166 N/$mm^2$, 30분 소결에서는 각각 186, 229, 219, 202 N/$mm^2$로 나타나, 세라믹스를 10% 첨가하여 12분 소결한 경우가 가장 우수한 인장강도 값을 나타내었다. 또한, 소결체의 최대 연신율값 3.6%는 세라믹스를 10% 첨가하여 30분 소결 후 시효처리한 소결체에서 나타났다. (3)시효처리 후의 소결체 표면의 최대 겉보기 경도값 ($H_RF$) 97은 세라믹스를 10% 첨가하고 30분 소결한 경우에 나타났다. (4)가장 낮은 내마모량 값 $174{\times}10^{-3}mm^3$은 10% 세라믹스를 첨가하여 시효처리한 소결체에서 나타났다. 이러한 결과들로부터 세라믹스를 10% 첨가한 2712 소결체가 Al 엔진부품 제조에 가장 적합한 것으로 판단되었다.