Effects of Alkoxy Side Chain on the Properties of Wholly Aromatic Liquid Crystalline Polyesters with Biphenylene Units

알콕시 곁사슬기가 비페닐렌구조를 갖는 전방향족 액정폴리에스터의 물성에 미치는 영향

Wholly aromatic polyesters having flexible alkoxy side chain were synthesized by direct polycondensation. The synthetic polymers have been characterized by $^1H$-NMR, FT-IR. DSC, TGA, optical polarizing microscope and X-ray diffractometer. The inherent viscosities (${\eta}_{inh}$) measured in 1,1,2,2-tetrachloroethane (TCE) were 0.46~2.41 dL/g. The polymers having side chain showed double melting transition, ie, solid-sanidic liquid crystalline (LC) phase transition ($T_{m1}$) and sanidic LC phase-nematic LC phase transition ($T_{m2}$). As incresing length of alkoxy side chain, phase transition temperatures decreased and solubilities in organic solvents incresed. The peaks of $2{\theta}\;{\simeq}5$ and $2{\theta}\;{\simeq}20$ in X-ray diffractograms are due to crystallization of polymer main chain and of long side chain, respectively.

유연한 알콕시 곁사슬을 갖는 전방향족 폴리에스터가 direct polycondensation에 의하여 합성되었으며, 합성된 중합체들은 $^1H$-NMR, FT-IR, DSC, TGA, 편광현미경 및 X-ray 분석기에 의하여 조사되었다. 1,1,2,2-테트라클로로에탄(TCE)을 용매로 사용하여 측정된 중합체의 고유점성도(${\eta}_{inh}$)는 0.46~2.41 dL/g의 값을 나타내었다. 곁사슬을 갖는 중합체들은 두 개의 용융전이 즉, 고체상-sanidic 액정상으로의 전이 ($T_{m1}$)와 sanidic 액정상-nematic 액정상으로의 전이 ($T_{m2}$)를 나타내었으며, 알콕시 곁사슬의 길이가 증가함에 따라 상전이온도들은 감소하고, 유기용매에 의한 용해도는 증가하는 경향을 나타내었다. X-ray 분석에서, $2{\theta}\;{\simeq}5$와 $2{\theta}\;{\simeq}20$ 피이크는 각각 중합체 주사슬과 긴 곁사슬의 결정화에 의한 것으로 나타났다.