Abstract
The glass formation and the dissolution property in $P_2O_5-K_2O$-FeO-CuO system were studied. In the batch process, the content of P2O5 was fixed at 60mol% and the other elements were varied from 10~40mol%. The prepared glasses were soaked in the D.I. water up to 13hr and the dissolution properties were investigated with the solutions sampled every 2 hr. The result shows that the $P_2O_5$ was leached out firstly from Phosphate glass system and then Cu and Fe ions were observed according to atmosphere change in solution. ICP shows that the dissolution amount in Phosphate was depended on the glass structure and the highest dissolution amount of CuO and FeO ions was observed when the 10mol% $K_2O$ was added in batch process.
$P_2O_5-K_2O$-FeO-CuO계 유리의 형성및 이온용출에 대하여 연구하였다. $P_2O_5$를 60mol%로 고정하고 $K_2O$-FeO-CuO의 mol%를 10mol%에서 40mol%까지 변화를 주었다 제조된 유리시편을 증류수에서 13시간 동안 침적시키며 2시간 간격으로 용출 특성을 평가 하였다. 초기 유리구조 내 Phosphate의 $P_2O_5$가 1차 용출이 일어나며 2차로 염기성 산화물의 용출이 일어나면서 Cu, Fe 이온이 함께 용출되는 것으로 관찰되엇다. ICP 관찰시에는 유리의 형성 구조의 차이에 따라 용출량이 변화 하였고, 용출은 $10K_2O$(mol%)함량일 때 CuO와 FeO의 용출량이 가장 많이 일어나는 것으로 관찰되었다.