Abstract
This study is on development of UV-cured water soluble coating composition which have more improved anti-cigar burning to prevent a surface of PVC tile from damage of heat. To make an anti-cigar burning coating solution, thermostable agent that synthesize main materials phosphorus compound, guanidine and ammonium phosphate dibasic used temporary flame retardants, changing their contents from 10 to 30wt% against quantities of resin and compounded. After coating PVC tiles using bar-coating method that can adjust a thickness, we estimated surface properties of coated layer such as anti-cigar burning, adhesive power, chemical resistance, thickness of coating, and so on. Results showed that a coating composition added 30 wt% of phosphorus compound and coated with No.12 bar-coater had the best optimized surface property in anti-cigar burning effect, adhesive power and chemical resistance. Also, we could find anti-cigar burning effect was improved as thermostable agents content and coating thickness increased.
본 연구는 건축용 바닥재로 널리 이용되는 PVC 상재의 표면을 열에 의한 손상으로부터 보호하기 위하여 기존에 사용하는 광경화형 우레탄-아크릴 수지에 내열성(anti-cigar burning)을 향상시킨 광경화형 수성도료 개발에 관한 것이다. PVC 바닥상재용으로 사용되는 내열기능성이 없는 우레탄-아크릴 수지에 인계화합물을 주원료로 합성한 내열재, 구아니딘을 주원료로 합성한 내열재, 일시적 방염제로 사용되는 제 2인산암모늄을 수지의 양 대비 함량(wt%)을 10, 20, 30%로 변화하여 첨가한 후 배합하여 수지의 내열성을 향상시킨 코팅액을 제조하였다. 제조한 코팅액은 코팅층의 두께조절이 가능한 Bar-coating을 사용하여 PVC 바닥상재에 코팅한 후, 내열성, 부착력, 내화학성, 코팅두께 등의 코팅층 표면물성을 평가하였다. 연구결과, 수지에 인계화합물을 주원료로 합성한 내열재 30%를 혼합하여 제조한 코팅액을 Bar-coater No.12로 코팅한 코팅표면이 열에 의한 손상이 가장 적고, 부착력 100%, 내화학성 양호로 가장 좋은 물성을 보였다. 전반적으로 내열재 함량이 높고, 코팅 두께가 두꺼울수록 내열성이 우수한 것으로 나타났다.