The primary purpose of this study is to estimate the guaranteed strength and construction quality of the combined high flowing concrete which is used in the slurry wall of underground LNG storage tank. The required compressive strength of this type of concrete become generally known as a non economical value because it is applied the high addition factor for variation coefficients and low reduction factor under water concrete. Therefore, after estimation of the construction quality and guaranteed strength in actual site work, this study is to propose a suitable equation to calculate the required compressive strength in order to improve its difference. Application results in actual site work are shown as followings. The optimum nix design proportion is selected that has water-cement ratio 51%, sand-aggregate ratio 48.8%, and replacement ratio 42.6% of lime stone powder by cement weight. Test results of slump flow as construction quality give average 616~634mm. 500mm flowing time and air content are satisfied with specifications in the rage of 6.3 seconds and 4.0% respectively. Results of strength test by standard curing mold show that average compressive strength is 49.9MPa, standard deviation and variation coefficients are low as 1.66MPa and 3.36%. Also test results by cored cylinder show that average compressive strength is 66.4MPa, standard deviation and variation coefficients are low as 3.64MPa and 5.48%. The guaranteed strength ratio between standard curing mold and cored cylinder show 1.23 and 1.32 in the flanks. It is shown that applied addition factor for variation coefficients and reduction factor under water concrete to calculate the required compressive strength is proved very conservative. Therefore, based on these results, it is proposed new equation having variation coefficients 7%, addition factor 1.13 and reduction factor 0.98 under water connote.
본 연구에서는 지하식 LNG 저장탱크의 지하연속벽에 사용되는 병용계 고유동 콘크리트의 시공 품질 및 보증강도 평가를 정리한 것이다. 일반적으로 지하연속벽에 사용되는 고유동 콘크리트의 배합강도는 높은 할증계수와 낮은 수중 콘크리트의 저감계수를 적용하기 때문에, 매우 비경제적인 배합설계가 된다. 이를 구명하기 위한 방안으로 현장에서 실시한 병용계 고유동 콘크리트의 시공 품질과 보증강도를 평가하여 이에 적합한 배합강도 산정식을 제안하고자 하였다. 연구 결과, 최적배합조건은 물-시멘트비 51%, 잔골재율 48.8%, 그리고 석회석 미분말을 시멘트의 중량비로 42.6% 치환한 것으로 선정하였다. 또한, 현장 적용 결과를 분석해 보면, 슬럼프 플로우에 대한 시공 품질 시험 결과 평균 616~634mm이고 500mm 플로우 도달시간은 평균 6.3초, 공기량은 평균 4.0%로 관리기준을 만족하였다. 표준양생 공시체의 압축강도에 대한 시공 품질 시험 결과, 평균 49.9MPa를 나타내었고 표준편차는 1.66MPa, 변동계수는 3.36%로 매우 낮았다. 코어 공시체의 압축강도는 평균 66.4MPa를 나타내었고, 표준편차는 3.64Pa, 변동계수는 5.48%로 나타났다. 표준양생 공시체와 코어 공시체의 보증강도비는 1.23 및 1.32로 나타났다. 기존에 배합강도를 산정하기 위하여 적용한 할증계수 및 저감계수가 매우 안정적인 것으로 나타났다. 본 연구에서는 이러한 결과를 통해 지하연속벽에 사용되는 병용계 고유동 콘크리트의 배합강도 산정에 있어서 변동계수 7%, 할증계수 1.13 및 수중 콘크리트의 강도저감 계수를 0.98로 제안하였다.