Abstract
The crosslinked poly(vinyl alcohol) (PVA) mwmbranes with poly(styrene sulfonic acid-co-maleic acid) (PSSA-MA) were used to measure the water vapor and air permeabilities at 25 and $35^{\circ}C$. In addition, the contact angles of crosslinked PVA membranes were observed and increased with PSSA-MA contents. The water vapor permeability of 15300 Baller (1 Baller=$10^{-10}cm^3(STP){\cdot}cm/cm^2{\cdot}s{\cdot}cmHg$) was shown the maximum value at $35^{\circ}C$ when PSSA-MA=7 wt% membrane was used. The gas permeability of 146 Barrer was indicated the maximum at PSSA-MA=7 wt% at $35^{\circ}C$ and $P(H_2O)/P(Air)$ was the highest value 109.2 at $25^{\circ}C$.
Poly(vinyl alcohol) (PVA)와 가교제 Poly(styrene sulfonic acid-co-maleic acid) (PSSA-MA)을 적용하여 제조된 막을 이용하여 수증기 및 공기에 대한 막 투과 실험을 하였다. 또한 PVA/PSSA-MA막에 대한 PSSA-MA의 함량별로 접촉각을 측정하였으며 함량이 3 wt%에서 접촉각이 가장 낮았고 함량이 증가할수록 접촉각은 증가하였다. $35^{\circ}C$에서 PSSA-MA 함량 변화에 따른 수증기 투과도는 7 wt%에서 15300 Barrer (1 Barrer=$10^{-10}cm^3(STP){\cdot}cm/cm^2{\cdot}s{\cdot}cmHg$)로서 최대를 나타내었다. 그리고 $25^{\circ}C$에서 PVA/PSSA-MA막의 수증기 투과 성능은 $35^{\circ}C$와 유사한 경향을 보였다. 공기의 투과도는 PSSA-MA의 함량이 7 wt%에서 최대가 되었으며 $35^{\circ}C$C에서 146 Barrer를 나타내었고, $P(H_2O)/P(Air)$는 $25^{\circ}C$에서 109.2로 최대를 나타내었다.