Study on the Compositional Construction of Epoxy Based Powder Paint

환경친화형 에폭시계 분체도료의 조성구축 연구

  • Lim, Hong-Joon (Department of Polymer Engineering, The University of Suwon) ;
  • Chung, Kyung-Ho (Department of Polymer Engineering, The University of Suwon)
  • 임홍준 (수원대학교 공과대학 신소재공학과) ;
  • 정경호 (수원대학교 공과대학 신소재공학과)
  • Received : 2006.01.26
  • Accepted : 2006.02.28
  • Published : 2006.03.01
Download PDF
⟨ Previous Next ⟩

Abstract

Main compositions of powder paint based on thermoset type epoxy resin consist of epoxy resin for powder coating, curing agent, filler and pigment. The curing system used in this study was based on diglycidyl ether of bisphenol-A (DGEBA) and dicyan diamide (DICY). The curing behavior and rheological properties of powder coating material were investigated using DSC and rheometer, respectively. And the adhesion strength between steel and powder coating material was measured using lap shear geometry. The optimum formulation of epoxy powder paint obtained from this study was base resin of 100 phr, DICY of 6 phr, $CaCO_3$ of 20 phr, and $TiO_2$ of 10 phr.

본 실험은 에폭시계 분체도료의 물성에 영향을 미치는 에폭시 수지, 경화제, 충전제 및 안료 의 최적 조성 결정에 대한 연구이다. 본 연구에서 사용된 에폭시계 수지의 경화 시스템은 Diglycidyl ether of bisphenol-A (DGEBA)와 경화제로 dicyan diamide (DICY)를 사용하였다. 코팅 재료의 경화거동과 유변물성은 DSC와 레오메터를 사용하여 조사되었다. 또한 코팅재료의 스틸에 대한 접착력은 lap shear 실험을 이용하여 조사되었다. 연구 결과에 따르면 에폭시계 분체도료의 최적 조성은 에폭시계 수지 기준으로 DICY 6 phr, $CaCO_3$ 20 phr 및 $TiO_2$ 10 phr 이었다.