Abstract
The influence of liquid shotcrete accelerators(alkali aluminate, two types of alkali-free) was investigated. Comparing to the existing alkali aluminate accelerator, new alkali-free accelerator, AF2, shortened initial and final setting of cement system, and after curing for 1 day compressive strength was analogous with others. On the other hand, compressive strength of specimen cured for 12 hour was the highest by the addition of alkali aluminate accelerator, but final strength was the lowest by that. But compressive strengths of AF1, AF2 were similar to Plain up to 28day. Further from XRD(X-Ray Diffractometer) and DSC(Differential Scanning Calorimeter) analyses, we confirmed that setting promoted by alkali aluminate was mainly because of Ca(OH)2(calcium hydroxide), but the accelerating behavior of alkali-free was influenced by the needle-like ettringite$(6CaO{\cdot}Al_2O_3{\cdot}3SO_3{\cdot}32H_2O)$ crystal.
액상 숏크리트 급결제(알칼리 알루미네이트, 2종의 알카리프리)가 시멘트 계의 수화 특성에 미치는 영향을 조사했다. 새로운 알카리프리계 숏크리트용 급결제(AF2)를 적용할 경우 기존의 알칼리 알루미네이트 급결제에 비해 초결, 종결 시간은 단축되었고, 1일 압축 강도는 유사했다. 12시간 경과된 모르타르 시편의 압축 강도는 알칼리 급결제가 첨가된 시편이 가장 높았으나, 이후 최종 강도는 알칼리 급결제를 첨가한 시편이 가장 낮았다. 그러나 알카리프리가 첨가된 AF1, AE2 시편의 압축 강도는 28일까지 plain과 유사했다. XRD와 DSC 분석을 통해 알칼리계 급결제는 주로 수산화칼슘, 알카리프리계 급결제는 에트링자이트 결정 성장으로 응결이 촉진된 것을 확인했다.