Effect of Temperature on $H_2$ Spillover over $Pt/H_xMoO_3$

Pt를 담지한 $H_xMoO_3$촉매의 수소 이동 속도에 미치는 온도의 영향

Rates of $H_2$ uptake into $Pt/MoO_3$ were measured for the noncalcined and $200^{\circ}C$ calcined $Pt/MoO_3$. Amount of $H_2$ uptake for $200^\circ{C}$calcined $Pt/MoO_3$ was greater than the amount of noncalcined $Pt/MoO_3$. From these two experiments, it was found that the rates of $H_2$ desorption were proportional to the increase of desorption temperature. XPS demonstrated that Cl reduced more faster in ITR after calcination at $200^{\circ}C$. This inducd smaller amount of residual chlorine at adlineation sites between Pt and $MoO_3$ substrates. This resulted in opening the more channel of hydrogen pathway into more $MoO_3$particles and controled the kinetics of hydrogen uptake.

비소성 Pt/MoO₃와 200℃에서 소성한 Pt/MoO₃가 150℃에서 수소를 흡착하는 속도를 측정하였다. 소성된 Pt/MoO₃의 수소 흡착량이 비소성 Pt/MoO₃의 수소 흡착량보다 증가하는 것으로 관찰되었다. 상기 두가지 흡착 속도를 나타내는 Pt/MoO₃ 촉매에서 탈착량은 흡착량과 탈착 온도의 증가에 비례하는 것을 알 수 있었다. 또한 X-Ray Photoelectron Spectroscope(XPS) 결과로부터 Pt와 MoO₃간의 활성점에 존재하는 Cl의 존재가 수소 이동 속도를 결정하는 것으로 판단되었다.