Testing and Numerical Analysis on the Fracture Characteristics of Composite Adhesive Bonded Single-Lap Joints

복합재료 Single-Lap 본딩 조인트의 파괴 특성에 대한 실험 및 수치해석 연구

  • 김광수 (한국항공우주연구원 우주발사체기술실 구조그룹) ;
  • 박재성 (한국항공우주연구원 우주발사체기술실 구조그룹) ;
  • 장영순 (한국항공우주연구원 우주발사체기술실 구조그룹) ;
  • 이영무 (한국항공우주연구원 우주발사체기술실 구조그룹)
  • Published : 2003.10.01
Download PDF
⟨ Previous Next ⟩

Abstract

The experimental and numerical investigations on the failure characteristics of the secondary bonded composite single-lap joints were performed. The initiations and growths of cracks were observed using CCD camera and acoustic emission sensor during the tension tests of the joint specimens. The structural behaviors of the specimens were predicted by the geometric nonlinear two-dimensional finite element analysis. The three types of observed initial cracks were included in each finite element models and the strain energy release rates of each specimen models were calculated by VCCT(Virtual Crack Closure Technique) technique. The tension tests showed that the initial cracks occurred in the 60∼90% of final failure loads and the major failure modes of the specimens were adhesive failure and the delamination between the 1st and 2nd ply of laminate. The specimens with the thicker bondline had earlier crack initiation loads but higher crack propagation resistance and eventually better loading capability. The delaminations were mostly observed in the thicker bondline specimens. The mode I values of calculated strain energy release rates were higher than the mode II values in the all specimen models considering the three types of initial cracks. The mode I and total strain energy release rates were calculated as higher values in the order of initial crack in the edge interface, comer interface and delamination between the plies of laminate.

본 논문에서는 이차 본딩으로 접착된 복합재료-복합재료 Single-Lap 조인트 시편에 대해 인장 시험 및 수치해석을 통해 그 파손 특성을 조사하였다. 시편시험에서는 시험 중에 CCD 카메라 및 AE 센서를 이용해 초기 균열의 발생 및 진전양상에 대한 시험적인 관찰을 수행하였다. 시편에 대해 기하비선형 유한요소해석 및 VCCT(Virtual Crack Closure Technique)기법을 이용해 시편의 거동 및 변형율에너지방출률을 계산하고 세 가지 관찰된 초기 균열 모드에 대해 파손강도를 계산하였다. 인장시험에서 초기 균열은 모서리 계면 균열, 측면 계면 균열 및 층간 분리 균열의 세 가지 형태로 최종 파손의 60∼90% 하중에서 발생하였다. 주된 파손 모드는 접착제 계면 파손(adhesive failure) 및 적층판의 첫 번째 및 두 번째의 층간 분리 파손이었다. 두꺼운 접착제 층을 갖는 시편들은 초기균열이 낮은 하중에서 발생하였지만 균열진전에 대한 저항성 및 파손하중은 높게 나타났다. 층간분리파손은 주로 두꺼운 접착제의 경우에 발생하였다. 세 가지 초기 균열 모드에 대해 변형률에너지방출률은 Mode I의 G값이 Mode II의 G값보다 크게 계산되었다. Mode I 및 전체 G값은 측면 계면 균열, 모서리 계면 균열, 층간분리 균열의 순서로 크게 계산되었다.

Keywords

References

  1. Composite Structures v.47 Stress Analysis of Adhesive-Bonded Lap Joints Her,S.C. https://doi.org/10.1016/S0263-8223(00)00052-0
  2. AIAA-97-1341 Stress Analysis Codes for Bonded Joints in Composite Structures Rastogi,N.;Deepak,B.P.;Soni,S.R.
  3. International Journal of Adhesion & Adhesive Stress Analysis of Double-Strap Bonded Joints Using a Variational Method Chalkley,P.;Rose,F.
  4. Computers & Structures v.55 no.4 Interfacial Stresses and Deformations of An Adhesive Bonded Bouble Strap Butt Joint under Tension Mitra,A.K.;Ghosh,B. https://doi.org/10.1016/0045-7949(94)00430-B
  5. J. Adhesion v.59 Comparison Between Experimental and Theoretical Analsysis of Stress Distribution in Adhesively-Bonded Joints : Tension and Mortise Joints and Single-Lap Joints Fargette,B.;Gilibert,Y.;Rimlinger,L. https://doi.org/10.1080/00218469608011085
  6. AIAA-97-120 Three-Dimensional Finite Element Analysis of adhesively Bonded Plates Bogdanovich,A.;Kizhakkethara,I.
  7. AIAA Journal v.18 no.11 Stress in Double-Lap Joints Bonded with a Viscoelastic Adhesive : Part Ⅱ. Parametric Study and Joint Design Sen,J.K.;Jones,R.M. https://doi.org/10.2514/3.7729
  8. Proceedings of American Society for Composites no.15 Stress and Failure Analysis of Adhesive-Bonded Composite Joints Using ASTM D3165 Specimen Huang,H.;Yang,C.C.;Romblin,J.S.;Harter,P.
  9. AIAA-98-1888 3-D Progressive Failure Analysis of Bonded Composite Joints Bogdanovich,A.E.;Yushanov,S.P.
  10. Composite Structures v.54 Stress concentrations caused by bond cracks in single-lap adhesive composite joints Kayupov,M.;Dzenis,Y.A. https://doi.org/10.1016/S0263-8223(01)00090-3
  11. Theoretical and applied fracture mechanics v.31 Progressive fracture of adhesively bonded composite structures Minnetyan,L.;Chamis,C.C. https://doi.org/10.1016/S0167-8442(98)00069-X
  12. 춘계학술발표대회 논문집 복합재료와 강재료를 이용한 동시 경화 조인트의 계면 모서리에서의 응력집중계수 신금철;이정주
  13. Eng. Fracture Mech v.28 Calculation of Strain-Energy Release Rates With Higher Order And Singular Finite Element Raju,I.S. https://doi.org/10.1016/0013-7944(87)90220-7
  14. Journal of Composites v.25 no.1 An Efficient Analysis for the Debonding of Stitched Skin-Stiffened Structures Glaessgen,E.H.;Raju,I.S.;Poe,C.C.
  15. Composite Structures v.57 Comparison of 2D finite element modeling assumptions with results from 3D analysis for composite skin-stiffener debonding Krueger,R.;Paris,I,L.;O'Brien,T.K.;Minguet,P.J. https://doi.org/10.1016/S0263-8223(02)00079-X
  16. Composites v.32 A shell/3D modeling techinique for the analysis of delaminated composite laminates Krueger,R.;O'Brien,T.K. https://doi.org/10.1016/S1359-835X(00)00133-0
  17. Engineering Fracture Mechanics v.9 A finite element calculation of stress intensity factors by a modified crack closure integral Rybicki,E.F.;Kanninen,M.F. https://doi.org/10.1016/0013-7944(77)90013-3
  18. Fracture, Handbuch der Physik v.6 Irwin,G.R.
  19. Hysol EA9309NA-Epoxy Paste Adhesive, Manufacturer Spec.