Properties of Physical and Surface Glossing of Exposed Concrete with the Contents of Granulated Blast Furnace Slag

고로슬래그 미분말의 치환율 변화에 따른 노출 콘크리트의 물리 및 표면광택 특성

  • Published : 2002.02.01

Abstract

This paper is Intended to investigate physical properties and surface glossing of exposed concrete incorporating granulated blast furnace slag(BS). According to test results there is no remarkable variations in fluidity and air content with increase of BS, but unit weight shows decline tendency Compressive strength at later age gains considerably due to potential hydraulicity reaction of BS. It shows that drying shrinkage increases. It is found that low W/B, surface coating and high BS content lead to favorable effects on the surface glossing of exposed concrete because of filling effects on the voids of the concrete. It is improved by about 7 % with increase every 10 % of BS content. The effects of form pannel kinds on the improvement of surface glossing are in order for acryl, fancy, steel and wood.

본 연구는 고로슬래그 미분말의 치환율 변화에 따른 노출 콘크리트의 물리적 성질 및 표면 광택도 특성에 대하여 검토하였다. 실험결과, 고로슬래그 치환율 증가에 따른 공기량 및 유동성은 유사하게 나타났고, 단위용적중량은 저하하였다. 후기재령에서의 압축강도는 고로슬래그의 잠재수경성 반응에 기인하여 증가하였다. 건조수축은 커지는 것으로 나타났다. 노출 콘크리트의 표면 광택도는 W/B가 낮을수록 또한, 표면 도포인 경우 증가하였다. 고로슬래그 미분말의 치환율 증가에 따른 광택도는 고로 슬래그의 공극충전효과 및 백색도에 의하여 증가하였는데, 이때 고로슬래그 미분말의 치환율 10% 증가시 약 7% 정도 증가하였다. 거푸집 종류에 따라서는 아크릴, 치장합판, 철판, 일반합판 순으로 광택도가 우수한 것으로 나타났다.

Keywords

References

  1. 장기인, "건축시공학," 보성각, 1996
  2. 宮本欣明; "打放しコンクリ トに關する賣驗的硏究(その1 せき板および諦固め方法が仕土がり,强度に皮ぼす影響について),"日本建築學會人會學術講演梗漑集, pp.185-186, 1993
  3. 柏木降男; "打放しコンクリ-トの色むらに關する基礎的硏究," 日本建築學會大會學術講演梗槪集, pp.1395-1396,1996
  4. 人橋正治, 田村博, 三井英和, 井ノ川尙; '打放しコンクリ-トの色調制御(その1 配合要因の影響),' 日本建築學會大會學術講演梗槪集, pp.1135-1136, 1998
  5. 柏本降男, 河津龍大, 寺嵨明彦, 太田昇; "打故しコンクリ-トの色調制御(その2 脫型時期·養生溫度.打繼ぎ時間間隔の影響)," 日本建築學帝大會學術講演梗槪集, pp.1137-1138, 1998
  6. ASTM D 523 ; Standard Test Method for Specular Gloss, 1980