Recycling of Safety Check Valves Contaminated with Radioactivity by Chemical Decontamination

化學除染에 의한 逆止밸브의 再使用

Chemical decontamination techniques have been employed to reuse the high cost check valves contaminated with radioactivity and to reduce the radiation exposure during the inspection and maintenance work of safety injection system containing check valves. After chemical decontamination, an ultrasonic treatment was conducted to remove the fine solid particles retained in the crevices of check valves. The decontamination process conditions and the amount of chemical reagents were determined from the results of a pre-test, using the (list arm holder. The decontamination factors (DF), estimated from the activity in the solution, ranged from 14.5 to 18.5 corresponding to the activity removal of 93-95ft. The corrosion test data indicated that the general corrosion rate during a chemical decontamination-ultrasonic treatment process are low for type 304 S tainless steel, Inconel -600 and Stellite-6 materials $ (2.1\times10^{-2}$ $6.0\times10^{-2}$ and$ 1.7\times10^{-2}$ mil, respectively).

원전 안전주입계통 역지밸브의 유지보수 작업과 관련하여 작업자 방사성 피폭저감과 고가 부품의 재사용을 위해 방사능으로 오염된 이들 밸브를 화학제염법으로 제염을 수행하였다. 화학제염 후 역지밸브 내부 틈새에 잔류한 미세 고형입자를 제거하기 위해 초음파세척을 병행하였다. 역지밸브 disk arm holder를 사용한 사전 시험결과를 토대로 제염공정과 제염시약량을 결정하였으며 제염에 의한 부식산화물 용해거동, 방사능 제거거동과 재료부식거동을 조사하였다. 화학제염에 이은 초음파 적용결과, 초기 방사능의 93-95%가 제거되었으며 역지밸브 구성재질인 Type 304 stainless steel, Inconel-600 및 Stellite-6 에 대한 일반부식량은 각각 $ 2.1$\times10^{-2}$ , $6.0\times10^{-2}$ 및 1.7 mil 로써 일반부식 허용한계치의 3.3%, 24.0 % 및 2.7% 수준을 나타내어 제염효과와 재질건전성 면에서 효과적이었다.