Journal of Korean Society of Environmental Engineers (대한환경공학회지)

Korean Society of Environmental Engineers (대한환경공학회)
권호 표지

Physical Properties and Sulfidation Kinetics of Mn-Based Sorbent for Hydrogen Sulfide Removal

황화수소 제거를 위한 망간계 탈황제의 물리적 특성과 황화반응 속도

  • Oh, Kwang-Joong (Department of Environmental Engineering, Pusan National University) ;
  • Shon, Byung-Hyun (Department of Environmental Engineering, Hanseo University) ;
  • Choi, Eun-Hwa (Department of Environmental Engineering, Pusan National University) ;
  • Yi, Gang Woo (Department of Environmental Engineering, Pusan National University)
  • Received : 2000.06.12
  • Accepted : 2000.10.04
  • Published : 2000.11.30
Download PDF
⟨ Previous Next ⟩

Abstract

The experiments have been made to develop manganese-based sorbent(MT, MFT) for the removal of hydrogen sulfide from simulated hot coal gases. Manganese-based sorbents were tested in an ambient-pressure fixed-bed reactor to calculate H2S removal efficiency. and a three hole jet attrition tester to characterize the sorbent physical properties. According to the experimental results of attrition test. the attrition resistance of 5% bentonite containing sorbent was higher than that of 2% bentonite. The attrition resistances of both sorbents increased with induration temperature. Effects of sulfidation temperature. space velocity. and $H_2S$ concentrations on the $H_2S$ removal efficiency were investigated. Experimental results showed that $H_2S$ could be removed from 5,100ppmv to 20ppmv at $450^{\circ}C$, and to 30~65ppmv at $550{\sim}650^{\circ}C$ for both MT/MFT sorbents. As for the change of space velocity, the breakthrough time was decreased with space velocity.

모사 고온석탄가스로부터 황화수소를 제거하기 위해 망간계 탈황제(MT, MFT)에 대한 실험을 수행하였다. 망간계 탈황제의 황화수소 제거효율과 탈황제의 물리적 특성을 파악하기 위해 각각 고정층 반응기와 attrition tester를 사용하여 실험하였다. 마멸저항에 대한 실험결과, 벤토나이트를 5% 함유한 탈황제가 2%를 함유한 탈황제보다 마멸저항이 컸으며 또한 경화온도가 높을수록 마멸저항이 큰 것으로 나타났다. 반응온도, 황화수소농도, 그리고 공간속도가 황화수소 제거효율에 미치는 영향을 조사한 결과, MT와 MFT 탈황제 모두 $450^{\circ}C$에서는 황화수소를 5,100ppmv에서 20ppmv까지 제거할 수 있었고, $550{\sim}650^{\circ}C$에서는30~65ppmv까지 제거할 수 있었으며, 공간속도가 증가함에 따라 파과시간은 감소하였다.