Cotton fabric was treated with chitosan by pad-dry(-cure) method to impart antimicrobial properties. Four chitosans of different degree of deacetylation (DAC: 65~95%) with similar molecular weight(MW: ca. 50, 000) and one chitosan oligomer(MW 1, 800, DAC 86%) were used. In order to improve the durability to laundering of antimicrobial activity for the fabrics treated with chitosan oligomer, crosslinker or binder was included in the finishing formulation. Antimicrobial activity against Staphylococcus aureus and Proteus vulgaris was evaluated by the Shake Flask Method. The treated fabrics were laundered up to 20 times according to AATCC Test Method 60-1986 or JIS 0217-104 and antimicrobial activity of the laundered fabrics was evaluated. The antimicrobial activity was increased with the increase of concentration and degree of deacetylation of chitosan. And the cured fabrics showed better durability to laundering than the not-cured fabrics according to AATCC Test Method 60-1986. Crosslinker and binder decreased antimicrobial according of the fabrics treated with chitosan oligomer and were not effective to improve the durability to laundering according to JIS 0217-104. (Korean J Human Ecology 1(1) : 103~112, 1998)

면직물에 항균성을 부여하기 위하여 패드-건조(-열처리법)에 의해 키토산처리를 하였다. 분자량이 약 50,000으로 비슷하고 탈아세틸화도가 65∼95％인 4종의 키토산과 분자량이 약 1,800이고 탈아세틸화도가 약 86％인 1종의 키토산올리고머를 사용하였다. 키노산올리고머로 처리한 경우에는 세탁내구력을 증진시키기 위하여 가교제 또는 바인더를 가공처리액에 첨가하였다. 항균성은 쉐이크플라스크법에 의해 공시균 Staphylococcus aureus 와 Proteus vulgaris를 사용하여 측정하였다. 세탁내구력은 AATCC Test Method 60-1986 또는 JIS 0217-104에 따라 20회까지 세탁한 후 항균성을 측정하였다. 실험결과, 항균성은 키토산의 농도와 탈아세틸화도가 증가함에 따라 증가하였으며 열처리 유무는 항균성에 큰 영향을 미치지 않았다. AATCC Test Method 60-1986에 따르면 열처리한 시료의 세탁내구력이 열처리하지 않은 시료보다 우수하였다. 가교제나 바인더의 첨가는 키토산올리고머를 처리한 시료의 항균성을 감소시켰으며, JIS 0217-104에 따라 실험한 결과 세탁내구력 향상에 효과가 없었다.