Abstract
The silicon doped $Al_{0.33}$G $a_{0.67}$As were grown by molecular beam epitaxy. The electroreflectance(ER) spectra of Schottky barrier Au/n-Al/suu x/G $a_{1-x}$ As have been measured at various modulation voltage( $V_{ac}$ ) and dc bias voltage( $V_{bias}$). From the observed Franz-Keldysh oscillations(FKO) peak, the band gap energy of the $Al_{x}$G $a_{1-x}$ As is 1.91 eV which corresponds to an Al composition of 33%. The internal electric field( $E_{i}$)of this sample is 2.96$\times$10$^{5}$ V/cm. As the modulation voltage( $V_{ac}$ ) is changed, the line shape of ER signal does not change but its amplitude varies linearly. The amplitude as a function of modulation voltage has saturated at 0.8 V. The internal electric field has decreased from 6.47$\times$10$^{5}$ V/cm to 2.00$\times$10$^{5}$ V/cm as the dc bias voltage( $V_{bias}$) increases from -3.5 V to +0.8 V. The values of built-in voltage( $V_{bi}$ ) and carrier concentration(N) determined from the plot of $V_{bias}$ from the plot of $V_{bias}$ versus $E_{i}$$^{2}$ are 0.855 V and 3.83$\times$10$^{17}$ c $m^{-3}$ , respectively.ively.y.y.y.