Characteristics of Diffusion Coefficient of High Performance Concrete using GGBFS for Road Structures by Accelerating Test Method

슬래그 미분말 혼입률에 따른 도로구조물용 고성능 콘크리트의 압축강도 및 촉진 염소이온 확산 특성

In recent years, the terminology "High-Performance Concrete(HPC)" has been introduced into the construction industry. Most high-performance concretes have a high cementitious content and a low water-cementitious material ratio. The proportions of the individual constituents vary depending on local preferences and local materials. Therefore, many trial batches are usually necessary before a successful mix is developed. The objective of this experiments is to investigate the fundamental properties of high performance concrete based binary cimentitious materials such as ordinary portland cement and ground granulated blast furnace slag. The results from the study will be utilized as the basic data and guideline in making standard mixproportions and the manufacture, construction work and quality control of HPC

본 연구에서는 도로공사의 교량 구조물 적용에 적합한 고성능 콘크리트의 배합도출을 목적으로 고로슬래그미분말을 사용한 고성능 콘크리트의 기초 물성을 평가하였다. 굳지않은 콘크리트의 유동성은 W/B에 상관없이 고로슬래그 미분말의 혼입율이 증가할수록 목표 슬럼프플로우를 만족시키기 위한 고성능감수제의 첨가율은 저하되는 것으로 나타났으며, 목표 공기량을 만족시키기 위한 AE제의 첨가량의 변화는 Plain 콘크리트와 동등한 것으로 나타났다. 고로슬래그 미분말의 경우 높은 혼입율로 인하여 수화반응이 지연되기 때문에 최고온도가 약 10시간 후에 도달되는 것으로 나타났으며, 혼입율 증가에 따른 단열 상승온도는 혼입율 45%까지 수화열 저감효과가 작게 나타났으나 혼입율 60%에서는 수화열이 약 $8^{\circ}C$가량 저감되었다. 이는 수화열이 작은 고로슬래그 미분말의 분량이 많아진 것에 기인된 것으로 사료된다. 압축강도 특성은 W/B=26, 30%에서는 고로슬래그 미분말 혼입율이 증가할수록 압축강도가 Plain 콘크리트에 비하여 약 10MPa가량 크게 증가되는 것으로 나타났지만, W/B=34%에서는 압축강도가 Plain 콘크리트와 거의 같은 수준으로 나타남으로써, 낮은 물결합재비에서 고로슬래그 미분말을 사용할 경우 압축강도 증진에 효과가 있는 것으로 사료된다.