The Evaluation of Mechanical Properties of Ultra High Performance Concrete with Using Steel Fiber of Wave Type

물결형 강섬유를 이용한 초고성능 콘크리트의 역학적 특성 평가

UHPC which was a structural material exhibiting very remarkable mechanical performances with compressive strength, tensile strength and flexural strength rising up to 200MPa, 15MPa and 35MPa, respectively. In addition, this material presents exceptional durability regard to the very low diffusion and penetration speeds of noxious substances like chloride ions This study was carry out to evaluate the effect of flexural behavior according to steel fiber type in UHPC. The results is showing that the steel fiber type have remarkable influence flexural strength Addition to it is showing that steel fiber type made little difference in the first cracking strength but considerable gap in the ultimate flexural strength to use the steel fiber of wave type.

초고성능 콘크리트(Ultra High Performance Concrete)는 압축강도 200MPa, 인장강도 15MPa 및 휨강도 35MPa 정도의 높은 강도 특성과 열화인자의 침투 및 확산 속도가 보통콘크리트에 비해 1/20에서 최대 1/10,000까지 낮은 고내구성을 나타내면서 동시에 슬럼프 플로우가 약 220mm 정도의 자기충전성 특성을 갖는 콘크리트이다. 또한 초고성능 콘크리트의 가장 큰 특징으로는 강섬유의 혼입함으로써 휨강도와 인성의 향상이다. 따라서 본 연구에서는 초고성능 콘크리트의 섬유 형상에 따라 휨거동특성에 미치는 효과를 평가하였다. 그 결과 섬유 형상에 따라 휨강도에 큰 영향을 미치는 것으로 나타났다. 또한 초기균열강도에는 큰 영향을 미치지 않고 물결타입의 강섬유 사용으로 최대 휨강도가 높게 나타났다.