Effect of Calcination Temperature and Sintering Additives on the Sintering Behaviors and Microwave Dielectric Properties of $(Zn_{0.8}Mg_{0.2})TiO_3$

하소온도와 소결조제가 $(Zn_{0.8}Mg_{0.2})TiO_3$계의 소결거동과 마이크로파 유전특성에 미치는 영향

We investigated the effects of calcination temperature and sintering additives on the sintering behaviors and microwave dielectric properties of $(Zn_{0.8}Mg_{0.2})TiO_3$. Highly densified samples were obtained at the sintering temperatures below $1000^{\circ}C$ with additions of 0.45 wt.% $Bi_2O_3$ and 0.55 wt.% $V_2O_5$. From the examination of the existing phases and microstructures before and after sintering of $(Zn_{0.8}Mg_{0.2})TiO_3$ system calcined at the various temperatures ranging from $800^{\circ}C$ to $1000^{\circ}C$, it was found that high $Q{\times}f_o$ values were obtained when unreacted or second phases in calcined body were reduced. When calcined at $1000^{\circ}C$ and sintered at $900^{\circ}C$, it consists of hexagonal as a main phase with uniform microstructure and exhibits $Q{\times}f_o$ value of 42,000 GHz and dielectric constant of 22.