$Ar/CF_{4}$ 유도결합 플라즈마에서 식각된 $(Ba_{0.6}Sr_{0.4})TiO_{3}$ 박막의 손상 감소

Study on Damage Reduction of $(Ba_{0.6}Sr_{0.4})TiO_{3}$ Thin Films in $Ar/CF_{4}$ Plasma

The barium strontium titannate (BST) thin films were etched in $CF_{4}/Ar$ inductively coupled plasma (ICP). The high etch rate obtained at a $CF_{4}(20%)/Ar(80%)$ and the etch rate in pure argon was twice higher than that in pure $CF_{4}$. This indicated that BST etching is sputter dominant process. It is impossible to avoid plasma-induced damages by the energetic particles in the plasma and the nonvolatile etch products. The plasma damages were evaluated in terms of leakage current density, residues on the etched sample, and the changes of roughness. After the BST thin films exposed in the plasma, the leakage current density and roughness increases. In addition, there are appeared a nonvolatile etch byproductsand from the result of X-ray photoelectron spectroscopy (XPS). After annealing at ${600^{\circ}C}$ for 10 min in $O_{2}$ ambient, the increased leakage current density, roughness and nonvolatile etch byproducts reduced. From the this results, the plasma induced damage recovered by annealing process owing to the relaxation of lattice mismatches by Ar ions and the desorption of metal fluorides in high temperature.