• Transactions on Electrical and Electronic Materials
• /
• v.3 no.2
• /
• pp.24-27
• /
• 2002

The NdBaCuO superconductor samples were zone-melted in low oxygen partial pressure (1%O$_2$+99%Ar). The zone-melting temperature was decreased about 12$0^{\circ}C$ film 1,06$0^{\circ}C$, the zone-melting temperature in air. Thus the loss of liquid phase (BaCuO$_2$ and CuO) was reduced during: the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased and, therefore, the substitution of Nd for Ba was occurred. The superconductivity of zone-melted Nd$_{1+x}$Ba$_{2-x}$Cu$_3$O$_{y}$ prepared under low oxygen partial pressure was distinctively improved.d.d.d.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• 2004.05a
• /
• pp.6-8
• /
• 2004

The NdBaCuO superconductor samples were zone-melted in low oxygen partial pressure (1 % $O_2$＋99%Ar). The zone-melting temperature was decreased about 12$0^{\circ}C$ from 1, 06$0^{\circ}C$, the zone-melting temperature in air. Thus the loss of liquid phase (BaCu $O_2$and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased and, therefore, the substitution of Nd for Ba was occurred. The superconductivity of zone-melted N $d_{1＋x}$B $a_{2－x}$C $u_3$ $O_{y}$prepared under low oxygen partial pressure was distinctively improved.d.d.d.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.18 no.6
• /
• pp.585-589
• /
• 2009

Extruder is divided to greatly three part at extrusion process. First, by hopper(Hopper) second, barrel(Barrel) with Screw that is point of extruder and third that is raw material supply wealth extrusion into dies(DIES) Part that decide shape of do product greatly divide. Hopper is role that distribute in raw material supply wealth (Feeding zone) of Screw preserving raw material in state of high quality how at extrusion process, and make distributed raw material as Screw in barrel rotates and 3 stage and inflicting heat and pressure raw material melting(Melting) state. And raw material of melting state Screw's measuring stoker(Metering zone) whereabouts anaphora do and product is completed through pipe channel of dies. Dies that is the most important as Screw in extrusion is part that is last part of melting state process of raw material and causes huge effect in quality of product. If more than design of dies happens, manufacture itself of dies is hard, but there are a lot of amount of losses accordingly. In this research, make pipe channel that raw material of melting state flows in dies can present dies basic design method through flow analysis of ideal pipe channel using CFdesign.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.85-88
• /
• 2001

The NdBaCuO superconductor samples were Zone-melted in low oxygen partial pressure (1% $O_{2}+ 99% Ar$ ). The Zone-melting temperature was decreased about $120^{\circ}C$ from $1060^{\circ}C$ the zone-melting temperature in air. Thus the loss of liquid phase ($BaCuO_{2}$ and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased, so was the substitution of Nd for Ba. The superconductivity of zone-melted $Nd_{1+x}Ba_{2-x}Cu_{3}O_{y}$ prepared under low oxygen partial pressure was distinctively improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.85-88
• /
• 2001

The NdBaCuO superconductor samples were Zone-melted in low oxygen partial pressure (1% O$_2$+99% Ar). The Zone-melting temperature was decreased about 120$^{\circ}C$ from 1060$^{\circ}C$ the zone-melting temperature in air. Thus the loss of liquid phase (BaCuO$_2$ and CuO) was reduced during the zone-melting process. The content of non-superconducting phase Nd422 in zone-melted NdBaCuO samples was clearly decreased, so was the substitution of Nd for Ba. The superconductivity of zone-melted Nd$\sub$1+x/Ba$\sub$2-x/Cu$_3$O$\sub$y/ prepared under low oxygen partial pressure was distinctively improved.

• Journal of Welding and Joining
• /
• v.34 no.1
• /
• pp.75-81
• /
• 2016

This study applied laser surface melting process using CW(Continuous wave) Yb:YAG laser and cold-work die steel SM45C and investigated microstructure and hardness. Laser beam speed, power and beam interval are fixed at 70 mm/sec, 2.8 kW and $800{\mu}m$ respectively. Depth of Hardening layer(Melting zone) was a minimum of 0.8 mm and a maximum of 1.0 mm that exceeds the limit of minimum depth 0.5 mm applying trimming die. In all weld zone, macrostructure was dendrite structure. At the dendrite boundary, Mn, Al, S and O was segregated and MnS and Al oxide existed. However, this inclusion didn't observe in the heat-affected zone (HAZ). As a result of interpreting phase transformation of binary diagram, MnS crystallizes from liquid. Also, it estimated that Al oxide forms by reacting with oxygen in the atmosphere. The hardness of the melting zone was from 650 Hv to 660 Hv regardless of the location that higher 60 Hv than the hardness of the HAZ that had maximum 600 Hv. In comparison with the size of microstructure using electron backscatter diffraction(EBSD), the size of microstructure in the melting zone was smaller than HAZ. Because it estimated that cooling rate of laser surface melting process is faster than water quenching.

• Transactions on Electrical and Electronic Materials
• /
• v.3 no.3
• /
• pp.21-24
• /
• 2002

Two kinds of $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$, the sintering samples and zone melting samples, were heat-treated under pure Ar at 950$^{circ}C$. The substitution of Nd ion for Ba ion in the $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$ before and after the heat treatment was investigated by XRD. In order to confirm the effects of the heat treatment, the Tc and Jc of samples with/without the heat treatment under Ar were comparatively studied. $Nd_{1+X}Ba_{2-X}Cu_3O_{7-{\delta}}$ samples were oxygenated under pure oxygen at $300^{circ}C$. From the XRD pattern it was found that the sample with x<0.4 was transferred from tetragonal phase to orthorhombic phase after the oxygenation, while the sample with x>0.4 did not show the phase transition even after a long time oxygenation. Therefore, the low oxygen partial pressure (Ar+1 % O$_2$) was used for the ambient atmosphere of the zone-melting samples, which could reduce the melting temperature and depress the substitution of Nd for Ba. After the improvement in the zone-melting process, the Jc value was increased to 2 x $10^4$A/$cm^2$ (0 T, 78 K). The particle orientation and the structure of zone-melted NdBaCuO were studied by the XRD and SEM analysis.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.292-295
• /
• 2001

The NdBaCuO superconducting samples were prepared by the Zone melting under low oxygen partial pressure. After the zone-melting the oxygenation process of the NdBaCuO samples in a oxygen flow furnace was studied. In order to compare the oxygenation condition the sintering NdBaCuO samples were studied also. In the study it is found that the optimum temperature for the oxygenation is $350^{\circ}C$, and the oxygen flow speed, the sample volume and the surface area of the sample would influence the oxygenation and the oxygen content.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.292-295
• /
• 2001

The NdBaCuO superconducting samples were prepared by the Zone melting under low oxygen partial pressure. After the zone-melting the oxygenation process of the NdBaCuO samples in a oxygen flow furnace was studied. In order to compare the oxygenation condition the sintering NdBaCuO samples were studied also. In the study it is found that the optimum temperature for the oxygenation is $350{\circ}C$, and the oxygen flow speed, the sample volume and the surface area of the sample would if1uence the oxygenation and the oxygen content.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.2
• /
• pp.110-113
• /
• 2016

(YNdSm)-Ba-Cu-O system high Tc composite superconductors were directionally grown by zone melting process, having large temperature gradient, in air atmosphere. Cylindrical green rods of $(YNdSm)_{1.8}Ba_{2.4}Cu_{3.4}O_x$ [(YNS)1.8]composite oxides by CIP (cold isostatic pressing) method using rubber mold were fabricated. The microstructure and superconducting properties were investigated by XRD, TEM and SQUID magnetometer. The size of nonsuperconducting $(YNdSm)_2BaCuO_5$ inclusions of the melt-textured (YNS)1.8 sample with $CeO_2$ additive were remarkably reduced and uniformly distributed within the superconducting (YNS)1.8 matrix. (YNS)1.8 samples, with / without $CeO_2$ additive, showed an onset $T_c{\geq}90K$ and sharp superconducting transition. The critical current density $J_c$ value of the (YNdSm)1.8 superconductor with $CeO_2$ additive were 840 A, $1.2{\times}104A/cm^2$ in 77 K, 0 Tesla by direct current transport method.