• Korean Journal of Materials Research
• /
• v.22 no.12
• /
• pp.669-674
• /
• 2012

Yellow phosphor dispersed color conversion glasses are promising phosphor materials for white LED applications because of their good thermal durability, chemical stability, and anti-ultraviolet property. Six color conversion glasses were prepared with high Tg and low Tg specimens of glass. Luminous efficacy, luminance, CIE (Commission Internationale de l'Eclairage) chromaticity, CCT (Correlated Color Temperature), and CRI (Color Rendering Index) of the color conversion glasses were analyzed according to the PL spectrum. Color conversion glasses with high Tg glass frit, sintered at higher temperature, showed better luminous properties than did color conversion glasses with low Tg glass frit. The characteristics of the color conversion glass depended on the glass composition rather than on the sintering temperature. The XRD peaks of the YAG phosphor disappeared in the color conversion glass with major components of $B_2O_3$-ZnO-$SiO_2$-CaO and, in the XRD results, new crystalline peaks of $BaSi_2O_5$ appeared in the color conversion glass with major components of $Bi_2O_3$-ZnO-$B_2O_3$-MgO. The characteristics of CIE chromaticity, CCT, and the CRI of low Tg color conversion glasses showed worse color properties than those of high Tg color conversion glasses. However, these color characteristics of low Tg glasses were improved by thickness variation. So color conversion glasses with good characteristics of both luminous and color properties were attained.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2008.10a
• /
• pp.1343-1346
• /
• 2008

$KSrPO_4$ and $Sr_3(Al_2O_5)Cl_2$ phosphors doped with $Eu^{2+}$ emit a blue and orange-yellow luminescence under ultraviolet (UV) excitation at ~ 400 nm, respectivel, which can be used for making white light emitting diodes.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2009.10a
• /
• pp.49-49
• /
• 2009

Phosphors with oxide host material, YAG:$Ce^{3+}$ and $(Ca,Sr,Ba)_2SiO_4:Eu^{2+}$ yellow phosphor, has been used for LED applications. The WLEDs using these phosphors are widely used for LCD backlighting, automobile, and general lighting applications since they have high conversion efficiency and good thermal and chemical stability which can meet necessary life time of LED products up to now. With advances of LED chip technology, the external quantum efficiency and driving current in chip get higher so that the phosphors for high power chip are required to maintain high conversion efficiency and stability at high temperature due to the heat dissipated from LED chips. In addition, higher color rendering index of LED lighting and color reproducibility of LCD than those of LEDs with single yellow phosphors are required. In order to overcome these technical issues rising from evolution of LED technology, new phosphors are in demand and nitride phosphors, one of the promising new candidate materials, will be discussed here.

• Korean Journal of Materials Research
• /
• v.26 no.1
• /
• pp.29-34
• /
• 2016

$NaLa_{1-x}{(MoO_4)}_2$:$Ho^{3+}/Yb^{3+}$ phosphors with the correct doping concentrations of $Ho^{3+}$ and $Yb^{3+}$ ($x=Ho^{3+}+Yb^{3+}$, $Ho^{3+}=0.05$ and $Yb^{3+}=0.35$, 0.40, 0.45 and 0.50) were successfully synthesized by the microwave-modified sol-gel method. Well-crystallized particles formed after heat-treatment at $900^{\circ}C$ for 16 h showed a fine and homogeneous morphology with particle sizes of $3-5{\mu}m$. The optical properties were examined using photoluminescence emission and Raman spectroscopy. Under excitation at 980 nm, the UC intensities of the doped samples exhibited strong yellow emissions based on the combination of strong emission bands at 545-nm and 655-nm emission bands in green and red spectral regions, respectively. The strong 545-nm emission band in the green region corresponds to the $^5S_2/^5F_4{\rightarrow}^5I_8$ transition in $Ho^{3+}$ ions, while the strong emission 655-nm band in the red region appears due to the $^5F_5{\rightarrow}^5I_8$ transition in $Ho^{3+}$ ions. Pump power dependence and Commission Internationale de L'Eclairage chromaticity of the upconversion emission intensity were evaluated in detail.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.3
• /
• pp.130-134
• /
• 2009

A new long persistent phosphors of $CaZrO_3$ was synthesized at high temperature with weak reduction atmosphere by a traditional solid state reaction method. Photoluminescence spectra analysis showed that the $CaZrO_3$ doped with $Tb^{3+}$ emitted green-yellow emission caused by the energy level transition from the $^5D_3$ and $^5D_4$ to $^7F_1{\sim}^7F_6$. The main emission spectra of 542 nm peak by the $^5D_4{\rightarrow}^7F_5$ transition was revealed through synthesizing at high temperature in $N_2$ gas atmosphere. The afterglow emission spectra of $CaZrO_3:Tb^{3+}$ long persistent phosphores arise at 546 nm peak of narrow range. After the 254 nm ultraviolet light excitation source was switched off, the green-yellow long persistent phosphor can be observed which could last for 8 h in the limit of light perception of dark-adapted human eyes ($0.32\;mcd/m^2$).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.04a
• /
• pp.181-184
• /
• 2003

GaN계 청색 여기용 광원으로 최적인 $Y_{3}AI_{5}O_{12}:Ce$계 phosphor를 고상반응으로 제조하여 white LED용 yellow 형광체로 신뢰성을 검토하였다. 출발시료는 metal hydrous oxide로 합성한 분말에 활성제로서 $Ce^{3+}$ 이온의 농도를 변화시키면서 로내의 온도와 시간을 변수로 하여 형광체를 제조하였다. 그 결과 $1650^{\circ}C$에서 2시간 소성시킨 분말의 경우, 입자 크기가 $3{\mu}m$이하인 순수 YAG 형광체를 얻을 수 있었으며 $Ce^{3+}$이온농도를 변화시킨 결과 0.03~0.05mol% 일 때가 가장 우수하여 해외제품수준을 능가하는 우수한 발광특성을 나타내었다. 이때 CIE1931 색좌표 값은 x=0.385, y=0.433으로서 green yellow 색을 나타내었다.

• Journal of the Korean institute of surface engineering
• /
• v.51 no.5
• /
• pp.271-276
• /
• 2018

The effects of activator ion on the structural, morphological, and optical properties of $LaNbO_4:RE^{3+}$ (RE = Dy, Dy/Sm, Sm) phosphors were investigated. X-ray diffraction patterns exhibited that all the phosphors showed a monoclinic system with a main (112) diffraction peak, irrespective of the concentration and type of activator ions. The grain size showed a slightly decreasing tendency as the concentration of $Sm^{3+}$ ions increased. The excitation spectra of the $LaNbO_4:Dy^{3+}$, $Sm^{3+}$ phosphor powders consisted of a strong charge transfer band centered at 259 nm in the range of 220-290 nm and five weak peaks. The emission spectra of the $La_{0.95}NbO_4$:5 mol% $Dy^{3+}$ phosphors exhibited two intense yellow and blue bands centered at 575 nm and 479 nm respectively, which resulted from the $^4F_{9/2}{\rightarrow}^6H_{13/2}$ and $^4F_{9/2}{\rightarrow}^6H_{15/2}$ transitions of $Dy^{3+}$. As the concentration of $Sm^{3+}$ was increased, the intensity of the yellow emission band was gradually decreased, while those of orange and red emission bands centered at 604 and 646 nm began to appear and reached maxima at 5 mol%, and then decreased rapidly with further increases in the $Sm^{3+}$ concentration. These results indicated that white light emission could be realized by controlling the concentrations of the $Dy^{3+}$ and $Sm^{3+}$ ions incorporated into the $LaNbO_4$ host crystal.

• Journal of the Korean Chemical Society
• /
• v.50 no.6
• /
• pp.471-476
• /
• 2006

series of Ca1-xSrxS:Ce phosphors were synthesized by solid-state reactions. The Ca1-xSrxS:Ce phosphors have a strong absorption in region from 430 nm to 470 nm. The emission peaks of CaS:Ce are located at 510 nm and 570 nm. The partial replacement of Ca by Sr in Ca1-xSrxS:Ce causes a blue shift of emission wavelengths. The Ca1-xSrxS:Ce can be used as bluish green and yellow emitting phosphors for white light emitting diodes (LEDs) pumped by the blue LED. We reported the optical properties of Ca1-xSrxS:Ce phosphors for application in phosphor converted white LEDs.

• Journal of Powder Materials
• /
• v.19 no.3
• /
• pp.220-225
• /
• 2012

YAG:Ce yellow phosphor particles were synthesized by spray pyrolysis with changing the solution properties and their luminous properties, crystal structure, and morphological changes were studied by using PL measurement, XRD, and SEM analysis. It was clear that the solution properties significantly affected the crystal phase, crystallite size, the PL intensity, and the morphology of YAG:Ce particles. At low calcination temperature, the addition of urea only to the spray solution was helpful to form a pure YAG phase without any impurity phases, as the result, the highest luminescence intensity was achieved at the calcination temperature of $900^{\circ}C$. When the calcination temperatures were larger than $1300^{\circ}C$, however, the YAG particles prepared without any additive showed the highest luminescent intensity. Regardless of the solution conditions, the emission intensity of YAG:Ce particles prepared by spray pyrolysis showed a linear relation with the crystallite size. In terms of the morphology of YAG:Ce particles, the addition of both DCCA and $NH_4OH$ to the spray solution was effective to prepare a spherical and dense structured YAG particles.

• Journal of the Semiconductor & Display Technology
• /
• v.16 no.4
• /
• pp.11-15
• /
• 2017

Red phosphors, $Sr_2Si_5N_8:Eu^{2+}$, were synthesized as a single-phase crystal structure by optimizing carbon and $Eu^{2+}$ contents in a carbothermal reduction nitridation method. With increasing $Eu^{2+}$ contents, the photoluminescence spectra were red-shifted from 600 nm peak for 1 mol% for to 700 nm for 7 mol%. It was suggested that this red shift is attributed to the energy transfer from one low-energy sited $Eu^{2+}$ (1) to other high-energy sited $Eu^{2+}$ (2). Finally, the best red sample (620 nm emission peak and 80 nm half width for 3 mole% of $Eu^{2+}$) was packaged on a Blue LED together with two additional green and yellow phosphors, the fabricated White LED showed a high color-rendering index of 90 and white color coordinates of x= 0.321 and y = 0.305.