• Journal of the Korean Wood Science and Technology
• /
• v.44 no.6
• /
• pp.828-841
• /
• 2016

Relatively little information is available regarding the correlation between wood and veneer quality, especially for Samama wood, an endemic wood species in eastern Indonesia. This study addresses the quality of 8 years old Samama wood and its effect on the veneer quality. Samama wood quality was determined by evaluating its specific gravity, moisture content, fiber dimensions, and microfibril angle from pith toward bark. Meanwhile, veneer quality was assessed by examining veneer thickness and lathe check characteristics. Geometry factor model was constructed to elaborate the quantities of lathe check from pith toward bark. Results show that fair variations of veneer thickness, ranging from 1.5 mm to 3.0 mm, could be obtained from Samama wood. The quantity, depth, and length of lathe check were noticeably decreasing toward bark. Further, in the same manufacturing process, geometry factor was determined as the dominant factor over other wood properties in affecting the frequency of lathe checks from pith towards bark. These facts should be put into consideration in producing veneer from Samama wood. Moreover, these results enlighten the potential of Samama wood as plywood and other excellent veneer-based products.

• Journal of the Korean Wood Science and Technology
• /
• v.8 no.2
• /
• pp.6-8
• /
• 1980

Japanese larch veneer, Cryptomeria veneer and japanese cypress veneer were peeled with condition of nose bar pressure at 5%, 10%, 15%, to find the optimum nose bar pressure. 1. Optimum nose bar pressure was 15% in 2mm thickness veneer of japanese larch. 2. Optimum nose bar pressure was 5% in 2mm thickness veneer of Cryptomeria. 3. Optimum nose bar pressure was 15% in 2mm thickness veneer of japanese cypress.

• Journal of the Korean Wood Science and Technology
• /
• v.38 no.5
• /
• pp.385-390
• /
• 2010

This study was carried out to manufacture very thin natural elm veneer overlaid charcoal board for enhancing aesthetic value of charcoal board for the indoor application, and to use the advantageous properties of the charcoal as a building material for solving the sick house problem. The thin elm veneer had 26.9% opening ratio. The experiment results showed that the spreading area and the nonvolatile content of adhesive did not affect the gas adsoprtion of fancy veneer overlaid charcoal board. The natural thin elm veneer overlaid charcoal board enhanced not only the aesthetic beauty but also showed the same gas adsorption by the charcoal board.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.3
• /
• pp.221-230
• /
• 2018

The purpose of this study was to evaluate the effect of several chemical treatments to prevent photodegradation of wood veneer by external UV (Ultraviolet) light. Of woods, walnut veneer is selected as a raw material for this study since it is known as a luxurious wood with dark color giving an esthetic effect. Alcohol-benzene, hydrogen peroxide ($H_2O_2$) and sodium hypochlorite (NaClO) solution were used for investigate the effect on color stabilization. Despite the removal of the extractive compounds, which is known as a discoloration component, a significant color change of walnut wood veneer was observed. Meanwhile, the veneers treated by 20 and 30% $H_2O_2$ solution at $75^{\circ}C$ for 1 h also showed the no positive effect of color stability exposed to UV light although they have a bleaching effect on wood veneer. Besides, it was difficult to maintain the original color of walnut veneer due to the elution of the extractive compounds. On the other hands, the veneer treated by NaClO solution indicated the good performance on color stability despite of the intensive UV light test. However, when the concentration exceeds 3%, surface roughness and fiber damage occurred simultaneously. Therefore, the walnut species should be treated with proper concentration when sodium hypochlorite is applied to the veneer.

• Journal of the Korean Wood Science and Technology
• /
• v.39 no.5
• /
• pp.451-458
• /
• 2011

Adhesives derived from renewable resources allow wood panel producers to make lower cost alternatives to formaldehyde-based adhesive resins. Among them, adhesive components extracted from industrial by-products or wastes are the most important research fields in the efficient utilization of waste and cost reduction. In our study, the rapeseed flour, which is a by product from the production of biodiesel extracted from rapeseed, was introduced to develop alternative adhesives for the production of wood flooring. The rapeseed flour was hydrolyzed with 1% sodium hydroxide solution and PF prepolymers were prepared with 3-molar ratios, 1.8, 2.1 and 2.4. The linear fracture mechanics was introduced to evaluate the glue bond quality in wood flooring composed of fancy-veneered and plywood, and the formaldehyde emission and adhesive penetration were also investigated. The formaldehyde emissions of wood flooring met the requirement of the standard of $SE_0$ specified in the KS standard. The rapeseed flour adhesive penetrated sufficiently into the vessel elements and lumens in fancy veneer and plywood and gave strong bond quality to the wood flooring. The fracture mechanics was introduced to evaluate the adhesive joint between fancy veneer and plywood. The critical stress intensity factor ($K_{IC}$) of boliva overlayed wood flooring was increased with increasing molar ratio and this was the same tendency in oak overlayed wood flooring. From the results, the formulated adhesives were efficiently used to bond fancy veneer onto the plywood to make wood flooring and showed a potential to be used as a component of environmentally friendly adhesive resin systems for production of flooring.

• Journal of the Korean Wood Science and Technology
• /
• v.47 no.2
• /
• pp.239-248
• /
• 2019

This research presents an improvement of the physical and mechanical properties of composite board (com-ply) made of Oriented Strand Board (OSB) coated with wood veneer of Pine (Pinus merkusii), Avocado (Persea Americana) and Mahogany (Swietenia mahogany). 1.5 mm thick veneers of those three wood types were adhered to the surface of OSB using two adhesive types: epoxy and isocyanate. The adhesive with the glue spread of $250g\;m^{-2}$ applied using single glue line was spread and then cold pressed with the pressure of $15kg\;cm^{-2}$ for 3 hours. The research result showed an improving dimension stability of com-ply, but not found on all parameters of physical property test. The moisture content seemed to be influenced by the com-ply type, yet not related to its thickness swelling, water absorption and linear expansion. The exception took place in the parallel linear expansion when immersed for 2 hours. The highest to the lowest increases of MOE and MOR were consecutively found on OSB coated with wood veneer of Pine, Mahogany and Avocado. However, the increases were statistically insignificant. The highest increasing screw hold power was found at the com-ply type AE (avocado veneer and epoxy adhesive) that was by 28%.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.4
• /
• pp.407-419
• /
• 2014

The analysis of shape before and after heating, Surface moisture content, Moisture weight change and surface heat distribution by fixed type microwave heating in forms of flat veneer and veneer roll of Korean pine, pitch pine, larch and yellow poplar was conducted. The results were as follows: In case of flat veneer, the quality after microwave heating was comparatively good, but it was somewhat warped. These phenomena may be due to transformation by nonuniform drying stress and stronger effect of local irradiation on the veneers when heating veneer owing to the characteristics of fixed type microwave equipment. In case of the features of roll-shaped veneer heated by microwave, the quality after heating was comprehensively excellent. Especially there was no warping unlike flat veneer. Heat distribution and diffusion were also very stable for roll-shaped veneer and such heat distribution had much influence on surface moisture content and moisture weight loss. Accordingly, the veneer roll would show sufficient drying efficiency in fixed type microwave equipment through a scrutinized examination on generating power and irradiation time according to species and thickness of veneer.

• Journal of the Korean Wood Science and Technology
• /
• v.22 no.3
• /
• pp.17-25
• /
• 1994

This study was carried out to compare the properties of Com-Ply Boards with those of OSBs. These two kinds of boards were made of same flakes. Com-Ply Boards were covered with three different thickness veneers, such as 4mm, 3mm, and 2.5mm. All manufactured Com-Ply Boards and OSBs were 12mm thick. In MOR, all Com-Ply Boards were higher than OSB, and especially 3mm-veneer and 2.5mm-veneer Com-Ply Board were highest. But OSB showed 420kg/$cm^2$. 3mm-veneer Com-Ply Board showed the highest internal bonding 7.0kg/$cm^2$ and then 2.5mm-veneer showed 6.8kg/$cm^2$, and OSB showed 6.6kg/$cm^2$. Screw holding strength showed the high value 23.9kg/$cm^2$, 25.5kg/$cm^2$, and 29.3kg/$cm^2$ respectively at 3mm-veneer, 2.5mm-veneer Com-Ply Board and OSB. Thickness swelling of Com-Ply Boards was lower than that of OSB, but Water absorption of OSB was lower. Finally it was very encouraging that all properties of OSB without veneer, whose cost is higher than flake and whose properties is better, were not worse than those of Com-Ply Board with veneer. It seems That more researches on OSB will be required.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.6
• /
• pp.23-35
• /
• 2004

The goal of study was to investigate the influence of the acrylated urethane oligomer on mechanical properties, the chemical resistance and thermal resistance of the UV curable urethane acrylate coatings for fancy veneer overlayed plywood flooring. The pencil hardness and abrasion resistance of the coated fancy veneer overlayed plywood floorings increased with increasing the acrylate functionality of the acrylated urethane oligomer. In the case of the UV cured film containing hexa-functional acrylated aliphatic urethane oligomer, high discoloration of the coated fancy veneer overlayed plywood flooring was observed near the cracks at the beginning of the chemical treatment. In this study, it was found that the degradation of the UV cured film caused by an alkaline reagent was higher than that of the UV cured film caused by an acidic treatment.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.1
• /
• pp.45-51
• /
• 2004

Combined microwave-convective drying of 2.4mm-thick radiata pine veneer grown in New Zealand was conducted to investigate drying characteristics. The veneers could be dried from 160% to 0% moisture content in 7.5 min by microwave drying combined with hot-air of 100℃. This drying rate is about three times higher than that of conventional convective drying with only hot air of 100℃. However there remained charred spots when too high microwave power was applied. Therefore investigations of the microwave-drying characteristics of veneer of various sizes and species are needed to determine the optimal drying conditions.