• 한국건축시공학회지
• /
• 제12권5호
• /
• pp.539-547
• /
• 2012

To manufacture laminated wood with improved mechanical properties by providing uniform adhesiveness, the adhesive was applied and the plate adhesive was laminated on the wood surface. Then, after laminating the wood on the top part of the adhesivebond, it was heated and dried while the adhesive was stiffened using microwaves, and the test piece was manufactured by compressing it with the press machine for thirty minutes. The temperature and the water content were examined according to the heating time of the wood heated with the microwave, and testing was conducted on the shear strength and flexural strength of the wood. In addition, the microstructure of the adhesive bond between the wood was recorded to confirm the penetrabilityinto the wood structure for the adhesive. After the test was conducted, it was found that the test piece manufactured with wood that has its water content leveled with the microwave heating showed improved shear strength and bending strength compared to the standard test piece. With regard to adhesives, liquefied polyvinyl acetate resin and plate's PVB resin were found to have superior adhesive strength. Also, after filming the cellular microstructure, it was found that when the laminated wood is heated with microwaves, the infiltration of the adhesive into the inside of the wood becomes easy, which makes it effective for improving adhesiveness.

• 임산에너지
• /
• 제24권1호
• /
• pp.33-38
• /
• 2005

목탄의 제조과정에서 발생되는 목타르의 신용도를 찾고자 목타르를 이용한 레졸형 페놀수지접착제를 제조하여, 합판에 대한 접착력 시험을 실시하였다. 소나무타르계 접착제는 미첨가 페놀접착제와 비교했을 때, 고형분, 점도와 같은 수지의 물성은 유사하였으며, 인장 전단 접착력에서도 비내수, 내수 모두 페놀접착제에 비해 크게 떨어지지 않았다. 그러나, 참나무타르계 접착제의 경우에서는 수지물성도 페놀수지와는 다른 물성을 보였으며, 내수접착력은 페놀접착제의 접착력에 비해 절반 정도의 낮은 접착력을 보였다. 포름알데히드 방출량은 목타르의 첨가량이 많을수록 많이 방출되었다.

• Journal of the Korean Wood Science and Technology
• /
• 제42권1호
• /
• pp.34-40
• /
• 2014

흰개미 방제 및 방곰팡이 효력이 입증된 저독성 네오티코치드계 목재보존제가 집성재 제조용 레조르시놀계 접착제의 접착력에 미치는 영향을 조사하였다. ACQ, CUAZ, 네오니코치드계 약제를 도포 처리한 다음 건조시킨 소나무 판재를 사용하였으며, 집성 접착 후에 블록 전단시험편을 채취하여 상태 및 촉진 열화 시험 후의 전단접착력과 목파율을 측정하여 비교하였다. ACQ 및 CUAZ 처리 집성재는 무처리 및 네오니코치드계 목재보존제 처리 집성재에 비하여 낮은 전단접착력을 보여 접착력 저하가 인정되었다. 이것은 이들 방부제 중에 함유되어 있는 구리화합물에 기인하는 것으로 판단되었다. 네오니코치드계 목재보존제 처리 집성재는 상태 및 촉진열화 시험 후에도 가장 우수한 전단접착력을 나타내 레조르시놀계 접착제의 접착성능에는 영향을 미치지 않는 것으로 판단하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제50권3호
• /
• pp.167-178
• /
• 2022

To investigate the influence of manufacturing environment on bonding performance of mixed cross laminated wood (CLT) using polyurethane (PUR) adhesive, a boiling water soak delamination test according to the temperature and relative humidity was conducted. The 5-ply mixed CLT consisted of Japanese Larch for external and middle layer and yellow poplar for internal layer. The PUR adhesives with different opening times of 10 and 30 minutes were used. The mixed CLT was manufactured according to pressing times of PUR and manufacturing environments of summer and winter. In case of summer environment, the delamination rate of the mixed CLT with pressing time of 4 hours using a PUR adhesive with open time of 10 minutes met the requirements of KS F 2081. In case of winter environment, the delamination rate of the mixed CLT didn't meet the requirements of KS standard. However, it was possible to confirm the effect of improving the adhesive performance by adjusting the pressing time according to the open time of the adhesive under the manufacturing conditions. The delamination rate of CLT with open time 30 minutes PUR, manufactured by indirect moisture supply methods was 11.2% better than direct moisture supply methods. As a result of delamination test in the same condition of relative humidity and adhesive, it was found that the temperature of manufacturing environment influences the adhesive performance.

• Journal of the Korean Wood Science and Technology
• /
• 제39권5호
• /
• pp.451-458
• /
• 2011

Adhesives derived from renewable resources allow wood panel producers to make lower cost alternatives to formaldehyde-based adhesive resins. Among them, adhesive components extracted from industrial by-products or wastes are the most important research fields in the efficient utilization of waste and cost reduction. In our study, the rapeseed flour, which is a by product from the production of biodiesel extracted from rapeseed, was introduced to develop alternative adhesives for the production of wood flooring. The rapeseed flour was hydrolyzed with 1% sodium hydroxide solution and PF prepolymers were prepared with 3-molar ratios, 1.8, 2.1 and 2.4. The linear fracture mechanics was introduced to evaluate the glue bond quality in wood flooring composed of fancy-veneered and plywood, and the formaldehyde emission and adhesive penetration were also investigated. The formaldehyde emissions of wood flooring met the requirement of the standard of $SE_0$ specified in the KS standard. The rapeseed flour adhesive penetrated sufficiently into the vessel elements and lumens in fancy veneer and plywood and gave strong bond quality to the wood flooring. The fracture mechanics was introduced to evaluate the adhesive joint between fancy veneer and plywood. The critical stress intensity factor ($K_{IC}$) of boliva overlayed wood flooring was increased with increasing molar ratio and this was the same tendency in oak overlayed wood flooring. From the results, the formulated adhesives were efficiently used to bond fancy veneer onto the plywood to make wood flooring and showed a potential to be used as a component of environmentally friendly adhesive resin systems for production of flooring.

• Journal of the Korean Wood Science and Technology
• /
• 제48권5호
• /
• pp.755-764
• /
• 2020

Due to pronounced mechanical performance and being environmental friendly, aqueous polymer isocyanate adhesive (API) has been widely applied in the production of formaldehyde-free wood products. In this study, flame retardant formaldehyde-free plywood was prepared by incorporation of flame retardants into the API adhesive. Partially phosphorylated poly (vinyl alcohol) (PPVA) which was prepared by reacting poly (vinyl alcohol) with phosphoric acid was used to replace PVA in API formula. In addition, Mg-Al layered double hydroxides (LDH) was chosen as additive flame retardant, replacing traditional filler CaCO₃ in API adhesive formula. And then, the flame retardant API adhesive with main agent (PPVA replacing PVA70wt.%, SBR emulsion 30wt.%), curing agent 10wt.% (accounts for of the main agent), and 20wt.% LDHs (accounts of the main agent) was used to prepare flame retardant plywood. The effect of application of PPVA and Mg-Al LDH on bonding strength of plywood was investigated. The flammability characteristics of the plywood were determined by cone calorimeter test (CCT). The results revealed that compared with the plywood prepared with API adhesive, the use of PPVA and LDH enhanced the flame retardancy of plywood without negatively affecting bonding strength. The CCT tests indicated that the heat release and smoke production flame retardant API plywood were lower than those of the ordinary API glued plywood. Promising developments for flame retardant API adhesive were expected in future applications of flame retardant formaldehyde-free plywood.

• Journal of the Korean Wood Science and Technology
• /
• 제44권6호
• /
• pp.872-879
• /
• 2016

Demand of natural interior finishing material has been widely sprayed in nowadays because many weak people as children, pregnant women, and elder people are being struggled with sick house syndrome due to volatile organic compounds such as formaldehyde, toluene, benzene, etc. Our research group developed a no-added formaldehyde adhesive for wood-based panels from mainly rice powder and some additives in the previous study for abating sick house syndrome. Since the rice powder adhesive provides a good source of nutrients with microorganisms, it was suspected a susceptibility of the rice powder adhesive to fungal and sapstain attack. We evaluated anti-sapstain activity of the rice powder adhesives modified by adding wood preservatives. We modified the rice powder adhesive by adding three different types of anti-sapstain preservatives at three different concentrations to assess their anti-sapstin activity. The bonding strengths of the modified rice powder adhesives were still outstanding performance on all samples. Moreover, the plywood manufactured with the modified rice powder adhesive satisfied outdoor use requirement for ordinary plywood (KS F3101, Korean Standard). The results obtained showed that at least 3% of preservative should be added to the rice powder adhesive to obtain effective anti-sapstain activity.

• 임산에너지
• /
• 제24권1호
• /
• pp.28-32
• /
• 2005

목탄의 제조 과정 중 얻어지는 목타르의 활용방안을 모색코자 페놀수지에 목타르를 혼합하여 합판을 제조하여, 물리적, 기계적 및 포름알데히드 방출성능을 조사하였다. 목타르를 혼합하여 제조된 합판의 경우, 목타르를 혼합하지 않은 합판에 비해 물리적, 기계적인 면에서 별다른 감소를 보이지 않았으며, 인장전단 접착력은 비내수, 내수 모두 목타르의 혼합으로 인하여 오히려 향상되는 것으로 나타났다. 또한 포름알데히드 방출량에서도 목타르의 첨가는 방출량을 감소시키는 것으로 나타났다.

• Journal of the Korean Wood Science and Technology
• /
• 제52권1호
• /
• pp.58-69
• /
• 2024

To evaluate the adhesive characteristics of mixed cross-laminated timber (CLT) using domestic softwoods structural lumber proposed by KS F 3020 and yellow poplar, penetration depth of adhesive and thickness of bonding line were analyzed based on the results of boiling water soaking delamination. 3 Types of adhesives and 2 types of major layer were divided into a 5 ply CLT using yellow popular as minor layer. The bonding performance of the mixed CLT as structural members was evaluated based on the KS F 2081. The thickness of bonding line between layers of the mixed CLT was measured with a scanning electron microscope, and the adhesive penetration depth in the layer members was measured with an optical microscope. As a result of boiling water soaking delamination test of mixed CLT, the CLT specimens using PRF and PUR adhesives met the requirements of KS F 2081. It was verified that the penetration path of the adhesive in the layes was mainly through the tracheid cell in the case of Japanese larch and Korean red pine layers, and through the vessel and radial tissue in yellow popular layers. The penetration depth of the adhesive was the highest for the PRF adhesive under the same pressing time conditions, and the thickness of the bonding line was in inverse proportion to the penetration depth in the case of the PUR adhesive.

• 한국가구학회지
• /
• 제22권3호
• /
• pp.174-182
• /
• 2011

Over the last decade, Sick Building Syndrome has become a significant social issue in Korea and many methods have been considered to maintain comfortable indoor air quality. To reduce toxic substances emitted from wood composite products, the source control is an efficient method through the reduction of formaldehyde content by using natural material-based adhesives for composite wood products production. Among alternative materials, soybean protein is considered an appropriate natural material to replace formaldehyde-based resin and many efforts have been made to produce new products, such as soap, shampoo, ink, resin, adhesive and textile through changing the chemical or physical properties of soybean. To process soybeans into these useful products, the beans are dehulled and the oil is removed by crushing at very high pressure or by solvent extraction. For use soybean as an adhesive, it is processed at temperatures below $70^{\circ}C$ to preserve the alkaline solubility of the proteins. In addition, soybean-based adhesive is undergone treatment process to improve mechanical properties using urea, urease inhibitor N-(n-butyl) thiophosphoric triamide and sodium dodecyl sulfate. The modified soybean-based adhesive exhibited sufficient mechanical properties to use as an adhesive for composite wood products. This paper is a review article to discuss the possibilities of soybean-based adhesive for environment-friendly furniture materials.