• Proceedings of the KWS Conference
• /
• 1995.04a
• /
• pp.65-67
• /
• 1995

The solidification crack susceptifility of aluminum alloy weld metal have been evaluated by means of the slef restraint and external restraint cracking test. It has been observed expermently as follows : (1) The manganese is beneficial to decrease the solidification cracking susceptibility. (2) Weld metal containing zirconium is less sensitive to the solidification cracking than the weld metal containing chromium does. (3) The self restraint test method shows the same tendency in results as the external restraint test does.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.3 s.33
• /
• pp.49-56
• /
• 1999

Welding is a reliable process and is mainly adopted for fabricating heavy structures. Recently, transverse cracks in the weld metal is serious problem, and they affect cost, efficiency, safety and joint reliability for various welded structures. In this view of point, this study investigated the potential factors for weld metal transverse crack. The main results obtained are as follows; 1) The content of diffusible hydrogen in the commercial flux cored are welding wire was remarkable change by manufacturer. 2) The diffusible hydrogen content was thd main factor for weld metal transverse cracks. 3) Weld metal was immune to transverse cracking under the condition of low diffusible hydrogen content of high restraint condition. 4) The factors for weld metal transverse crack would be the content of diffusible hydrogen and restraint of weld joint.

• Journal of Welding and Joining
• /
• v.33 no.6
• /
• pp.6-12
• /
• 2015

Thermal fatigue life of the automobile exhaust manifold is directly affected by the restraint force according to the structure of exhaust system and bead shape of the welded joints. In the present study, the microstructural changes and precipitation behavior during thermal fatigue cycle of the 18wt% Cr ferritic stainless steel weld heat affected zone (HAZ) considering restraint stress were investigated. The simulation of weld HAZ and thermal fatigue test were carried out using a metal thermal cycle simulator under complete constraint force in the static jig. The change of the restraint stress on the weld HAZ was simulated by changing the shape of notch in the specimen considering the stress concentration factor. Thermal fatigue properties of the weld HAZ were deteriorated during cyclic heating and cooling in the temperature range of $200^{\circ}C$ to $900^{\circ}C$ due to the decrease of Nb content in solid solution and coarsening of MX type precipitates, laves phase, $M_6C$ with coarsening of grain and softening of the matrix. As the restraint stress on the specimen increased, the thermal fatigue life was decreased by dynamic precipitation and rapid coarsening of the precipitates.

• Journal of Welding and Joining
• /
• v.10 no.2
• /
• pp.43-50
• /
• 1992

This study was aimed at resolving uncertainties about lamellar tearing initiation temperatures and studying the effect of nonmetallic inclusions on the tear initiation. In order to measure the lamellar tearing initiation temperature, the slice bend test was conducted in the temperature range of 20.deg.C to 425.deg.C on A572 Grade 50 and A588 Grade A steels. In addition, the weld restrain test was carried out to measure directly the tear initiation temperature with A572 steel. In slice bend tests, A572 steel showed the most susceptible region to lamellar tearing to be in the range of 100 to 300.deg.C, where the steel showed the minimum ductility. The observed tear initiation by the weld restraint test was to be in the range of 200to 300.deg.C. The tears became narrower and less rounded at the susceptible temperatures. It was confirmed in this study that lamellar teraring initiated during cooling from welding in the range of 200 to 300.deg.C and they were initiated by strain aging embrittlement.

• Journal of Welding and Joining
• /
• v.34 no.4
• /
• pp.28-33
• /
• 2016

The purpose of this study is to evaluate the redistribution of transverse residual stress in the multi-pass FCA butt weld of YP47 in the hatch coaming top plate of ultra large size containership under the tensile cyclic load. In order to do it, the configuration of modified H type specimen including restraint length was first designed to simulate the restraint condition of the butt weld in hatch coaming top plate. FE analysis procedure for evaluating the transverse residual stress was verified by comparing the calculated mean and surface residual stresses with the measured results in the test specimen. After that, the effect of the cyclic load on the redistribution of transverse residual stress was evaluated by comprehensive FEA. From the results, it was found that although the maximum transverse residual stress decreased with an increase in the applied maximum load, the effect of the cyclic load on the mean residual stress is small enough to be negligible. It is because the maximum stress of the ship corresponding to the probability of 10E-8 is less than 70% of yield stress of the weld.

• Journal of Ocean Engineering and Technology
• /
• v.13 no.3 s.33
• /
• pp.57-67
• /
• 1999

Welding is widely applicable and reliable process and is mainly adopted for fabricating heavy structures. Recently, weld metal transverse cracks in butt and fillet weld joint is a serious problem, and they must be eliminated for improving weld joint reliability. The weld metal transverse crack susceptibility of butt and fillet joint was carried out by cantilever type tensile crack testing jig and CTS test. In this view of point, this study investigated the potential factors for weld metal transverse crack. The main results obtained were as follows: 1. The content o fdiffusible hydrogen in weld metal played an important role for weld metal transverse cracks. 2. From cantilever type tensile crack tests, it was pointed out that the higher the diffusible hydrogen content and tensile restraint, the more susceptible to weld metal transverse craking. 3. The TSN(thermal severity number) and diffusible hydrogen were important factors for determining weld metal transverse cracks in fillet weld joints.

• Journal of Welding and Joining
• /
• v.2 no.2
• /
• pp.62-69
• /
• 1984

In this study, cold crack susceptibility of high strength steel (ABS EH32 Steel) welded zone with shielded metal are welding was investigated by tensile restraint cracking test method. Effects of diffusible hydrogen content on root cracking, lower critical stress, crack initiation and fracture mode, hardness value distribution of welded zone and fractograph were mainly investigated. Following conclusions are made: 1. In the view of the lower critical stress level, wet electrode, containing much diffusible hydrogen content shows lower value than dried electrode. 2. Hardness value(Hv 5kg) in Heat Affected Zone of wet electrode is higher than that of dried electrode caused by hydrogen embrittlement. 3. In the case of wet electrode, root crack is initiated and propagated in Heat Affected Zone and then propagated to weld metal, but using of dried electrode, root crack is initiated in Heat Affected Zone and propagated to weld metal without propagating in HAZ. 4. For wet electrode, quasi-cleavage fracture mode is majorly observed on the fracture surface of HAZ and partially of weld metal due to hydrogen embrittlement.

• Journal of Welding and Joining
• /
• v.28 no.4
• /
• pp.26-32
• /
• 2010

The purpose of this study is to evaluate the residual stresses at the multi-pass FCA weldment using the finite element analysis (FEA). In order to do it, an H-type specimen was selected as a test specimen. The variable used was in-plane restraint intensity. The temperature distribution at the multi-pass FCA butt weldment was evaluated in accordance with the relevant guidance recommended by the KWJS. The effective conductivity for the weld metal corresponding to each welding pass was introduced to control the maximum temperature below the vaporization temperature of weld metal. The heat flux caused by welding arc was assumed to be applied to the weld metal corresponding to welding pass. With heat transfer analysis results, the distribution of transverse residual stresses was evaluated using the thermo-mechanical analysis and compared with the measured results by XRD and uniaxial strain gage. In thermo-mechanical analysis, the plastic strain resetting at the temperature above melting temperature of $1450^{\circ}C$ was considered and the weld metal and base metal was assumed to be bilinear kinematics hardening continuum. According to the comparison between FEA and experiment, transverse residual stresses at the multi-pass FCA butt weldment obtained by FEA had a good agreement with the measured results, regardless of in-plane rigidity. Based on the results, it was concluded that thermo-mechanical FE analysis based on temperature distribution calculated in accordance with the KWJS’s guidance could be used as a tool to predict the distribution of residual stress of the multi-pass FCA butt weldment.

• Journal of Welding and Joining
• /
• v.15 no.4
• /
• pp.143-153
• /
• 1997

In this study, bending test was performed on the real-scale, built-up beam test model fabricated by the $CO_2$ arc spot welding to evaluate the applicability of the welding method to the production of the stiffened plate in car-carrying ship. The built-up beam models which were fixed at both ends in longitudinal direction or simply supported to the rigid foundation, depending on the restraint condition of the corresponding car decks considered, were subjected to simulated design vehicle loads or concentrated point loads. During the test, the central deflection and the longitudinal bending stresses were measured from several points on the longitudinal flange face to predict the section properties of the built-up beams. The longitudinal bending stress on each spot weld were also measured to calculate the average horizontal shear force subjected to spot welds. Test results revealed that the shear strength of spot welds with their current weld nugget size and welding pitch was adequate enough to withstand the horizontal shear forces under the design vehicle loads. Although the built-up beam fabricated by the arc spot welding was a discontinuous beam, its mechanical behavior was well explained by the continuous beam theory using the effective breadth of plate. Based on test results, the criterion for the size of spot weld of which the average shear stress might meet the allowable stress requirement of AWS Code could be established.