• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.204-204
• /
• 2000

There are many weld defects such as surface crack, lack of fusion, and incomplete penetration(IP) in the butt joint weld of the existing steel bridges. The crack-like defects may significantly reduce the life of the structure. This paper presents the procedure and the results of the fatigue life assessment of the butt joints with weld defects in the existing steel girder bridge. The butt joint welds with incomplete penetration were instrumented with strain gages to determine the stress histogram under normal traffic. Based on the measured stress histogram the crack propagation analysis were performed for the fatigue life assessment. By using the suggested procedure and methodology, one can decide the time of periodic inspection and the necessity of repair of the butt joint welds with serious weld defects in the existing steel bridge. (Received October 1, 1999)

• Journal of Welding and Joining
• /
• v.18 no.2
• /
• pp.77-85
• /
• 2000

There are many weld defects such as surface crack, lack of fusion, and incomplete penetration (IP) in the butt joint weld of existing steel bridges. The crack-like defects may significantly reduce the fatigue life of the structure. This paper presents the procedure and the results of the fatigue life assessment of the butt joints with weld defects in the existing steel girder bridge. The butt joint welds with incomplete penetration were instrumented with strain gages to determine the stress histogram under normal traffic. Based on the measured stress histogram the crack propagation analysis were performed for the fatigue life assessment. By using the suggested procedure and methodology, one can decide the time of periodic inspection and the necessity of repair of the butt joint welds with serious weld defects in the existing steel bridge.

• Journal of Welding and Joining
• /
• v.16 no.1
• /
• pp.77-87
• /
• 1998

This paper deals with the effect of laser welding parameters on the weld formation. Thin steels for automotive application were prepared so as to be welded with high power carbon dioxide laser system. Major process parameters were position of focus and travel speed. The effect of shielding gas was also discussed by employing the high speed photometry. Test results showed that the optimal position of focus varied in accordance with the joint configuration; bead-on-plate, butt or lap welding. It was recommended that the position of focus for the lap welding be located at slightly inner part of the material to be welded. In this case, however, it was noticeable that the weld penetration ratio, d/t$_{0}$ dropped drastically at the critical region. Results also demonstrated that both the bead width and penetration reduced as the travel speed increased. The penetration ratio showed two distinct regions; stabilized zone at the lower range of the travel spped and sudden drop zone at the higher range of travel speed. Lower limit of the penetration for acceptable weld was proved to be about 90% of the parent metal thickness based on the physical properties of the weld. Mixed gas application for both the shielding of molten metal and laser induced plasma control was recommended as far as the penetration was concerned.d.

• Proceedings of the KWS Conference
• /
• 2003.05a
• /
• pp.81-83
• /
• 2003

The potential advantages of the hybrid welding process are improved weld penetration, enhanced gap tolerance, control of weld metal composition, and improved weld quality in comparison to laser or arc welding. Especially, the deep penetration of hybrid welding is very attractive in welding of thick plates. In this study, therefore, the influence of arc power in hybrid welding on detailed bead dimensions at different laser power levels was investigated.

• International Journal of Advanced Culture Technology
• /
• v.3 no.1
• /
• pp.169-178
• /
• 2015

This research aims to study the effects of various welding parameters in gas metal arc welding (GMAW) process on welding penetration, microstructure and hardness of AS3578-A350 high strength steel with the thickness of 10 mm. The welding process parameters were a welding current of 100-200A, an arc voltage of 20-30V, a welding speed of 20-60 cm/min and a gas shielding type of Ar and $Ar+CO_2$. The summarized experimental results are as follows. An increase of the welding current and voltage affected to increase the penetration depth of the joint. However, when the welding speed was decreased, it increased the penetration depth of the joint. Using the Ar gas for shielding the weld area, produced the higher penetration depth and the less narrow weld bead than the joint that was shielded by the mix gas of $Ar+CO_2$. The variation of the welding process parameters affected to produce the various microstructures of weld metal and heat affected zone and also showed the various kind of hardness along the weld joint.

• Journal of Welding and Joining
• /
• v.11 no.2
• /
• pp.62-73
• /
• 1993

Weld pool oscillation for the full-penetration GTA welding process was investigated for its possible application to weld penetration control through theoretical modeling and experiment. Energy method was used to estimate the natural frequency of the molten pool having the physically-acceptable weld geometry and oscillation modes. An unique experimental system was built which had the data acquisiton and video capabilities so that the pool oscillation signals and molten pool surfaces could be monitored continuously. Pool oscillation was detected through arc voltage and arc light emission simultaneously. The signal from arc light emission showed good coherence with that from arc voltage, and arc light generated the higher quality signal. The molten pool was found to oscillate in different oscillation modes based on the travel speed and weld geometry. The natural frequency estimated from the theoretical model agreed reasonably well with the experimental results.

• Journal of Welding and Joining
• /
• v.18 no.3
• /
• pp.68-75
• /
• 2000

The incomplete penetration(IP) discontinuity in butt joint weld, which is detected during safety analysis of the steel bridge by nondestructive evaluation(NDE) method, is classified as unacceptable defect according to the NDE codes and standards. In fact, there are a little allowance in butt joint weld in the view point of design criterion, and also detected IP discontinuity should be classified and evaluated for the fatigue strength and residual life estimation. In this study, we performed fatigue test to evaluate the fatigue strength of high strength steel(SWS490A) containing IP discontinuities in various size, the results compared and classified according to the bridge construction standard specification which published by korea administration of construction and traffic. Experimental results could be used to evaluate and estimate the IP discontinuities considering different stress range in butt joint bridge weld during periodic safety inspection.

• Proceedings of the KSME Conference
• /
• 2000.04a
• /
• pp.200-205
• /
• 2000

Fatigue failure modes of load-carrying cruciform weld joints are dependent on the characteristics of the fatigue crack initiation and propagation from the weld toe or the weld root. In this study, constant amplitude fatigue tests on load-carrying fillet welded specimen carried out, and fatigue strengths were evaluated. Also, an attempt is made to develop a new analytical model with more accuracy to predict the fatigue crack propagation life of fillet welded cruciform joints of SWS 490B steels containing lack of penetration defects. From the result of this study, fatigue crack growth characteristics of load-carrying fillet welded cruciform joints, containing lack of penetration defects are found to be affected by the weld geometry, stress range and microstructures of the weld zone.

• Journal of Welding and Joining
• /
• v.29 no.6
• /
• pp.71-76
• /
• 2011

Submerged arc welding method from both sides is generally applied to the welding of main panel manufacturing process during ship construction. The tandem SAW method is applied to improve the productivity. The various weld defects that occur during tandem SAW method are melt through, incomplete penetration, undercut and overlap etc. It could be thought that the reasons for these defects are mainly lack of prediction ability for penetration depth and deposited metal area. In this research, total 5 kinds of welding factors for experiment like current of lead pole, voltage of lead pole, current of trail pole, voltage of trail pole and welding speed are adopted. Weld tests are carried out for the analysis of variation effects of these factors on penetration depth and deposited metal area. Based on the test and analysis results, it is possible to obtain the prediction equation for the effect of these factors on the amount of deposited metal and penetration depth. As per the verification of the results by additional tests, it is confirmed that the prediction equation, include a error margin of ${\pm}2mm$ for penetration depth and ${\pm}10mm2$ for deposited metal area.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.746-751
• /
• 2002

In order to make clear the physical relation among the arc plasma, the anode heat transfer and the weld penetration, the results of experimental measurements of temperatures of arc plasma, the distributions of heat input and current on the anode and the weld penetration were presented The experimental results showed that the electron temperature above the anode and current and heat input density on the anode was dominated by the position of the cathode. Furthermore, it was showed that electron temperature of arc plasma was dominated by the cathode shape. These results were related with the results of the welded penetration measurements. As a result, it was showed that the electron temperature above the anode and current density distribution on the anode decided the heat input density distribution on the anode and that the heat input density on the anode remarkably dominated the size of the weld penetration in argon GTA welding process. Furthermore, it was suggested that the cathode played the important role in the determination of the weld penetration in argon GTA welding process.