• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.22 no.3
• /
• pp.88-93
• /
• 2021

SAW (Submerged Arc Welding) is often used for ship construction or welding pressure vessels and involves spraying a flux in a powder form to a welding site to a certain thickness and continuously supplying electrode wires therein. This welding method enables high current welding up to 1,500 to 3,000 A. Arc efficiency is higher than 95% and the technique allows clean work as it creates less welding fume, which is composed of fine metal oxide particles, and the arc beam is not exposed. In this study, SM490C-TMC thick plates were heterogeneously welded by SAW. Mechanical properties of welds were measured, and welds were assessed macroscopically and for adhering magnetic particles. The following conclusions were drawn. Bending tests showed no spots exploded on sample surfaces or any other defect, and plastic deformation testing confirmed sufficient weld toughness. These results showed the 1F welding method has no shortcomings in terms of bending performance.

• Corrosion Science and Technology
• /
• v.22 no.6
• /
• pp.435-446
• /
• 2023

Corrosion behaviors of laser-welded super duplex stainless steel (SDSS) tubes after exposure to an actual power plant environment for one year and those of fin-tube welded SDSS were evaluated. Results showed that corrosion damage on the back side of the SDSS tube in the direction of hot air was higher than that on the front side regardless of weldment location. However, corrosion damage showed no difference between weldment and base metal due to recovery of phase fraction in the weldment through post weld heat treatment (PWHT). Nevertheless, the SDSS tube showed severe corrosion damage along grain boundary due to surface phase transformation (δ → γ) and Cr₂N precipitation caused by PWHT with a high N₂ atmosphere. Corrosion resistance of the SDSS tube was recovered when degraded surface was removed. Corrosion sensitivity of a fin-tube increased significantly due to pre-existing crevice, unbalanced phase fraction, and σ phase precipitation adjacent to the fusion line. Although corrosion resistance was improved by recovered phase fraction and sufficient dissolution of σ phase during PWHT, corrosion reaction was concentrated at the pre-existing crevice. These results suggest that welding conditions for fin-tube steel should be optimized to improve corrosion resistance by removing pre-existing crevice in the weldment.

• Journal of Welding and Joining
• /
• v.30 no.2
• /
• pp.59-64
• /
• 2012

Welding is an essential process in the automotive industry. Most welding processes that are used for auto body are spot welding and $CO_2$ welding are used in a small part. In production field, $CO_2$ welding process is decreased and spot welding process is increased due to welding quality is poor and defects are occurred in $CO_2$ welding process frequently. But $CO_2$ welding process should be used at robot interference parts and closed parts where spot welding couldn't. Because of the 0.65mm ~ 2.0mm thickness steel sheet were used in the automotive industry, poor quality of welding area such as burn through and under fill were happened frequently in $CO_2$ process. In this paper, we will study about the penetration depth which gives a huge impact on burn through changing a degree of base metal, welding position and torch angle. Voltage, current and welding speed were fixed but degree of base metal, welding position and torch angle were changed. And Cold- Rolled(CR) steel sheet was used. Penetration depth was analysed by multiple regression analysis to derive approximate calculations. And reliability of approximate calculations were confirmed through additional experiments. As the results of this research, we confirmed the effect of torch and plate angle to bead shape. And we present a possibility that can simulate more accurate to weld geometry, as deduced the verification equations that has tolerance of less than 21.69%.

• Journal of Energy Engineering
• /
• v.18 no.1
• /
• pp.49-55
• /
• 2009

Occurrence of hydrogen embrittlement could be one of the main obstacles for using structural equipment under hydrogen environment. It is required to develop assessment methods of hydrogen embrittlement for the metals used in production, storage, transmission and application utilities of hydrogen. The most probable method of hydrogen mass transmission is using existing natural gas pipeline. Base or weld part of the pipeline can be damaged by mixed gas of hydrogen in the pipeline. In this study small punch (SP) testing was employed to evaluate the hydrogen embrittlement behavior for a line pipe steel (API X65) with electrochemically hydrogen charged specimens. Results showed that the SP test can be a good candidate test method for hydrogen damage evaluation method. Strength of steel is known to be decreased with the level of hydrogen charging. However, for API X65 steel base metal need in this study, the effect of hydrogen to strength was not significant. It can be negligible regardless of the hydrogen contents in the steel. With this test different strength levels with various hydrogen charging conditions were observed. It can also be anticipated that more sensitive evaluation of material behavior be obtainable by the SP test method.

• Journal of the Korean Institute of Gas
• /
• v.2 no.1
• /
• pp.7-13
• /
• 1998

In this study, for the safety performance of LNG storage tank, the fracture toughness in X-grooved weld HAZ(heat-affected zone) of $9\%$ Ni steel was evaluated qualitatively and quantitatively, and the relation with the change in microstructure was analyzed. The toughness assessment was peformed through the modified CTOD test proposed for thick weldment with X-groove. Additionally, microstructures of HAZ were evaluated by OM, SEM and XRD. From the results, HAZ toughness of SMA(shielded metal arc)-welded $9\%$ Ni steel decreased as the evaluated region approached the fusion line. The decrease in toughness was apparently caused by the increase in the fraction of coarse-grained zone within HAZ. On the other hand, toughness drop with decreasing test temperature in F.L.(fusion line) ${\~}$F.L.+3mm was larger than that in F.L.+5mm${\~}$F.L.+7mm region due to the fact that in the former regions, retained austenite had poor stability.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.39 no.4
• /
• pp.405-413
• /
• 2015

In the US, the number of cases of subterranean water contamination from tritium leaking through a damaged buried nuclear power plant pipe continues to increase, and the degradation of the buried metal piping is emerging as a major issue. A pipe blocked from corrosion and/or degradation can lead to loss of cooling capacity in safety-related piping resulting in critical issues related to the safety and integrity of nuclear power plant operation. The ASME Boiler and Pressure Vessel Codes Committee (BPVC) has recently approved Code Case N-755 that describes the requirements for the use of polyethylene (PE) pipe for the construction of Section III, Division 1 Class 3 buried piping systems for service water applications in nuclear power plants. This paper contains tensile and slow crack growth (SCG) test results for high-density polyethylene (HDPE) pipe welds under the environmental conditions of a nuclear power plant. Based on these tests, the fracture surface of the PENT specimen was analyzed, and the fracture mechanisms of each fracture area were determined. Finally, by using 3D finite element analysis, limit loads of HDPE related to premature failure were verified.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.29 no.2
• /
• pp.153-161
• /
• 2009

After several PWSCCs were found in Bugey(France), Ringhals(Sweden), Tihange(Belgium), Oconee, Arkansas, Crystal Fever, Davis-Basse, VC Summer(U.S.A.), Thuruga(Japan), USNRC and PNNL started the research on PWSCC, that is, PINC project. The aim of this project is to fabricate and obtain representative NDE mock-ups with flaws to simulate tight PWSCC cracks, to identify and quantitatively assess NDE methods for accurately detecting, sizing and characterizing tight cracks such as PWSCC, to document the range of locations and crack morphologies associated with PWSCC and observed responses and to incorporate findings from other ongoing PWSCC research programs, as appropriate. By participating in PINC project, Korean morphology technique about PWSCC and NDE technique have improved and become similar lever with other advanced country. Therefore, the evaluation technique of integrity for nickel alloy component has been improved by cooperation with university, research institute and industries.

• Journal of Korean Society of Steel Construction
• /
• v.16 no.4 s.71
• /
• pp.479-492
• /
• 2004

When U-ribs of steel deck plates are connected at the field, overhead welding should be done with backing strips. Misalignments may occur and lead to eccentric moments as well as high stress concentrations at welded joints. In this study, stress analyses and fatigue tests were carried out. Stress analyses for U-ribs' welded joints with backing strips were performed with different misalignments, root shapes, root gaps, and backing strip sizes. From the stress analyses, the stress concentration factors increased with increasing misalignments and root gaps. With the fixed misalignments and root gaps, the stress concentration factors obtained in the case of the semi-circle root shape were lower than those in the case of the right-angle root shape. It was verified that backing strip sizes have little influence on stress concentration factors. The fatigue tests for U-ribs' welded joints with backing strips indicated that increased misalignments shorten fatigue life drastically and cracks usually initiate at the root of the base metal and are propagated to the weld bead surface. Based on the results of the stress analyses, root-shape control methods were developed to mitigate stress concentration by changing welding condition control, radius curvature, and flank angle.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.7
• /
• pp.434-441
• /
• 2016

Friction Stir Welding (FSW) is a solid-state joining process involving the frictional heat between the materials and tools. The amount of heat conducted into the workpiece determines the quality of the welded zone. Excessive heat input is the cause of oxides and porosity defects, and insufficient heat input can cause problems, such as tunnel defects. Therefore, analyzing the temperature history and distribution at the center of the Friction Stir Welded zone is very important. In this study, the temperature distribution of the friction stir welding region of an AZ61 magnesium alloy was investigated. To achieve this goal, the temperature and metal flow was predicted using the finite element method. In FE analysis, the welding tool was simplified and the friction condition was optimized. Moreover, the temperature measuring test at the center of the welding region was performed to verify the FE results. In this study, the tool rotation speed was a more dominant factor than the welding speed. In addition, the predicted temperature at the center of the welding region showed good agreement with the measurement results within the error range of 5.4% - 7.7%.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.17 no.11
• /
• pp.42-50
• /
• 2016

Overlay welding affects the chemical components and weld hardness by dilution of the lamination layer thickness, which determines the surface properties. This study experimentally investigates different numbers of layers for overlay welding monel materials, which are anti-corrosion materials. The Fe content, weldability of the base metal and monel materials, hardness, and surface flatness were examined. Each evaluation was carried out after overlay welding with three layers on the base material and pipe base material of the plate. The Fe content was evaluated by analyzing the constituents of each layer. The Fe content was satisfactory in the three layers. The weldability of the laminate specimens was evaluated by a bending test. The hardness and bead flatness of the laminate specimens were evaluated by micro Vickers and 3D measurements. The hardness was highest in the heat-affected zone with one layer, and it decreased with increasing lamination. In the case of bead flatness, there is a sharp difference in the deviation with increasing numbers of laminations, which should be considered carefully.