• Corrosion Science and Technology
• /
• v.8 no.3
• /
• pp.116-118
• /
• 2009

Korea Institute of Construction Materials founded Seosan Outdoor Exposure Test Site 2005 at Korea, which is a part of Worldwide Exposure Network (WEN). To evaluate the test site along with other exposure test sites, three different types of paints have been under real time weathering conditions at three major weathering test facilities around the world. Using these test specimens several spectroscopic experiments along with physical tests have been performed. Also acceleration tests have been performed using the same paints. The correlation of weathered paints among three different test facilities and accelerated test results has been compared. From the results the reliability of Seosan Weathering Test Facility and reasonable life time prediction tests are discussed.

• Structural Engineering and Mechanics
• /
• v.65 no.2
• /
• pp.191-201
• /
• 2018

The corrosion environments in a steel structure are significantly different depending on the individual parts of the members. To ensure the safety of weathering steel structures, it is important to evaluate the time-dependent corrosion behavior. Thus, the progress and effect of corrosion damage on weathering steel members should be evaluated; however, the predicted corrosion depth, which is affected by the corrosion environment, has not been sufficiently considered until now. In this study, the time-dependent thicknesses of the corrosion product layer were examined to quantifiably investigate and determine the corrosion depth of the corroded surface according to the exposure periods and corrosion environments. Thus, their atmospheric exposure tests were carried out for 4 years under different corrosion environments. The relationship between the thickness of the corrosion product layers and mean corrosion depth was examined based on the corrosion environment. Thus, the micro corrosion environments on the skyward and groundward surfaces of the specimens were monitored using atmospheric corrosion monitor sensors. In addition, the evaluated mean corrosion depth was calculated based on the thickness of the corrosion product layer in an atmospheric corrosion environment, and was verified through a comparison with the measured mean corrosion depth.

• Journal of Conservation Science
• /
• v.4 no.1 s.4
• /
• pp.11-42
• /
• 1995

Stone-monuments, distributed in this area, have been investigated and studied on the characteristics and the rock phases in the geological and conservational points of view. Most of them may have been built from the end of the Shilla Kingdom to the Koryeo Kingdom, which are based on the typical characteristics of the form. The used rocks in these monuments are mainly biotite granite of the Jurassic age which is widely distributed around the area. Black slate and marbles are also used in some monuments, which may be obtained from other areas. The biotite granite of massive and coarse texture contains often inclusions of biotite aggregates or fragments of dioritic rock phase. However, the biotite granite in the area may be very weak to the chemical weathering so that irregular rock surface shows generally $2\~3mm$ relief. The irregular relief is mainly due to different relative degree on the chemical weathering according to the kind of minerals especially quartz, feldspar and biotite. The chemical weathering is also influenced by organisms. For conservation, they must be scientifically considered based on the characteristics, kind of the rock phase, factors on the weathering process, situation in situ or being transported, and protection.

• Transactions of the Korean Society for Noise and Vibration Engineering
• /
• v.22 no.11
• /
• pp.1099-1105
• /
• 2012

Transparent noise barrier panels have the advantages of transmitting light to nearby residents and allowing drivers to orientate themselves by providing views of the surrounding area. To develop guidelines on quality criteria for transparent soundproof panels, their sound transmission loss and weatherability were experimentally investigated. In Korea, the sound transmission loss of noise barrier panels should be more than 25 dB at 500 Hz and 30 dB at 1000 Hz. The transmission loss tests of transparent panels were performed in accordance with KS F 2808. Typically, plastic materials suffer from color changes when exposed to ultraviolet(UV) light over extended periods. Therefore, weathering of plastics is one of the most important properties for outdoor applications. Protection against UV radiation and weathering is usually accomplished by using UV stabilizer additives or coatings. Transparent materials for soundproof panels were examined through accelerated weathering tests and their weathering resistances were evaluated from changes in yellowness index.

• 보존과학연구
• /
• s.33
• /
• pp.57-67
• /
• 2012

The Uiseong Tapriri Five-Storied stone pagoda has occurred exfoliation, granular disintegration and discoloration by physical and chemical weathering factors with the major deterioration occurring due to efflorescence by salt. According to the results of SEM-EDS and X-ray diffraction analysis, salts consists of gypsum, taranakite. Artificial salt weathering tests were carried out using the same type of rocks as those in the stone pagoda. The test results showed that efflorescence occurred on the surface of the rock, and that exfoliation and granular disintegration occurred inside the rock due to salt crystallization.

• Journal of the Korean institute of surface engineering
• /
• v.47 no.2
• /
• pp.57-62
• /
• 2014

The biogas holder is composed of an outer membrane and an inner membrane which are subject to outdoor exposure and gas exposure respectively. The influence of weathering conditions on the photo-degradation of a biogas holder was investigated. Tests were performed under three different methods - outdoor exposure tests (Seosan, Arizona), accelerated tests (Xenon-are lamp) with the outer-membrane of biogas. Moreover, the changes in the aging process were monitored using color difference, gloss, the contact angle and an optical microscope. Changes in physical properties, such as decrease reduction in gloss, decrease in the contact angle, increase in color difference were observed in the aging process. The comparison between membrane 3B, 4B and membrane 5B under xenon-arc were discussed. Membrane 5B was very sensitive to ultraviolet (UV) ray. There were many difficulties in the outdoor exposure test due to acid rain, dust, and stain resistance.

• Geomechanics and Engineering
• /
• v.25 no.2
• /
• pp.99-109
• /
• 2021

Tunnel provide faster, safer and convenient way of transportation for different objects. The region where it is construction and surrounding medium has significant influence on the overall stability and performance of tunnel. The present simulation has been carried out in order to understand the behaviour of rock tunnel under static loading condition. The present numerical model has been validated with the laboratory scaled model and field data of underground tunnels. Both lined and unlined tunnels have been considered in this paper. Finite element technique has been considered for the simulation of static loading effect on tunnel through Abaqus/Standard. The Mohr-Coulomb material model has been considered to simulate elastoplastic nonlinear behaviour of different rock types, i.e., Basalt, Granite and Quartzite. The four different stages of rock weathering are classified as fresh, slightly, moderately, and highly weathered in case of each rock type. Moreover, extremely weathered stage has been considered in case of Quartzite rock. It has been concluded that weathering of rock and overburden depth has great influence on the tunnel stability. However, by considering a particular weathering stage of rock for each rock type shows varying patterns of deformations in tunnel.

• Journal of The Geomorphological Association of Korea
• /
• v.25 no.3
• /
• pp.19-42
• /
• 2018

In this study, we surveyed weathering progressing aspect by major elements variation and rock hardness by using XRF analysis, schmidt hammer, and thin section analysis. This observation suggested that the weathering process is likely to develop differently according to microstructural characteristics. R-value on the inside wall are lower than those on the outside. Also, the shadier the environment was, the closer it was to inshore areas, the R-value appeared to be lower. The movement of the elements such as Ca, Na and K shows that feldspar is hydrolyzed and can form salt crystallization like a gypsum or halite when they combine with the elements such as S or Cl. It proved a high CaO, $Na_2O$ and $K_2O$ content on flaking inside wall and rock meal. The exfoliation was mainly observed along the shady backwall and ceiling of tafoni. This helped in predicting the growth of tafoni as well as the direction of its progress.

• Corrosion Science and Technology
• /
• v.21 no.4
• /
• pp.258-272
• /
• 2022

Steel structures exposed to the outdoors experienced several types of corrosion, which may reduce their thickness. Since atmospheric corrosion can induce economic losses, it is important to consider the atmospheric corrosion behavior of a variety of metals and alloys. This work performed outdoor exposure tests for 10 years at 14 areas in Korea and calculated the atmospheric corrosion rate of weathering steel. This paper discussed the atmospheric corrosion behavior of weathering steel based on various corrosion factors. The average corrosion rates in coastal, industrial, urban, and rural areas were found to range from (2.83 to 4.23) ㎛/y, (2.99 to 4.23) ㎛/y, (1.72 to 3.14) ㎛/y, and (1.57 to 2.85) ㎛/y respectively. It should be noted that the maximum corrosion rate was about 6.0 times greater than the average corrosion rate. Regardless of the exposure sites, the color differences were increased, but the glossiness was reduced and there was no relationship between the corrosion rate and environmental factors and the glossiness.

• Journal of The Geomorphological Association of Korea
• /
• v.27 no.3
• /
• pp.1-11
• /
• 2020

A CIA analysis (A-CN-K and A-CNK-FM ternary diagram) indicates that, unlike the general granitic hills of the Korean Peninsula, the chemical weathering of the granitic grus (sandy regolith) in the eastern Jincheon basin is variable in geomorphic site except the Chuncheon basin. In the study area, there are three types of hills, such as; inner hills, linear isolated hills, and outer hills. The weathered mantles of the outer hills and linear isolated hills are weakly altered, whereas the inner hill, the Bonghyeon profile, shows a stronger chemical loss of the compositions approximating saprolite. There are small differences between the outer hills and linear isolated hills. The Geumwang site is considered fresh rock due to a low lever of alteration, although its sampling profile shows sandy weathering mantles. In the profiles of the Masan and Mugeuks sites, the lower part of weathering mantles has not experienced a significant level of component loss, but the upper regoliths have substantially been modified. The alteration of the hills occurs by chemical loss of CaO and Na₂O. K₂O exhibited little variation at all sampling suites and it has not changed into saprolite.