• Journal of the Korea Institute of Building Construction
• /
• v.21 no.6
• /
• pp.593-604
• /
• 2021

In this study, a comparative test was conducted on a specially developed elastic waterproof paint and general water-based paint for the purpose of responding to cracks occurring on the outer wall of concrete structures and improving watertightness. Through the comparative experiment, it was confirmed that the watertightness could be improved by securing the crack shielding property, and it was also confirmed that about 10 times more crack responsiveness was secured compared to general water-based paint. In addition, it was confirmed that the adhesion performance of at least 1.3MPa and resistance to a water permeation pressure of 0.1MPa were possible, confirming that stability was secured from a waterproofing perspective.

• Polymer(Korea)
• /
• v.34 no.4
• /
• pp.306-312
• /
• 2010

Triphenylvinylsilane (TPVS) containing vinyl acetate (VAc), butyl acrylate (BA), and Nmethylolacrylamide (NMA) copolymers were prepared by emulsion polymerization. The polymerization was performed at $80^{\circ}C$ in the presence of auxiliary agents and ammonium peroxodisulfate (APS) as the initiator. Sodium dodecyl sulphate (SDS) and Arkupal N-300 were used as anionic and nonionic emulsifiers, respectively. The resulting copolymers were characterized by using Fourier transform infrared spectroscopy (FTIR), gel permeation chromatography (GPC), and dynamic light scattering (DLS). Thermal properties of the copolymers were studied by using thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The morphology of copolymers was also investigated by scanning electron microscopy (SEM) and then the effects of silicone concentrations on the properties of the TPVS-containing VAc-acrylic emulsion copolymers were discussed. The obtained copolymers have high solid content (50%) and can be used in weather resistant emulsion paints as a binder.

• Fire Science and Engineering
• /
• v.23 no.5
• /
• pp.78-83
• /
• 2009

17 kinds of fire resistant paint which are currently used were painted on the MDF, to find flame resistance performance and smoking characteristics according to principal ingredient and characteristics of fire resistant paint. 45 degree combustion test and smoke density test were conducted to investigate the flame resistance performance and smoking characteristics. According to the 45 degree combustion test, acrylic resin type fire resistant paint showed the most excellent fire resistance performance. And the water soluble fire resistant paint showed better fire resistance performance compare to the solvent soluble paints. Also gloss paint showed better fire resistance performance than the flat paint. Based on the smoke density test, the smoke generation of fire resistant treated specimen of acrylic resin type was least. And the water soluble fire resistant paint generate little smoke than solvent soluble fire resistant paint.